The kinetics of reductive leaching of manganese from low grade pyrolusite in dilute sulfuric acid in the presence of molasses alcohol wastewater was investigated. The shrinking core model was applied to quantify the e...The kinetics of reductive leaching of manganese from low grade pyrolusite in dilute sulfuric acid in the presence of molasses alcohol wastewater was investigated. The shrinking core model was applied to quantify the effects of reaction parameters on leaching rate. The leaching rate increases with reaction temperature, concentrations of H 2 SO 4 and organic matter in molasses alcohol wastewater increase and ore particle size decreases. The leaching process follows the kinetics of a shrinking core model and the apparent activation energy is 57.5 kJ·mol –1 . The experimental results indicate a reaction order of 0.52 for H2SO4 concentration and 0.90 for chemical oxygen demand (COD) of molasses alcohol wastewater. It is concluded that the reductive leaching of pyrolusite with molasses alcohol wastewater is controlled by the diffusion through the ash/inert layer composed of the associated minerals.展开更多
Gasification of polyvinyl alcohol （PVA）-contaminated wastewater in supercritical water （SCW） was investigated in a continuous flow reactor at 723-873 K, 20-36 MPa and residence time of 20-450 s. The gas and liquid...Gasification of polyvinyl alcohol （PVA）-contaminated wastewater in supercritical water （SCW） was investigated in a continuous flow reactor at 723-873 K, 20-36 MPa and residence time of 20-450 s. The gas and liquid products were analyzed by GC/TCD, and TOC analyzer. The main gas products were H2, CH4, CO and CO2. Pressure change had no significant influence on gasification efficiency. Higher temperature and longer residence time enhanced gasification efficiency, and lower temperature favored the production of H2. The effects of KOH catalyst on gas product composition were studied, and gasification efficiency were analyzed. The TOC removal efficiency （RTOC）, carbon gasification ratio （RCG） and hydrogen gasification ratio （RHG） were up to 96.00%, 95.92% and 126.40% at 873 K and 60 s, respectively, which suggests PVA can be completely gasified in SCW. The results indicate supercritical water gasification for hydrogen generation is a promising process for the treatment ofPVA wastewater.展开更多
基金Supported by the National Natural Science Foundation of China （20866001） the Natural Science Foundation of GuangxiProvince （0832035）
文摘The kinetics of reductive leaching of manganese from low grade pyrolusite in dilute sulfuric acid in the presence of molasses alcohol wastewater was investigated. The shrinking core model was applied to quantify the effects of reaction parameters on leaching rate. The leaching rate increases with reaction temperature, concentrations of H 2 SO 4 and organic matter in molasses alcohol wastewater increase and ore particle size decreases. The leaching process follows the kinetics of a shrinking core model and the apparent activation energy is 57.5 kJ·mol –1 . The experimental results indicate a reaction order of 0.52 for H2SO4 concentration and 0.90 for chemical oxygen demand (COD) of molasses alcohol wastewater. It is concluded that the reductive leaching of pyrolusite with molasses alcohol wastewater is controlled by the diffusion through the ash/inert layer composed of the associated minerals.
基金Project supported by the National Natural Science Foundation of China(No.20277010)the Hi-Tech Research and Development Program(863) of China(No.2006AA062378).
文摘Gasification of polyvinyl alcohol （PVA）-contaminated wastewater in supercritical water （SCW） was investigated in a continuous flow reactor at 723-873 K, 20-36 MPa and residence time of 20-450 s. The gas and liquid products were analyzed by GC/TCD, and TOC analyzer. The main gas products were H2, CH4, CO and CO2. Pressure change had no significant influence on gasification efficiency. Higher temperature and longer residence time enhanced gasification efficiency, and lower temperature favored the production of H2. The effects of KOH catalyst on gas product composition were studied, and gasification efficiency were analyzed. The TOC removal efficiency （RTOC）, carbon gasification ratio （RCG） and hydrogen gasification ratio （RHG） were up to 96.00%, 95.92% and 126.40% at 873 K and 60 s, respectively, which suggests PVA can be completely gasified in SCW. The results indicate supercritical water gasification for hydrogen generation is a promising process for the treatment ofPVA wastewater.