A type of polymer-coated Al2O3/ZrO2/TiC ceramic powder was prepared. The laser sintering mechanism of polymer-coated Al2O3/ZrO2/TiC powder was investigated by studying the dynamic laser sintering process. It is found ...A type of polymer-coated Al2O3/ZrO2/TiC ceramic powder was prepared. The laser sintering mechanism of polymer-coated Al2O3/ZrO2/TiC powder was investigated by studying the dynamic laser sintering process. It is found that the mechanism is viscous flow when the sintering temperature is between 80 ℃ and 120 ℃, and it is melting/solidification when the temperature is above 120 ℃. The process parameters of selective laser sintering were optimized by using ortho-design method. The results show that the optimal parameters include laser power of 14 W, scanning velocity of 1 400 mm/s, preheating temperature of 50 ℃ and powder depth of 0.15 mm. A two-step post-treatment process is adopted to improve the mechanical properties of laser sintered part, which includes polymer debinding and high temperature sintering. After vacuum sintering for 2 h at 1 650 ℃, the bending strength and fracture toughness of Al2O3/ZrO2/TiC ceramic part reach 358 MPa and 6.9 MPa·m1/2, respectively.展开更多
The reduction rate of Fe^tO in CaOSiO_2Al_2O_3Fe_tO slags with graphite powder has been determined in an alumina crucible at 1 673-1 823 K. The effects of temperature, slag basicity and Fe_tO content on the reduc...The reduction rate of Fe^tO in CaOSiO_2Al_2O_3Fe_tO slags with graphite powder has been determined in an alumina crucible at 1 673-1 823 K. The effects of temperature, slag basicity and Fe_tO content on the reduction rate have also been discussed. Test results show that the reduction rate increases with the increase of temperature or Fe_tO concentration in slags, and the reduction rate has a parabolic relation with slag simple basicity or optical basicity. The maximum reduction rate is observed around CaO/SiO_2=1.5 of molten slags. The reaction order is 1.26 or 1.31, and the reduction activation energy is 126.8 or 129.7 kJ/mol respectively in regard to Fe_tO content or Fe_tO activity calculated by using regular solution model. The reduction rate of Fe_tO in CaOSiO_2Al_2O_3Fe_tO slags with graphite powder is in the range of 0.15×10^-4-0.86×10^-4 molO/cm^2·s.展开更多
基金Project(03022) supported by the Key Science Research Program of Education Ministry of China
文摘A type of polymer-coated Al2O3/ZrO2/TiC ceramic powder was prepared. The laser sintering mechanism of polymer-coated Al2O3/ZrO2/TiC powder was investigated by studying the dynamic laser sintering process. It is found that the mechanism is viscous flow when the sintering temperature is between 80 ℃ and 120 ℃, and it is melting/solidification when the temperature is above 120 ℃. The process parameters of selective laser sintering were optimized by using ortho-design method. The results show that the optimal parameters include laser power of 14 W, scanning velocity of 1 400 mm/s, preheating temperature of 50 ℃ and powder depth of 0.15 mm. A two-step post-treatment process is adopted to improve the mechanical properties of laser sintered part, which includes polymer debinding and high temperature sintering. After vacuum sintering for 2 h at 1 650 ℃, the bending strength and fracture toughness of Al2O3/ZrO2/TiC ceramic part reach 358 MPa and 6.9 MPa·m1/2, respectively.
文摘The reduction rate of Fe^tO in CaOSiO_2Al_2O_3Fe_tO slags with graphite powder has been determined in an alumina crucible at 1 673-1 823 K. The effects of temperature, slag basicity and Fe_tO content on the reduction rate have also been discussed. Test results show that the reduction rate increases with the increase of temperature or Fe_tO concentration in slags, and the reduction rate has a parabolic relation with slag simple basicity or optical basicity. The maximum reduction rate is observed around CaO/SiO_2=1.5 of molten slags. The reaction order is 1.26 or 1.31, and the reduction activation energy is 126.8 or 129.7 kJ/mol respectively in regard to Fe_tO content or Fe_tO activity calculated by using regular solution model. The reduction rate of Fe_tO in CaOSiO_2Al_2O_3Fe_tO slags with graphite powder is in the range of 0.15×10^-4-0.86×10^-4 molO/cm^2·s.