Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub&...Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.展开更多
Optically transparent alumina ceramics were fabricated by conventional process and sintered without pressure in H2 atmosphere. The results indicate that relative densities of alumina specimens increase to theoretical ...Optically transparent alumina ceramics were fabricated by conventional process and sintered without pressure in H2 atmosphere. The results indicate that relative densities of alumina specimens increase to theoretical densities （T. D. ） with increasing content of La2O3. With increasing holding time during sintering, much less pores and larger grains were found in the sintered alumina samples. Higher transmittance was achieved in alumina codoped with MgO and La2O3 as compared with that doped with MgO only. The total-transmittance of alumina sample is up to 86% at twavelength range of 300 - 800 nm.展开更多
The catalytic hydrogenation of p-nitrophenol to p-aminophenol was investigated over Ni/Al2O3 catalyst on alumina support with different particle size. It is found that support particle size has significant influences ...The catalytic hydrogenation of p-nitrophenol to p-aminophenol was investigated over Ni/Al2O3 catalyst on alumina support with different particle size. It is found that support particle size has significant influences on physiochemical properties and catalytic activity of the resulting Ni/Al2O3 catalyst, but little influence on the selec-tivity. At a comparable amount of Ni loading, the catalytic activity of Ni/Al2O3 prepared with alumina support of smaller particle size is lower. The reduction behavior of the catalyst is a key factor in determining the catalytic activity of Ni/Al2O3 catalyst. The supported nickel catalyst 10.3Ni/Al2O3-3 improves the life span of the membrane by reducing fouling on the membrane surface compared to nano-sized nickel.展开更多
This work reports the influence of alumina fiber reinforcement of an AZ91Nd MMC(metal matrix composite)on the PEO coating formation process in a sodium phosphate-based electrolyte.By comparison with the pure AZ91Nd,th...This work reports the influence of alumina fiber reinforcement of an AZ91Nd MMC(metal matrix composite)on the PEO coating formation process in a sodium phosphate-based electrolyte.By comparison with the pure AZ91Nd,the evolution of alumina fiber during the processing and the characteristics of the resultant PEO coating were investigated.The voltage response as a function of processing time was changed.Lower voltage in the presence of alumina fiber is responsible for the lower coating thickness.The morphology and phase composition of the coatings are also influenced by the incorporation of the fiber.Firstly,the fiber is embedded in the coating and interrupts the continuity of the coating.With increasing processing time,the fiber is found to be reactively incorporated in the coating.The intention to produce a MgAl_(2)O_(4)containing coating is achieved and it is mainly accumulated near the coating surface.However,due to the low number of fibers,the Al content is overall still low and only near to the fibers the MgAl_(2)O_(4)spinel phase can form.展开更多
Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass r...Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass ratio of CaO to Al_2O_3 on surface tension were investigated.The results indicate that surface tension decreased with increasing MgO content(from 0 to 4.86%),followed by an increase with further increasing MgO content up to 11.33%.The trend that surface tension changed with the mass ratio of CaO to Al_2O_3 was the same as the trend that surface tension changed with the MgO content.The surface tension was varied from 0.617 N/m to 0.710 N/m,for the mass ratio of CaO to Al_2O_3 varying between 0.60 and 1.28.An attempt was made to estimate surface tension of CaO-Al_2O_3-MgO slag and its sub-system,and the application showed that the model worked well.展开更多
Alumina coated LiNi1/3Mn1/3Co1/3O2 particles were obtained by a simple method of solid state reaction at room temperature. The reaction mechanism of solid state reaction at room temperature was investigated. The struc...Alumina coated LiNi1/3Mn1/3Co1/3O2 particles were obtained by a simple method of solid state reaction at room temperature. The reaction mechanism of solid state reaction at room temperature was investigated. The structure and morphology of the coating materials were investigated by XRD, SEM and TEM. The electrochemical performances of uncoated and Al2O3-coated LiNi1/3Co1/3Mn1/3O2 cathode materials were studied within a voltage window of 3.00?4.35 V at current density of 30 mA/g. SEM, TEM and EDS analytical results indicate that the surface of LiNi1/3Mn1/3Co1/3O2 particles is coated with very fine Al2O3 composite, which leads to the improved cycle ability though a slight decrease in the first discharge capacity is observed. It is proposed that surface treatment by solid state reaction at room temperature is a simple and effective method to improve the cycle performance of LiNi1/3Co1/3Mn1/3O2 particles.展开更多
以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO ...以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO 颗粒以 2 2 3 2“晶内型”和晶界型两种形式存在。合理的配方组成及制备工艺有利于 Z r O 以四方亚稳相存在。Z r O 含量为 2 23 0 w t % 时,其四方相含量可达 6 9 %,有利于应力诱导相变增韧,该 Z T A 复相陶瓷的抗弯强度、断裂韧性分别达到 604MPa、6.87MPa·m1/2。展开更多
文摘Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.
