The Sm–Zr–Fe–Co–Ti quinary-alloys with ThMn12 structure has attracted wide attention for ultra-high intrinsic magnetic properties,showing potentiality to be developed into rare-earth permanent magnets.The Ti eleme...The Sm–Zr–Fe–Co–Ti quinary-alloys with ThMn12 structure has attracted wide attention for ultra-high intrinsic magnetic properties,showing potentiality to be developed into rare-earth permanent magnets.The Ti element in alloys is crucial for phase stability and magnetic properties,and lower Ti content can increase intrinsic magnetic properties but reduce phase stability.In this study,the 1:12 single-phase melt-spun ribbons with low Ti content was successfully prepared using a rapid solidification non-equilibrium method for the Sm1.1Zr_(0.2)Fe_(9.2)Co_(2.3)Ti_(0.5) quinary-alloy.However,this non-equilibrium ribbon did not achieve good magnetic hardening due to the uneven microstructure and microstrain.Then,annealing was carried out to eliminate micro-strain and homogenize microstructure,therefore,remanence and coercivity were significantly improved even the precipitation of a small amount of a-Fe phase which were not conducive to coercivity.The remanence of 86.1 emu/g and coercivity of 151 kA/m was achieved when annealing at 850℃ for 45 min.After hot pressing,under the action of high temperature and pressure,a small portion of ThMn12 phases in the magnet decompose into Sm-rich phases and a-Fe,while remanence of 4.02 kGs(1 Gs=10^(-4) T),and coercivity of 1.12 kOe(1 Oe=79.5775 A·m^(-1))were still acquired.Our findings can provide reference for exploring practical permanent magnets made of 1:12 type quinary-alloys.展开更多
基金the National Key Research and De-velopment Program of China(Grant No.2021YFB3500300)the National Natural Science Foundation of China(Grant No.51931007)the Program of Top Disciplines Construc-tion in Beijing(Grant No.PXM2019014204500031).
文摘The Sm–Zr–Fe–Co–Ti quinary-alloys with ThMn12 structure has attracted wide attention for ultra-high intrinsic magnetic properties,showing potentiality to be developed into rare-earth permanent magnets.The Ti element in alloys is crucial for phase stability and magnetic properties,and lower Ti content can increase intrinsic magnetic properties but reduce phase stability.In this study,the 1:12 single-phase melt-spun ribbons with low Ti content was successfully prepared using a rapid solidification non-equilibrium method for the Sm1.1Zr_(0.2)Fe_(9.2)Co_(2.3)Ti_(0.5) quinary-alloy.However,this non-equilibrium ribbon did not achieve good magnetic hardening due to the uneven microstructure and microstrain.Then,annealing was carried out to eliminate micro-strain and homogenize microstructure,therefore,remanence and coercivity were significantly improved even the precipitation of a small amount of a-Fe phase which were not conducive to coercivity.The remanence of 86.1 emu/g and coercivity of 151 kA/m was achieved when annealing at 850℃ for 45 min.After hot pressing,under the action of high temperature and pressure,a small portion of ThMn12 phases in the magnet decompose into Sm-rich phases and a-Fe,while remanence of 4.02 kGs(1 Gs=10^(-4) T),and coercivity of 1.12 kOe(1 Oe=79.5775 A·m^(-1))were still acquired.Our findings can provide reference for exploring practical permanent magnets made of 1:12 type quinary-alloys.
