A large single crystal of TPAF-AlPO4-5 molecular sieve was synthesized by hydrothermal crystallization in the presence of ammonium fluoride. Starting material composition was · 1 P2O5 · 1 Al2O3 · 2. 2 T...A large single crystal of TPAF-AlPO4-5 molecular sieve was synthesized by hydrothermal crystallization in the presence of ammonium fluoride. Starting material composition was · 1 P2O5 · 1 Al2O3 · 2. 2 TPAOH · 1. 7 NH4F ·318 H2O. The crystal size has a hexagonal prism with 80μm across and 500μm length.The structure of tetrapropylarnmonium fluoride - aluminium phosphate type-5 was investigated with X-ray diffraction. The unit cell composition is 12AlPO4 · TPAF, space group P6cc (a= 13. 740(5), c= 8. 474(4) A ). Average bond distances are: P-O 1. 564A and Al-O 1. 640A ,which may be due to the partial disorder of the arrangement of P, Al in the framework. The angles of O-T-O and T-O-T (T?P, Al) are 102-116° and 148-176°, respectively. Residue electron density was not well enough defined to give a precise position for tetrapropylammonium fluoride (TPAF). The template agent, TPA+ cations, situate in the 12-ring channels and F- anions locate in double 4-rings near the 12-ring channels. Fixing atomic positions for the TPAF reduced the unweighted and weighted R, R, from 0. 063 and 0. 082 to 0. 046 and 0. 042,respectively.展开更多
Large AlPO4-5 molecular sieve single crystals with high optical quality were synthesized hydrothermally by using TPA as template. As-synthesized crystals were calcined under O2 atmosphere to remove the organic templat...Large AlPO4-5 molecular sieve single crystals with high optical quality were synthesized hydrothermally by using TPA as template. As-synthesized crystals were calcined under O2 atmosphere to remove the organic templates in the channels. Disperse-Red-1 （DR1） and p-nitroaniline （pNA） molecules have been successfully incorporated into the one-dimensional channels of AlPO4-5 single crystals respectively by means of vapor phase diffusion. XRD patterns reveal that the loading of organic molecules has not destroyed the structures of AlPO4-5 crystals. Polarizing microscope and SHG results indicate that the DR1 and pNA molecules are well aligned in a preferred direction along the crystal channels. The different polarization-dependence SH intensity shows that different SHG processes occur in the DR1- and pNA-loaded AlPO4-5 crystals.展开更多
文摘A large single crystal of TPAF-AlPO4-5 molecular sieve was synthesized by hydrothermal crystallization in the presence of ammonium fluoride. Starting material composition was · 1 P2O5 · 1 Al2O3 · 2. 2 TPAOH · 1. 7 NH4F ·318 H2O. The crystal size has a hexagonal prism with 80μm across and 500μm length.The structure of tetrapropylarnmonium fluoride - aluminium phosphate type-5 was investigated with X-ray diffraction. The unit cell composition is 12AlPO4 · TPAF, space group P6cc (a= 13. 740(5), c= 8. 474(4) A ). Average bond distances are: P-O 1. 564A and Al-O 1. 640A ,which may be due to the partial disorder of the arrangement of P, Al in the framework. The angles of O-T-O and T-O-T (T?P, Al) are 102-116° and 148-176°, respectively. Residue electron density was not well enough defined to give a precise position for tetrapropylammonium fluoride (TPAF). The template agent, TPA+ cations, situate in the 12-ring channels and F- anions locate in double 4-rings near the 12-ring channels. Fixing atomic positions for the TPAF reduced the unweighted and weighted R, R, from 0. 063 and 0. 082 to 0. 046 and 0. 042,respectively.
文摘Large AlPO4-5 molecular sieve single crystals with high optical quality were synthesized hydrothermally by using TPA as template. As-synthesized crystals were calcined under O2 atmosphere to remove the organic templates in the channels. Disperse-Red-1 （DR1） and p-nitroaniline （pNA） molecules have been successfully incorporated into the one-dimensional channels of AlPO4-5 single crystals respectively by means of vapor phase diffusion. XRD patterns reveal that the loading of organic molecules has not destroyed the structures of AlPO4-5 crystals. Polarizing microscope and SHG results indicate that the DR1 and pNA molecules are well aligned in a preferred direction along the crystal channels. The different polarization-dependence SH intensity shows that different SHG processes occur in the DR1- and pNA-loaded AlPO4-5 crystals.