Wire Arc Additive Manufactured CuMn_(13)Al_(7)High-Manganese Aluminium Bronze

In this work,high-manganese aluminium bronze CuMn_(13)Al_(7)samples were prepared by arc additive manufacturing technology.The phase composition,microstructure,and crystal structure of the high-manganese aluminium bronze CuMn_(13)Al_(7)arc additive manufactured samples were analysed using direct-reading spectrometer,metallographic microscope,scanning electron microscope,and transmission electron microscope.The micro-hardness tester,tensile tester,impact tester,and electrochemical workstation were also used to test the performance of the CuMn_(13)Al_(7)samples.By studying the microstructure and properties of the CuMn_(13)Al_(7)samples,it was found that preparation of the samples by the arc additive manufacturing technology ensured good forming quality,almost no defects,and good metallurgical bonding inside the sample.The metallographic structure(α+β+point phase)mainly comprises the following:the metallographic structure in the equiaxed grain region has an obvious grain boundaryα;the metallographic structure in the remelting region has no obvious grain boundaryα;the thermal influence on the metallographic structure produced a weaker grain boundaryαthan the equiaxed grain region.The transverse and longitudinal cross sections of the sample had uniform microhardness distributions,and the average microhardness values were 190.5 HV0.1 and 192.7 HV0.1,respectively.The sample also had excellent mechanical properties:yield strength of 301 MPa,tensile strength of 633 MPa,elongation of 43.5%,reduction of area by 58%,Charpy impact value of 68 J/cm^(2)at–20℃,and dynamic potential polarisation curve test results.Further,it was shown that the average corrosion potential of the sample was–284.5 mV,and the average corrosion current density was 4.1×10–3 mA/cm^(2).

Effect of RE on Cast Structure and Properties of High Manganese Aluminium Bronze

The effects of various amount of Y and La on the cast structure.the fluidity,the wearability and corrosion resistance of the high manganese aluminium bronze have been investigated.The results have shown that a proper content of rare earth elements is able to refine the cast structure of the alloy,and furthermore to enhance its wearability and corrosion resistance.The reasons for these phenomena have also been discussed.

Corrosion and Cavitation Erosion Behaviours of Cast Nickel Aluminium Bronze in 3.5% NaCl Solution with Different Sulphide Concentrations

The effect of sulphide(Na2S)concentration(SC)on the corrosion and cavitation erosion behaviours of a cast nickel aluminium bronze(NAB)in 3.5% NaCl solution is investigated in this study.The results show that when the SC exceeds 50 ppm,the hydrogen evolution reaction dominates the cathodic process,and a limiting current region appears in the anodic branch of the polarisation curve due to the formation of a copper sulphide film,which is a diffusion-controlled process.After longterm immersion,the increased mass loss rate of NAB with the sulphide additions of 20 and 50 ppm is attributed to the less protective films,which contains a mixture of copper oxides and sulphides.Moreover,NAB undergoes severe localised corrosion(selective phase corrosion,SPC)at the β’phases and eutectoid microstructureα+κⅢ.By comparison,NAB undergoes general corrosion and a copper sulphide film is formed in 100 and 200 ppm sulphide solutions.Cavitation erosion greatly increases the corrosion rate of NAB in all solutions and causes a negative potential shift in 3.5%NaCl solution due to the film destruction.However,a positive potential shift occurs in the solutions with SC higher than 50 ppm due to the accelerated mass transfer of the cathodic process.The cavitation erosion mass loss rate of NAB increases with the increase of SC.The occurrence of severe SPC decreases the phase boundary cohesion and causes brittle fracture under the cavitation impact.The corrosion-enhanced erosion is the most predominant factor for the cavitation erosion damage when the SC exceeds 50 ppm.