The rheo-diecasting mold filling capacity and the microstructure of the semi-solid A380 aluminum alloy slurry were investigated. The results show that the mold filling capacity was strengthened with increasing pouring...The rheo-diecasting mold filling capacity and the microstructure of the semi-solid A380 aluminum alloy slurry were investigated. The results show that the mold filling capacity was strengthened with increasing pouring temperature or increasing injection pressure. Under certain process parameters, the mold cavity was fully filled. However, the mold filling capacity decreased with increasing holding time. The mold filling capacity was improved with increasing shape factor of primary α(Al) grains; however, the solid fraction and the grain size significantly increased at the same time. In addition, the microstructures along the route of the spiral samples obviously differed. The grain size decreased gradually from the near-end to the far-end, whereas the shape factor increased gradually.展开更多
We implemented the process of producing a new Rib in three different ways, and we selected the process that was the most affordable and required the least labor, and we did it. This paper also considers the influence ...We implemented the process of producing a new Rib in three different ways, and we selected the process that was the most affordable and required the least labor, and we did it. This paper also considers the influence of the cost of the form from MDF, Alumina and Steel on the quality of the product.展开更多
The effects of the wavelength and orientation of machined grooves on a mold surface, casting speed, and melt superheat on the formation of surface marks on as-cast ingots were studied with an immersion casting tester ...The effects of the wavelength and orientation of machined grooves on a mold surface, casting speed, and melt superheat on the formation of surface marks on as-cast ingots were studied with an immersion casting tester and copper mold chill blocks. The mold surface topographies included a polished smooth surface, and those with machined unidirectional parallel contoured grooves oriented either parallel (vertical) or perpendicular (horizontal) to the casting direction. The unidirectional grooves were 0.232 mm deep with wavelength or spacing between 1 and 15 mm. The casting speed and melt superheat were between 1 and 200 mm/s, and 10 and 50 K, respectively. Two primary types of surface marks were observed on ingots cast with the copper mold with smooth surface topography, namely the finer and closely spaced ripples (Type I), and the widely spaced but coarser laps (Type II). The latter were more prevalent at the higher casting speeds and melt superheats. Qualitatively, formation of both types of surface marks on the as-cast ingots of the aluminum alloy 3003 appeared to be alleviated by increase in casting speed and melt superheat, and by the use of molds with grooved surface topography. In fact, casting with a mold surface with 1 mm spaced grooves that are perpendicular to the casting direction eliminated the formation of surface marks at casting speeds greater than 1 mm/s. It also improved the uniformity of the ingot subsurface microstructure and eliminated the associated subsurface segregation.展开更多
基金financially supported by the National Basic Research Program of China (No. 2011CB606300)the National Natural Science Foundation of China (No. 5077400)
文摘The rheo-diecasting mold filling capacity and the microstructure of the semi-solid A380 aluminum alloy slurry were investigated. The results show that the mold filling capacity was strengthened with increasing pouring temperature or increasing injection pressure. Under certain process parameters, the mold cavity was fully filled. However, the mold filling capacity decreased with increasing holding time. The mold filling capacity was improved with increasing shape factor of primary α(Al) grains; however, the solid fraction and the grain size significantly increased at the same time. In addition, the microstructures along the route of the spiral samples obviously differed. The grain size decreased gradually from the near-end to the far-end, whereas the shape factor increased gradually.
文摘We implemented the process of producing a new Rib in three different ways, and we selected the process that was the most affordable and required the least labor, and we did it. This paper also considers the influence of the cost of the form from MDF, Alumina and Steel on the quality of the product.
文摘The effects of the wavelength and orientation of machined grooves on a mold surface, casting speed, and melt superheat on the formation of surface marks on as-cast ingots were studied with an immersion casting tester and copper mold chill blocks. The mold surface topographies included a polished smooth surface, and those with machined unidirectional parallel contoured grooves oriented either parallel (vertical) or perpendicular (horizontal) to the casting direction. The unidirectional grooves were 0.232 mm deep with wavelength or spacing between 1 and 15 mm. The casting speed and melt superheat were between 1 and 200 mm/s, and 10 and 50 K, respectively. Two primary types of surface marks were observed on ingots cast with the copper mold with smooth surface topography, namely the finer and closely spaced ripples (Type I), and the widely spaced but coarser laps (Type II). The latter were more prevalent at the higher casting speeds and melt superheats. Qualitatively, formation of both types of surface marks on the as-cast ingots of the aluminum alloy 3003 appeared to be alleviated by increase in casting speed and melt superheat, and by the use of molds with grooved surface topography. In fact, casting with a mold surface with 1 mm spaced grooves that are perpendicular to the casting direction eliminated the formation of surface marks at casting speeds greater than 1 mm/s. It also improved the uniformity of the ingot subsurface microstructure and eliminated the associated subsurface segregation.
