Semi-quantitative electron probe microanalysis （EPMA） mapping, scanning electron microscopy （SEM） and transmission electron microscopy （TEM） were employed to study the effect of one-step and two-step treatments ...Semi-quantitative electron probe microanalysis （EPMA） mapping, scanning electron microscopy （SEM） and transmission electron microscopy （TEM） were employed to study the effect of one-step and two-step treatments on the Zr distribution and Al3Zr dispersoid characteristics in as-cast commercial AA7150 aluminum alloy. It is shown that the Zr concentration in the dendrite centre regions is higher than that near the dendrite edges in the as-cast condition, and that homogenization at 460 °C for 20 h is insufficient to remove these concentration gradients. After homogenizing at 460-480 °C, a high number density of larger dispersoids can be observed in dendrite centre regions but not near dendrite edges. Furthermore, the dispersoid size increases with increasing the temperature during both one-step and two-step homogenization treatments.展开更多
The precipitation behaviours of Al3Zr precipitate in the Al-Cu-Zr and Al-Cu-Zr-Ti-V alloys were studied by transmission electron microscopy. Metastable Al3Zr precipitates are homogeneously nucleated in dendrite centre...The precipitation behaviours of Al3Zr precipitate in the Al-Cu-Zr and Al-Cu-Zr-Ti-V alloys were studied by transmission electron microscopy. Metastable Al3Zr precipitates are homogeneously nucleated in dendrite centres resulting in homogeneous distribution. However, the precipitation in the interdendritic regions is complex and the precipitation morphologies, helical-like and stripe-like shapes, were observed, which are composed of many spherical Al3Zr precipitates. The stripe-like precipitate clusters have preferential orientations along with the -100- Al directions, which is inferred to be related to θ′（Al2Cu） and θ phases. Addition of Cu can accelerate the L12→D023 structural transformation of the Al3Zr precipitate.展开更多
文摘Semi-quantitative electron probe microanalysis （EPMA） mapping, scanning electron microscopy （SEM） and transmission electron microscopy （TEM） were employed to study the effect of one-step and two-step treatments on the Zr distribution and Al3Zr dispersoid characteristics in as-cast commercial AA7150 aluminum alloy. It is shown that the Zr concentration in the dendrite centre regions is higher than that near the dendrite edges in the as-cast condition, and that homogenization at 460 °C for 20 h is insufficient to remove these concentration gradients. After homogenizing at 460-480 °C, a high number density of larger dispersoids can be observed in dendrite centre regions but not near dendrite edges. Furthermore, the dispersoid size increases with increasing the temperature during both one-step and two-step homogenization treatments.
基金Project (CDJZR12130048) supported by the Fundamental Research Funds for the Central Universities, ChinaProject supported by a Grant from the French Norwegian Foundation for Scientific and Technological Research and Industrial Development
文摘The precipitation behaviours of Al3Zr precipitate in the Al-Cu-Zr and Al-Cu-Zr-Ti-V alloys were studied by transmission electron microscopy. Metastable Al3Zr precipitates are homogeneously nucleated in dendrite centres resulting in homogeneous distribution. However, the precipitation in the interdendritic regions is complex and the precipitation morphologies, helical-like and stripe-like shapes, were observed, which are composed of many spherical Al3Zr precipitates. The stripe-like precipitate clusters have preferential orientations along with the -100- Al directions, which is inferred to be related to θ′（Al2Cu） and θ phases. Addition of Cu can accelerate the L12→D023 structural transformation of the Al3Zr precipitate.
