Microstructure and interracial reactions of Al2O3 joints brazed with Al2O3-particulate-contained composite Ag-Cu-Ti filler material were researched by scanning electron microscopy （SEM）, electron probe microscopy an...Microstructure and interracial reactions of Al2O3 joints brazed with Al2O3-particulate-contained composite Ag-Cu-Ti filler material were researched by scanning electron microscopy （SEM）, electron probe microscopy analysis （EPMA）, energy dispersive spectroscopy （EDS） and X-ray diffraction （XRD）. The interracial reaction layer thickness of joints brazed with conventional active filler metal and active composite filler materials with different volume fraction of Al2O3 particulate was also studied. The experimental results indicated although there were Al2O3 particulates added into active filler metals, the time dependence of interracial layer growth of joints brazed with active composite filler material is t^1/2 as described by Fickian law as the joints brazed with conventional active filler metal.展开更多
To improve the cyclic stability at high temperature and thermal stability, the spherical Al2O3-modified Li（Ni0.5Co0.2Mn0.3）O2 was synthesized by a modified co-precipitation method, and the physical and electrochemic...To improve the cyclic stability at high temperature and thermal stability, the spherical Al2O3-modified Li（Ni0.5Co0.2Mn0.3）O2 was synthesized by a modified co-precipitation method, and the physical and electrochemical properties were studied. The TEM images showed that Li（Ni0.5Co0.2Mn0.3）O2 was modified successfully with nano-Al2O3. The discharge capacity retention of Al2O3-modified Li（Ni0.5Co0.2Mn0.3）O2 maintained about 99% after 200 cycles at high temperature（55 ℃）, while that of the bare one was only 86%. Also, unlike bare Li（Ni0.5Co0.2Mn0.3）O2, the Al2O3-modified material cathode exhibited good thermal stability.展开更多
A series of mesoporous Cu-Mn-Al2O3（CMA） materials was synthesized at moderate temperature and their structures were characterized by XRD, N2 physical adsorption and TPR techniques. It was found that using metal comp...A series of mesoporous Cu-Mn-Al2O3（CMA） materials was synthesized at moderate temperature and their structures were characterized by XRD, N2 physical adsorption and TPR techniques. It was found that using metal complex ion[Cu（NH3） 4^2＋-Mn（NH3）6^2＋] as raw materials is easier to form good-structure mesoporous Cu-Mn-Al2O3 materials than using its nitrate salt [Cu（NO3）2-Mn（NO3）2]. The TPR tests results indicate that CuO and MnOx were homogeneously dispersed in the mesoporous materials. Their catalytic application to preferential catalytic oxidation of CO in a hydrogen-rich stream was studied. The activity varies in the order of CMA（1：1, molar ratio）〉 CMA（1：2）〉CMA（2：1）〉CMA（CP）〉CMA（1：0）≈CMA（0：1）. The CMA（1：0） and CMA（0：1） have lower activity compared to other samples, implying that there existed coordination effect between Cu-Mn in the samples. The selectivity varied in the order of CMA（0：1）≥CMA（1：2）〉CMA（1：1）〉CMA（2：1）〉CMA（1：0） at higher temperature （≥ 120 ℃）, indicating that increasing the Cu content enhanced the conversion of H2. The sample CMA（CP） made by coprecipitation method has a lower CO oxidation activity and selectivity than its counter-parts of mesoporous Cu-Mn-Al2O3 materials[CMA（1：2）], this attributed to the lower surface area of the former and poor interaction of CuO with MnOx.展开更多
Paraffin/γ-Al2O3 composites as phase change energy storage materials were prepared by absorbing paraffin in porous network of γ-Al2O3.In the composite materials,paraffin was used as a phase change material(PCM)for t...Paraffin/γ-Al2O3 composites as phase change energy storage materials were prepared by absorbing paraffin in porous network of γ-Al2O3.In the composite materials,paraffin was used as a phase change material(PCM)for thermal energy storage,and γ-Al2O3 acted as supporting materials.Characterizations were conducted to evaluate the energy storage performance of the composites,and differential scanning calorimeter results showed that the PCM-3 composite has melting latent heat of 112.9 kJ/kg with a melting temperature of 62.9 ℃.Due to strong capillary force and surface tension between paraffin and γ-Al2O3,the leakage of melted paraffin from the composites can be effectively prevented.Therefore,the paraffin/γ-Al2O3 composites have a good thermal stability and can be used repeatedly.展开更多
基金the National Natural Science Foundation of China(Grant No.50075019) the Visiting Scholar Foundation of Key Lab.in University of China
文摘Microstructure and interracial reactions of Al2O3 joints brazed with Al2O3-particulate-contained composite Ag-Cu-Ti filler material were researched by scanning electron microscopy （SEM）, electron probe microscopy analysis （EPMA）, energy dispersive spectroscopy （EDS） and X-ray diffraction （XRD）. The interracial reaction layer thickness of joints brazed with conventional active filler metal and active composite filler materials with different volume fraction of Al2O3 particulate was also studied. The experimental results indicated although there were Al2O3 particulates added into active filler metals, the time dependence of interracial layer growth of joints brazed with active composite filler material is t^1/2 as described by Fickian law as the joints brazed with conventional active filler metal.
