A series of polyesteramide prepolymers[PrePEA（0/4,8）s] having mixed alternating bisesterdiamide units was synthesized via melt polycondensation from N,N＇-bis（2-hydroxyethyl）oxamide（0） and N,N＇-bis（2-hydroxyet...A series of polyesteramide prepolymers[PrePEA（0/4,8）s] having mixed alternating bisesterdiamide units was synthesized via melt polycondensation from N,N＇-bis（2-hydroxyethyl）oxamide（0） and N,N＇-bis（2-hydroxyethyl）-adipamide（4） with sebacic acid（8） at different molar ratios.Chain extension of them was conducted with 2,2＇-（1,4-phenylene）-bis（2-oxazoline） and adipoyl biscaprolactamate as combined chain extenders.The chain extended polyesteramides[ExtPEA（0/4,8）s] were characterized by proton nuclear magnetic resonance（1H NMR）,gel permeation chromatography（GPC）,differential scanning calorimetry（DSC）,thermogravimetry analysis（TGA）,wide angle X-ray scattering,tensile test and enzymatic degradation.The results show that ExtPEA（0/4,8）s were crystalline polyesteramides.They had Tm up to 136.5 ℃ and initial decomposition temperature above 297.5 ℃.They crystallized in similar crystallites into Nylon-66 and degraded under the catalysis of protease or lipase.They are thermoplastic materials with tensile strength up to 21.5 MPa and elongation at break above 64.0％.展开更多
Two kinds of aliphatic alternating polyesteramide prepolymers were prepared through melt polycondensation from N,N＇-bis（2-hydroxyethyl）-adipamide and adipic acid or sebacic acid. Chain extension of them was conduct...Two kinds of aliphatic alternating polyesteramide prepolymers were prepared through melt polycondensation from N,N＇-bis（2-hydroxyethyl）-adipamide and adipic acid or sebacic acid. Chain extension of them was conducted with 2,2＇-（1,4- phenylene）-bis（2-oxazoline） and adipoyl biscaprolactamate as combined chain extenders. The chain extended polyesteramides （ExtPEAs） were characterized by IR, 1H-NMR, differential scanning calorimetry, thermogravimetric analysis, wide angle X-ray scattering, tensile test and enzymatic degradation. The results showed that the ExtPEA（4,m）s were mainly constituted with the diester adipamide alternating units. ExtPEA（4,4） and ExtPEA（4,8） had Tm of 83.8℃ and 85.8℃ and initial decomposition temperature above 310.0℃. They crystallized similarly as Nylon-66 did and were flexible thermoplastic materials with tensile strength up to 25.64 MPa and strain at break up to 737%.展开更多
基金Supported by the National Natural Science Foundation of China（Nos.50873013, 21244006）.
文摘A series of polyesteramide prepolymers[PrePEA（0/4,8）s] having mixed alternating bisesterdiamide units was synthesized via melt polycondensation from N,N＇-bis（2-hydroxyethyl）oxamide（0） and N,N＇-bis（2-hydroxyethyl）-adipamide（4） with sebacic acid（8） at different molar ratios.Chain extension of them was conducted with 2,2＇-（1,4-phenylene）-bis（2-oxazoline） and adipoyl biscaprolactamate as combined chain extenders.The chain extended polyesteramides[ExtPEA（0/4,8）s] were characterized by proton nuclear magnetic resonance（1H NMR）,gel permeation chromatography（GPC）,differential scanning calorimetry（DSC）,thermogravimetry analysis（TGA）,wide angle X-ray scattering,tensile test and enzymatic degradation.The results show that ExtPEA（0/4,8）s were crystalline polyesteramides.They had Tm up to 136.5 ℃ and initial decomposition temperature above 297.5 ℃.They crystallized in similar crystallites into Nylon-66 and degraded under the catalysis of protease or lipase.They are thermoplastic materials with tensile strength up to 21.5 MPa and elongation at break above 64.0％.
基金financially supported by the National Natural Science Foundation of China (Nos.50873013 and 21244006)
文摘Two kinds of aliphatic alternating polyesteramide prepolymers were prepared through melt polycondensation from N,N＇-bis（2-hydroxyethyl）-adipamide and adipic acid or sebacic acid. Chain extension of them was conducted with 2,2＇-（1,4- phenylene）-bis（2-oxazoline） and adipoyl biscaprolactamate as combined chain extenders. The chain extended polyesteramides （ExtPEAs） were characterized by IR, 1H-NMR, differential scanning calorimetry, thermogravimetric analysis, wide angle X-ray scattering, tensile test and enzymatic degradation. The results showed that the ExtPEA（4,m）s were mainly constituted with the diester adipamide alternating units. ExtPEA（4,4） and ExtPEA（4,8） had Tm of 83.8℃ and 85.8℃ and initial decomposition temperature above 310.0℃. They crystallized similarly as Nylon-66 did and were flexible thermoplastic materials with tensile strength up to 25.64 MPa and strain at break up to 737%.