Microstructure evolution and mechanical properties of the aging treated AlN/AZ91 composites were systematically investigated by optical microscopy(OM),high resolution scanning electron microscopy(HRSEM)with an energy ...Microstructure evolution and mechanical properties of the aging treated AlN/AZ91 composites were systematically investigated by optical microscopy(OM),high resolution scanning electron microscopy(HRSEM)with an energy dispersive spectrum(EDS),and high-angle annular dark field scanning transmission electron microscopy(HAADF-STEM).The results show that the higher fracture elongation(14±1%)and ultimate tensile strength(275±6 MPa)were simultaneously obtained in the peak-aged AlN/AZ91 composites.Comparied with AZ91 matrix alloy,the strength was increased by about 44%and the elongation was approximately five times higher,which mainly attributed to the precipitation of nano-sizedγ-Mg_(17)Al_(12)phase and the activation of non-basal slip systems induced by in-situ AlN particles at room temperature.However,the in-situ formation of AlN reinforcements consumed part of Al element in the matrix alloy,which resulted into the volume fraction decreasing ofγ-Mg_(17)Al_(12)precipitates,and then the age hardening and strengthening efficiency were reduced in the AlN/AZ91 composites.On the other hand,the mismatch of thermal expansion coefficient between AlN particles and AZ91 matrix generated high density dislocations around AlN particles,which promoted the precipitation ofγ-Mg_(17)Al_(12)phase,and then the peak aging time and temperature were decreased.展开更多
In this study, magnesium matrix composites reinforced with different loading of AlN particles were fabricated by the powder metallurgy technique. The microstructure, bending strength and fracture behavior of the resul...In this study, magnesium matrix composites reinforced with different loading of AlN particles were fabricated by the powder metallurgy technique. The microstructure, bending strength and fracture behavior of the resulting Mg-Al/Al N composites were investigated. It showed that the 5 wt% AlN reinforcements led to the highest densification and bending strength. The total strengthening effect of AlN particles was predicted by considering the contributions of CTE mismatch between the matrix and the particles,load bearing and Hall-Petch mechanism. The results revealed that the increase of dislocation density,the change of Mg17Al12 phase morphology, and the effective load transfer were the major strengthening contributors to the composites. The fracture of the composites altered from plastic to brittle mode with increasing reinforcement content. The regions of clustered particles in the composites were easy to be damaged under external load, and the fracture occurred mainly along grain boundaries.展开更多
基金support for this research by the National Natural Science Foundation of China(Grant Nos.52071268,51771151)Key Laboratory of Interface Science and Engineering in Advanced Materials,Ministry of Education,Taiyuan University of Technology,Taiyuan 030024,China(Grant No.KLISEAM201603)+1 种基金State Key Laboratory of Advanced Metals and Materials(Grant No.2019-Z06)the Innovation Foundation for Doctor Dissertation of Northwestern Polytechnical University,China(Grant No.CX201905).
文摘Microstructure evolution and mechanical properties of the aging treated AlN/AZ91 composites were systematically investigated by optical microscopy(OM),high resolution scanning electron microscopy(HRSEM)with an energy dispersive spectrum(EDS),and high-angle annular dark field scanning transmission electron microscopy(HAADF-STEM).The results show that the higher fracture elongation(14±1%)and ultimate tensile strength(275±6 MPa)were simultaneously obtained in the peak-aged AlN/AZ91 composites.Comparied with AZ91 matrix alloy,the strength was increased by about 44%and the elongation was approximately five times higher,which mainly attributed to the precipitation of nano-sizedγ-Mg_(17)Al_(12)phase and the activation of non-basal slip systems induced by in-situ AlN particles at room temperature.However,the in-situ formation of AlN reinforcements consumed part of Al element in the matrix alloy,which resulted into the volume fraction decreasing ofγ-Mg_(17)Al_(12)precipitates,and then the age hardening and strengthening efficiency were reduced in the AlN/AZ91 composites.On the other hand,the mismatch of thermal expansion coefficient between AlN particles and AZ91 matrix generated high density dislocations around AlN particles,which promoted the precipitation ofγ-Mg_(17)Al_(12)phase,and then the peak aging time and temperature were decreased.
基金financially supported by the State Key Laboratory for Mechanical Behavior of Materials (No. 20151712)
文摘In this study, magnesium matrix composites reinforced with different loading of AlN particles were fabricated by the powder metallurgy technique. The microstructure, bending strength and fracture behavior of the resulting Mg-Al/Al N composites were investigated. It showed that the 5 wt% AlN reinforcements led to the highest densification and bending strength. The total strengthening effect of AlN particles was predicted by considering the contributions of CTE mismatch between the matrix and the particles,load bearing and Hall-Petch mechanism. The results revealed that the increase of dislocation density,the change of Mg17Al12 phase morphology, and the effective load transfer were the major strengthening contributors to the composites. The fracture of the composites altered from plastic to brittle mode with increasing reinforcement content. The regions of clustered particles in the composites were easy to be damaged under external load, and the fracture occurred mainly along grain boundaries.