To address the issues of reduced performance and shortened lifespan during the low-carbonizating process of Al_(2)O_(3)-C refractories,nano-crystalline ZrC modified graphite was prepared using Zr powder and flake grap...To address the issues of reduced performance and shortened lifespan during the low-carbonizating process of Al_(2)O_(3)-C refractories,nano-crystalline ZrC modified graphite was prepared using Zr powder and flake graphite as raw materials,with NaCl and NaF mixed salt serving as the medium.The flake graphite was gradually replaced by ZrC modified graphite in the preparation of Al_(2)O_(3)-C refractories,and its impact on the material’s structure and properties was investigated.The results indicate that,compared to samples with only flake graphite,the introduction of 1 mass%to 5 mass%nano-crystalline ZrC modified graphite can significantly enhance the mechanical performance of low-carbon Al_(2)O_(3)-C refractories.When 5 mass%ZrC modified graphite is added,the mechanical properties of the samples are optimal,with the cold modulus of rupture and elastic modulus reaching 22.5 MPa and 65.0 GPa,respectively.展开更多
Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub&...Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.展开更多
Effects of particle size (A:d50 = 336. 9 μm, B:d50 =123.5μm, C: d50=19.5 μm, D: dso=2.21μm) and content (1 wt% , 3 wt% , 5 wt% , 7 wt% ) of silicon powder on cold crushing strength (CCS) , pore size dis...Effects of particle size (A:d50 = 336. 9 μm, B:d50 =123.5μm, C: d50=19.5 μm, D: dso=2.21μm) and content (1 wt% , 3 wt% , 5 wt% , 7 wt% ) of silicon powder on cold crushing strength (CCS) , pore size distribution and microstructure of Al2O3 - ZrO2 - C refractories coked at high temperature had been investigated by means of mercury porosimeter, SEM, EDS, tic. The results indicated that particle size and content of silicon powder affected the cold crushing strength of coked specimens. It increased with the addition of silicon powder and its finer particle size. However, it decreased greatly when using too fine silicon powder. The particle size and content of silicon powder also impacted the phase evolution and microstructure of coked specimens, much more β-SiC whiskers constituted network structure and well distributed in specimens with reduction of their slenderness ratios when finer silicon powder was added, corresponding to that, the specimens' pore size distribution range became narrower with smaller pore diameter, but β-SiC whiskers were distributed sparsely and the specific pore volume of small pores increased when much finer powder was added. It was worthly mentioned that some nitride could form in specimens with addition of appropriate particle size and content of silicon powder.展开更多
文摘To address the issues of reduced performance and shortened lifespan during the low-carbonizating process of Al_(2)O_(3)-C refractories,nano-crystalline ZrC modified graphite was prepared using Zr powder and flake graphite as raw materials,with NaCl and NaF mixed salt serving as the medium.The flake graphite was gradually replaced by ZrC modified graphite in the preparation of Al_(2)O_(3)-C refractories,and its impact on the material’s structure and properties was investigated.The results indicate that,compared to samples with only flake graphite,the introduction of 1 mass%to 5 mass%nano-crystalline ZrC modified graphite can significantly enhance the mechanical performance of low-carbon Al_(2)O_(3)-C refractories.When 5 mass%ZrC modified graphite is added,the mechanical properties of the samples are optimal,with the cold modulus of rupture and elastic modulus reaching 22.5 MPa and 65.0 GPa,respectively.
文摘Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.
文摘Effects of particle size (A:d50 = 336. 9 μm, B:d50 =123.5μm, C: d50=19.5 μm, D: dso=2.21μm) and content (1 wt% , 3 wt% , 5 wt% , 7 wt% ) of silicon powder on cold crushing strength (CCS) , pore size distribution and microstructure of Al2O3 - ZrO2 - C refractories coked at high temperature had been investigated by means of mercury porosimeter, SEM, EDS, tic. The results indicated that particle size and content of silicon powder affected the cold crushing strength of coked specimens. It increased with the addition of silicon powder and its finer particle size. However, it decreased greatly when using too fine silicon powder. The particle size and content of silicon powder also impacted the phase evolution and microstructure of coked specimens, much more β-SiC whiskers constituted network structure and well distributed in specimens with reduction of their slenderness ratios when finer silicon powder was added, corresponding to that, the specimens' pore size distribution range became narrower with smaller pore diameter, but β-SiC whiskers were distributed sparsely and the specific pore volume of small pores increased when much finer powder was added. It was worthly mentioned that some nitride could form in specimens with addition of appropriate particle size and content of silicon powder.