文摘Optically transparent alumina ceramics were fabricated by conventional process and sintered without pressure in H2 atmosphere. The results indicate that relative densities of alumina specimens increase to theoretical densities （T. D. ） with increasing content of La2O3. With increasing holding time during sintering, much less pores and larger grains were found in the sintered alumina samples. Higher transmittance was achieved in alumina codoped with MgO and La2O3 as compared with that doped with MgO only. The total-transmittance of alumina sample is up to 86% at twavelength range of 300 - 800 nm.
基金Supported by the Special Funds for Major State Basic Research Program of China （No.2003CB615702）, the National Natural Science Foundation of China （No.20636020） and the Natural Science Foundation of Jiangsu Province （No.BK2006722）.
文摘The catalytic hydrogenation of p-nitrophenol to p-aminophenol was investigated over Ni/Al2O3 catalyst on alumina support with different particle size. It is found that support particle size has significant influences on physiochemical properties and catalytic activity of the resulting Ni/Al2O3 catalyst, but little influence on the selec-tivity. At a comparable amount of Ni loading, the catalytic activity of Ni/Al2O3 prepared with alumina support of smaller particle size is lower. The reduction behavior of the catalyst is a key factor in determining the catalytic activity of Ni/Al2O3 catalyst. The supported nickel catalyst 10.3Ni/Al2O3-3 improves the life span of the membrane by reducing fouling on the membrane surface compared to nano-sized nickel.
基金China Scholarship Council for the award of fellowship and funding (No. 201708510113)。
文摘This work reports the influence of alumina fiber reinforcement of an AZ91Nd MMC(metal matrix composite)on the PEO coating formation process in a sodium phosphate-based electrolyte.By comparison with the pure AZ91Nd,the evolution of alumina fiber during the processing and the characteristics of the resultant PEO coating were investigated.The voltage response as a function of processing time was changed.Lower voltage in the presence of alumina fiber is responsible for the lower coating thickness.The morphology and phase composition of the coatings are also influenced by the incorporation of the fiber.Firstly,the fiber is embedded in the coating and interrupts the continuity of the coating.With increasing processing time,the fiber is found to be reactively incorporated in the coating.The intention to produce a MgAl_(2)O_(4)containing coating is achieved and it is mainly accumulated near the coating surface.However,due to the low number of fibers,the Al content is overall still low and only near to the fibers the MgAl_(2)O_(4)spinel phase can form.
基金Project(51204115)supported by the National Natural Science Foundation of ChinaProject(BK20130308)supported by the Basic Research Program of Jiangsu Province,ChinaProject(2014M561710)supported by China Postdoctoral Science Foundation
文摘Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass ratio of CaO to Al_2O_3 on surface tension were investigated.The results indicate that surface tension decreased with increasing MgO content(from 0 to 4.86%),followed by an increase with further increasing MgO content up to 11.33%.The trend that surface tension changed with the mass ratio of CaO to Al_2O_3 was the same as the trend that surface tension changed with the MgO content.The surface tension was varied from 0.617 N/m to 0.710 N/m,for the mass ratio of CaO to Al_2O_3 varying between 0.60 and 1.28.An attempt was made to estimate surface tension of CaO-Al_2O_3-MgO slag and its sub-system,and the application showed that the model worked well.
基金Project(50604018) supported by the National Natural Science Foundation of China
文摘Alumina coated LiNi1/3Mn1/3Co1/3O2 particles were obtained by a simple method of solid state reaction at room temperature. The reaction mechanism of solid state reaction at room temperature was investigated. The structure and morphology of the coating materials were investigated by XRD, SEM and TEM. The electrochemical performances of uncoated and Al2O3-coated LiNi1/3Co1/3Mn1/3O2 cathode materials were studied within a voltage window of 3.00?4.35 V at current density of 30 mA/g. SEM, TEM and EDS analytical results indicate that the surface of LiNi1/3Mn1/3Co1/3O2 particles is coated with very fine Al2O3 composite, which leads to the improved cycle ability though a slight decrease in the first discharge capacity is observed. It is proposed that surface treatment by solid state reaction at room temperature is a simple and effective method to improve the cycle performance of LiNi1/3Co1/3Mn1/3O2 particles.
文摘以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO 颗粒以 2 2 3 2“晶内型”和晶界型两种形式存在。合理的配方组成及制备工艺有利于 Z r O 以四方亚稳相存在。Z r O 含量为 2 23 0 w t % 时,其四方相含量可达 6 9 %,有利于应力诱导相变增韧,该 Z T A 复相陶瓷的抗弯强度、断裂韧性分别达到 604MPa、6.87MPa·m1/2。