Aluminated mesoporous silica was prepared by multiple post-grafting of alumina onto uniform mesoporous SiO2 ,which was assembled from monodisperse SiO2 microspheres.Hydrodesulfurization（HDS）catalyst was prepared by ...Aluminated mesoporous silica was prepared by multiple post-grafting of alumina onto uniform mesoporous SiO2 ,which was assembled from monodisperse SiO2 microspheres.Hydrodesulfurization（HDS）catalyst was prepared by loading Ni and Mo active components onto the aluminated uniform mesoporous SiO2 ,and its HDS catalytic performance was evaluated using hydrodesulfurization of dibenzothiophene as the probe reaction at 300℃ and 6.0 MPa in a tubular reactor.The samples were characterized by N2 physisorption,scanning electronic microscopy,Fourier transform infrared spectrum,X-ray diffraction（XRD）,temperature-programmed desorption of ammonia（NH3-TPD）,^27Al nuclear magnetic resonance（^27Al-NMR）and high-resolution transmission electron microscopy（HRTEM）.The results showed that the Si–OH group content of SiO2 was mainly dependent on the pretreatment conditions and had significant influence on the activity of the Ni Mo catalyst.The surface properties of the aluminated SiO2 varied with the Al2O3-grafting cycles.Generally after four cycles of grafting,the aluminated SiO2 behaved like amorphous alumina.In addition,plotting of activity of Ni Mo catalysts supported on aluminated meso–macroporous silica materials against the Al2O3-grafting cycle yields a volcano curve.展开更多
基金Financial support by the National Natural Science Foundation of China (Grant No. 91534120)the Shanghai Petrochemical Company of Sinopec (under the contract number 30450127-13-ZC0607-0001)
文摘Aluminated mesoporous silica was prepared by multiple post-grafting of alumina onto uniform mesoporous SiO2 ,which was assembled from monodisperse SiO2 microspheres.Hydrodesulfurization（HDS）catalyst was prepared by loading Ni and Mo active components onto the aluminated uniform mesoporous SiO2 ,and its HDS catalytic performance was evaluated using hydrodesulfurization of dibenzothiophene as the probe reaction at 300℃ and 6.0 MPa in a tubular reactor.The samples were characterized by N2 physisorption,scanning electronic microscopy,Fourier transform infrared spectrum,X-ray diffraction（XRD）,temperature-programmed desorption of ammonia（NH3-TPD）,^27Al nuclear magnetic resonance（^27Al-NMR）and high-resolution transmission electron microscopy（HRTEM）.The results showed that the Si–OH group content of SiO2 was mainly dependent on the pretreatment conditions and had significant influence on the activity of the Ni Mo catalyst.The surface properties of the aluminated SiO2 varied with the Al2O3-grafting cycles.Generally after four cycles of grafting,the aluminated SiO2 behaved like amorphous alumina.In addition,plotting of activity of Ni Mo catalysts supported on aluminated meso–macroporous silica materials against the Al2O3-grafting cycle yields a volcano curve.