The magnesium matrix composites reinforced by graphite particles and Al2O3 short fibers were fabricated by squeeze-infiltration technique.The additions dispersed uniformly and no agglomeration and casting defect were ...The magnesium matrix composites reinforced by graphite particles and Al2O3 short fibers were fabricated by squeeze-infiltration technique.The additions dispersed uniformly and no agglomeration and casting defect were observed.The microstructures and wear properties of the composites with different Ce contents of 0,0.4%,0.8%and 1.0%,respectively,were investigated.Especially,the effect of Ce on the properties was discussed.The results reveal that Ce enriches around the boundaries of graphite particles and forms Al3Ce phase with Al.The addition of Ce refines the microstructures of the composites.With the increase of Ce content,the grain size becomes smaller and the wear resistance of the composite is improved.At low load,the composites have similar worn surface.At high load,the composite with 1.0%Ce has the best wear resistance due to the existence of Al3Ce phase.The Al3Ce phase improves the thermal stability of the matrix so the graphite particles can keep intact,which can still work as lubricant. At low load,the wear mechanism is abrasive wear and oxidation wear.At high load,the wear mechanism changes to delamination wear for all the composites.展开更多
基金National Natural Science Foundation of China(51165032,51364035)Funded by the Ministry of Education Tied up with the Special Research Fund for the Doctoral Program for Higher School(20133601110001)+2 种基金Innovative Group of Science and Technology of College of Jiangxi Province(00008713)Production and Teaching and Research Cooperation Plan of Nanchang Non-party Experts and Doctor(2012-CYH-DW-XCL-002)Special Funds for Postgraduate Innovation of Jiangxi Province
基金Projects(20085012,20060308)supported by the Development Program of Science and Technology of Jilin Province,ChinaProject supported by"985 Project"of Jilin University,China
文摘The magnesium matrix composites reinforced by graphite particles and Al2O3 short fibers were fabricated by squeeze-infiltration technique.The additions dispersed uniformly and no agglomeration and casting defect were observed.The microstructures and wear properties of the composites with different Ce contents of 0,0.4%,0.8%and 1.0%,respectively,were investigated.Especially,the effect of Ce on the properties was discussed.The results reveal that Ce enriches around the boundaries of graphite particles and forms Al3Ce phase with Al.The addition of Ce refines the microstructures of the composites.With the increase of Ce content,the grain size becomes smaller and the wear resistance of the composite is improved.At low load,the composites have similar worn surface.At high load,the composite with 1.0%Ce has the best wear resistance due to the existence of Al3Ce phase.The Al3Ce phase improves the thermal stability of the matrix so the graphite particles can keep intact,which can still work as lubricant. At low load,the wear mechanism is abrasive wear and oxidation wear.At high load,the wear mechanism changes to delamination wear for all the composites.