Five types of rare earth/alkaline earth oxide-doped CeO2 superfine-powders were synthesized by a low-temperature combustion technique. The relevant solid electrolyte materials were also sintered by pressureless sinter...Five types of rare earth/alkaline earth oxide-doped CeO2 superfine-powders were synthesized by a low-temperature combustion technique. The relevant solid electrolyte materials were also sintered by pressureless sintering at different temperatures. The results of X-ray diffraction and transmission electron microscopy showed that the grain size of the powders was approximately 20-30 nm, and rare earth/alkaline earth oxides were completely dissolved into ceria-based solid solution with fluorite structure. The electrical conductivities of the SmzO3-CeO2 system were measured by the ac impedance technique in air at temperatures ranging from 513-900℃. The results indicated that the ionic conductivities of Srno.2oCe0.8Ol.875 solid electrolyte increase with increasing sintering temperature, and the relationship between the conductivities and measuring temperature obeys the An＇henius equation. Then the SmzO3-CeO2 material was further doped with other rare earth/alkaline earth oxide, and the conductivities improve with the effective index.展开更多
Methane conversions at lower temperature were studied. The aetivity of Y_2O_3 sample at 823K was fairly high with some formation of C_2H_4 and C_2H_6, the catalysts based on alkaline earth oxides and yttria would give...Methane conversions at lower temperature were studied. The aetivity of Y_2O_3 sample at 823K was fairly high with some formation of C_2H_4 and C_2H_6, the catalysts based on alkaline earth oxides and yttria would give better results. The influences of flux ratio, space velocity, and reaction temperature were also discussed.展开更多
In gaseous reduction of iron ore fines, alkaline earth oxides have profound effects on the precipitation behavior of fresh metal- lic iron on the particle surface. In this work, in situ observation was performed to re...In gaseous reduction of iron ore fines, alkaline earth oxides have profound effects on the precipitation behavior of fresh metal- lic iron on the particle surface. In this work, in situ observation was performed to reveal the influence of alkaline earth oxides on the precipitation morphology and micro-structure variation of fresh metallic iron from microscopic level by simulation of the gas-solid reaction condition on the surface of ore particles. Experimental results indicate that doping MgO in the particle surface can inhibit the reduction of iron oxide and however doping CaO, SrO and BaO promote; all alkaline earth oxides tested in this study can change the precipitation morphology of fresh metallic iron; minimum doping mole fraction of one oxide to inhibit iron whiskers growth （ NAO ） is related to its cation radius （ r：＋ ） and its extranuclear electronic layers（nAD ）, which can be expressed as NAO = 1.3 × 10^-5r^2AD,√nA^2.展开更多
Several compounds of rare earth complex oxides containing manganese and titanium were synthesized in Ar, and their crystal structures were analyzed by powder X-ray diffraction data and Rietveld method. Structures of A...Several compounds of rare earth complex oxides containing manganese and titanium were synthesized in Ar, and their crystal structures were analyzed by powder X-ray diffraction data and Rietveld method. Structures of A0.67Ln0.33 Mn0.33Ti0.6703（A = Ca or Sr and Ln = rare earth） were found to have orthorhombic symmetry with the space group Pnrna, and their interatomic distances and bond angles were obtained. This space group was also derived from electron microscopic study. Electrical conductivity of Cao.67Ln0.33Mn0.33Ti0.6703 for several rare earth elements showed a semiconducting property with the activation energy of 0.4 eV. Some of these compounds of the strontium system show the antiferromagnetic properties below 10 K.展开更多
文摘Five types of rare earth/alkaline earth oxide-doped CeO2 superfine-powders were synthesized by a low-temperature combustion technique. The relevant solid electrolyte materials were also sintered by pressureless sintering at different temperatures. The results of X-ray diffraction and transmission electron microscopy showed that the grain size of the powders was approximately 20-30 nm, and rare earth/alkaline earth oxides were completely dissolved into ceria-based solid solution with fluorite structure. The electrical conductivities of the SmzO3-CeO2 system were measured by the ac impedance technique in air at temperatures ranging from 513-900℃. The results indicated that the ionic conductivities of Srno.2oCe0.8Ol.875 solid electrolyte increase with increasing sintering temperature, and the relationship between the conductivities and measuring temperature obeys the An＇henius equation. Then the SmzO3-CeO2 material was further doped with other rare earth/alkaline earth oxide, and the conductivities improve with the effective index.
文摘Methane conversions at lower temperature were studied. The aetivity of Y_2O_3 sample at 823K was fairly high with some formation of C_2H_4 and C_2H_6, the catalysts based on alkaline earth oxides and yttria would give better results. The influences of flux ratio, space velocity, and reaction temperature were also discussed.
基金supported by the National Natural Science Foundation of China and Baosteel (Grant No.50834007)the National Basic Research Program of China (973 Program) (Grant No.2012CB720401)
文摘In gaseous reduction of iron ore fines, alkaline earth oxides have profound effects on the precipitation behavior of fresh metal- lic iron on the particle surface. In this work, in situ observation was performed to reveal the influence of alkaline earth oxides on the precipitation morphology and micro-structure variation of fresh metallic iron from microscopic level by simulation of the gas-solid reaction condition on the surface of ore particles. Experimental results indicate that doping MgO in the particle surface can inhibit the reduction of iron oxide and however doping CaO, SrO and BaO promote; all alkaline earth oxides tested in this study can change the precipitation morphology of fresh metallic iron; minimum doping mole fraction of one oxide to inhibit iron whiskers growth （ NAO ） is related to its cation radius （ r：＋ ） and its extranuclear electronic layers（nAD ）, which can be expressed as NAO = 1.3 × 10^-5r^2AD,√nA^2.
基金Foundation ite ms:Project supported bythe Grant-in-Aidfor Scientific Research (C) (18560662) bythe Japan Societyfor the Promotion of Science
文摘Several compounds of rare earth complex oxides containing manganese and titanium were synthesized in Ar, and their crystal structures were analyzed by powder X-ray diffraction data and Rietveld method. Structures of A0.67Ln0.33 Mn0.33Ti0.6703（A = Ca or Sr and Ln = rare earth） were found to have orthorhombic symmetry with the space group Pnrna, and their interatomic distances and bond angles were obtained. This space group was also derived from electron microscopic study. Electrical conductivity of Cao.67Ln0.33Mn0.33Ti0.6703 for several rare earth elements showed a semiconducting property with the activation energy of 0.4 eV. Some of these compounds of the strontium system show the antiferromagnetic properties below 10 K.