基金Funded by the National High Technology Research and Development Program of China(863 Program)(No.2015AA034600)Province Science and Technology in Anhui(No.1301021011)
文摘To improve the cyclic stability at high temperature and thermal stability, the spherical Al2O3-modified Li（Ni0.5Co0.2Mn0.3）O2 was synthesized by a modified co-precipitation method, and the physical and electrochemical properties were studied. The TEM images showed that Li（Ni0.5Co0.2Mn0.3）O2 was modified successfully with nano-Al2O3. The discharge capacity retention of Al2O3-modified Li（Ni0.5Co0.2Mn0.3）O2 maintained about 99% after 200 cycles at high temperature（55 ℃）, while that of the bare one was only 86%. Also, unlike bare Li（Ni0.5Co0.2Mn0.3）O2, the Al2O3-modified material cathode exhibited good thermal stability.
基金Supported by the Science and Technology Development Project of Shandong Province,China(No.2007GG3WZ03018)
文摘A series of mesoporous Cu-Mn-Al2O3（CMA） materials was synthesized at moderate temperature and their structures were characterized by XRD, N2 physical adsorption and TPR techniques. It was found that using metal complex ion[Cu（NH3） 4^2＋-Mn（NH3）6^2＋] as raw materials is easier to form good-structure mesoporous Cu-Mn-Al2O3 materials than using its nitrate salt [Cu（NO3）2-Mn（NO3）2]. The TPR tests results indicate that CuO and MnOx were homogeneously dispersed in the mesoporous materials. Their catalytic application to preferential catalytic oxidation of CO in a hydrogen-rich stream was studied. The activity varies in the order of CMA（1：1, molar ratio）〉 CMA（1：2）〉CMA（2：1）〉CMA（CP）〉CMA（1：0）≈CMA（0：1）. The CMA（1：0） and CMA（0：1） have lower activity compared to other samples, implying that there existed coordination effect between Cu-Mn in the samples. The selectivity varied in the order of CMA（0：1）≥CMA（1：2）〉CMA（1：1）〉CMA（2：1）〉CMA（1：0） at higher temperature （≥ 120 ℃）, indicating that increasing the Cu content enhanced the conversion of H2. The sample CMA（CP） made by coprecipitation method has a lower CO oxidation activity and selectivity than its counter-parts of mesoporous Cu-Mn-Al2O3 materials[CMA（1：2）], this attributed to the lower surface area of the former and poor interaction of CuO with MnOx.
文摘Paraffin/γ-Al2O3 composites as phase change energy storage materials were prepared by absorbing paraffin in porous network of γ-Al2O3.In the composite materials,paraffin was used as a phase change material(PCM)for thermal energy storage,and γ-Al2O3 acted as supporting materials.Characterizations were conducted to evaluate the energy storage performance of the composites,and differential scanning calorimeter results showed that the PCM-3 composite has melting latent heat of 112.9 kJ/kg with a melting temperature of 62.9 ℃.Due to strong capillary force and surface tension between paraffin and γ-Al2O3,the leakage of melted paraffin from the composites can be effectively prevented.Therefore,the paraffin/γ-Al2O3 composites have a good thermal stability and can be used repeatedly.