Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub&...Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.展开更多
运用等离子喷涂技术在7005铝合金表面制备Al2O3-40%TiO2纳米结构颗粒增强镍基合金复合涂层，分析其微观结构，研究其在不同载荷和速度条件下的摩擦磨损性能。结果表明：复合涂层主要由γ-Ni、α-Al2O3、γ-Al2O3和金红石型-TiO2等相组...运用等离子喷涂技术在7005铝合金表面制备Al2O3-40%TiO2纳米结构颗粒增强镍基合金复合涂层，分析其微观结构，研究其在不同载荷和速度条件下的摩擦磨损性能。结果表明：复合涂层主要由γ-Ni、α-Al2O3、γ-Al2O3和金红石型-TiO2等相组成，其摩擦因数和磨损失重较镍基合金涂层显著降低。在轻载3 N 时，复合涂层磨损表面的接触应力较低，主要发生微观切削磨损；当载荷上升至6~12 N时，接触应力高于磨损表面的弹性极限应力，复合涂层的磨损机理变为多次塑变磨损、微观脆性断裂磨损和磨粒磨损。随着速度的增大，磨损表面的接触温度逐渐升高，复合涂层以多次塑变磨损、疲劳磨损和粘着磨损为主。展开更多
文摘Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.
文摘运用等离子喷涂技术在7005铝合金表面制备Al2O3-40%TiO2纳米结构颗粒增强镍基合金复合涂层，分析其微观结构，研究其在不同载荷和速度条件下的摩擦磨损性能。结果表明：复合涂层主要由γ-Ni、α-Al2O3、γ-Al2O3和金红石型-TiO2等相组成，其摩擦因数和磨损失重较镍基合金涂层显著降低。在轻载3 N 时，复合涂层磨损表面的接触应力较低，主要发生微观切削磨损；当载荷上升至6~12 N时，接触应力高于磨损表面的弹性极限应力，复合涂层的磨损机理变为多次塑变磨损、微观脆性断裂磨损和磨粒磨损。随着速度的增大，磨损表面的接触温度逐渐升高，复合涂层以多次塑变磨损、疲劳磨损和粘着磨损为主。
