Solid-solid surface adsorption of Eu2O3 on amorphous Al2O3 have been investigated by Mossbauer spectroscopy, X- ray diffraction analysis and laser Raman spectra (LRS). No X-ray diffraction peak of crystalline Eu2O3 ca...Solid-solid surface adsorption of Eu2O3 on amorphous Al2O3 have been investigated by Mossbauer spectroscopy, X- ray diffraction analysis and laser Raman spectra (LRS). No X-ray diffraction peak of crystalline Eu2O3 can be found for all samples studied. The LRS show that two peaks at 998 and 1051 cm-1 assigned to two-dimensional surface europium-oxygen species appear at Eu2O3 content of 18.7 wt%. The peak at 1068 cm-1 due to the surface species and another peak at 342cm-1 due to crystalline Eu2O3 content start to appear for the sample with an Eu2O3 content of 36.5 wt%. The dispersity of Eu2O3 on the surface of amorphous Al2O3 were compared with that of α-Al2O3,η-Al2O3 and SiO2 gel. The results of these studies indicate that the structure of Eu2O3 dispersed onto the support surface depend on the structure of support and that there is an inductive effect of support on the structure of the Eu2O3.展开更多
Surface tension of sodium aluminate solution and the contact angle between Al（OH）3 particles and aluminate solution were measured, then the dependence of Al（OH）3 solubility on its particle size was calculated and ...Surface tension of sodium aluminate solution and the contact angle between Al（OH）3 particles and aluminate solution were measured, then the dependence of Al（OH）3 solubility on its particle size was calculated and thus the variation of the critical nucleus sizes was determined based on the Ostwald ripening formula. The results show that the Al（OH）3 solubility in sodium aluminate solution decreases with the increment of particle size, and the critical nucleus sizes increase with the rise of alkali concentration, caustic ratio and precipitation temperature. The results also imply that the presence of small particles in seeded precipitation system is an important factor to limit the depth of precipitation.展开更多
文摘Solid-solid surface adsorption of Eu2O3 on amorphous Al2O3 have been investigated by Mossbauer spectroscopy, X- ray diffraction analysis and laser Raman spectra (LRS). No X-ray diffraction peak of crystalline Eu2O3 can be found for all samples studied. The LRS show that two peaks at 998 and 1051 cm-1 assigned to two-dimensional surface europium-oxygen species appear at Eu2O3 content of 18.7 wt%. The peak at 1068 cm-1 due to the surface species and another peak at 342cm-1 due to crystalline Eu2O3 content start to appear for the sample with an Eu2O3 content of 36.5 wt%. The dispersity of Eu2O3 on the surface of amorphous Al2O3 were compared with that of α-Al2O3,η-Al2O3 and SiO2 gel. The results of these studies indicate that the structure of Eu2O3 dispersed onto the support surface depend on the structure of support and that there is an inductive effect of support on the structure of the Eu2O3.
基金Project(51274242)supported by the National Natural Science Foundation of China
文摘Surface tension of sodium aluminate solution and the contact angle between Al（OH）3 particles and aluminate solution were measured, then the dependence of Al（OH）3 solubility on its particle size was calculated and thus the variation of the critical nucleus sizes was determined based on the Ostwald ripening formula. The results show that the Al（OH）3 solubility in sodium aluminate solution decreases with the increment of particle size, and the critical nucleus sizes increase with the rise of alkali concentration, caustic ratio and precipitation temperature. The results also imply that the presence of small particles in seeded precipitation system is an important factor to limit the depth of precipitation.