The crystallization behaviour of the laser synthesized nanometric amorphous Si3N4 powders with the particle size of 15 nm in diameter has been studied between 1200° and 1700℃ by XRD,TEM and FTIR techniques. A sm...The crystallization behaviour of the laser synthesized nanometric amorphous Si3N4 powders with the particle size of 15 nm in diameter has been studied between 1200° and 1700℃ by XRD,TEM and FTIR techniques. A small amount of β-Si3N4 formed at 1250℃ and increased slowly until the α- β transformation happened at 1700℃, whereas α-Si3N4 appeared at 1300℃ andincreased rapidly between 1500-1600℃. The formation of β phase at the lower temperature was caused by the nitridation of free Si due to the preexisted β-nuclei in the Si3N4 particles, whereasthe α phase was formed by solid crystallization from the amorphous matrix. There were α and β SiC formed at 1700℃ due to the presence of Sio and Co gases in the system. FTIR analysis shows that two new IR absorption at 1356 and 1420 cm-1, and an overall strong absorption in wide wavenumber range resulted from the powders annealed at 1600 and 1700℃ respectively展开更多
The homogeneous plastic flow of fully amorphous and partially crystallized Zr(41.2)Ti(13.8)Cu(12.5)Ni(10)Be(22.5) bulk metallic glass (Vitl) has been investigated by compression tests at high temperatures in supercool...The homogeneous plastic flow of fully amorphous and partially crystallized Zr(41.2)Ti(13.8)Cu(12.5)Ni(10)Be(22.5) bulk metallic glass (Vitl) has been investigated by compression tests at high temperatures in supercooled liquid region. Experimental results show that at sufficiently low strain rates, the supercooled liquid of the fully amorphous alloy reveals Newtonian flow with a linear relationship between the flow stress and strain rate. As the strain rate is increased, a transition from linear Newtonian to nonlinear flow is detected, which can be explained by the transition state theory. Over the entire strain rate interval investigated, however, only nonlinear flow is present in the partially crystallized alloy, and the flow stress for each strain rate is much higher. It is found that the strain rate-stress relationship for the partially crystaltized alloy at the given temperature of 646 K also obeys the sinh law derived from the transition state theory, similar to that of the initial homogeneous amorphous alloy. Thus, it is proposed that the flow behavior of the nanocrystalline/amorphous composite at 646 K is mainly controlled by the viscous flow of the remaining supercooled liquid.展开更多
Bulk amorphous crystal and microcrystal for Pr60Cu(20-x)Ni10Al10Fex (x = 0, 8, 15, 20) with the diameter ofΦ2 ~ 6 mm were manufactured by electric arc smelting, high frequency heating and copper mold upper suction ca...Bulk amorphous crystal and microcrystal for Pr60Cu(20-x)Ni10Al10Fex (x = 0, 8, 15, 20) with the diameter ofΦ2 ~ 6 mm were manufactured by electric arc smelting, high frequency heating and copper mold upper suction casting, and its structure was analyzed by X-ray diffract meter. It showed soft magnetic characteristic gradually when Fe content in it was up to 8% . The material was applied to magnetic-electric sensor as key component, output signal of which was measured with the change of Fe content. It shows that the signal changes from weak to strong with the increase of Fe content and presents the largest peak value when Fe is replaced by Cu completely.展开更多
The powders of pure Al, Fe, and Zr for preparing Al78Fe20Zr2 were subject to a high-energy planetary ball milling.The microstructure evolution of the mixtures at the different intervals of milling was characterized by...The powders of pure Al, Fe, and Zr for preparing Al78Fe20Zr2 were subject to a high-energy planetary ball milling.The microstructure evolution of the mixtures at the different intervals of milling was characterized by X-ray diffraction（XRD）, transmission electron microscopy（TEM） and differential scanning calorimetry（DSC）.It was found that a nearly complete amorphization could be achieved in the mixtures after ball milling for 23 h.Further ball milling led to the crystallization of the amorphous powders.A long time ball milling, e.g., 160 h, led to a complete crystallization of the amorphous powders and the formation of Al3Zr and Al13Fe4.The crystallization products caused by ball milling are almost the same as that produced by isothermal annealing of the amorphous powders in vacuum at 800 K for 1 h.展开更多
Aim To investigate the multiple melting behavior of polyamide 6(PA 6) in polyamide 6/linear low density polyethylene blends crystallized from the crystal amorphous state. Methods\ The effects of annealing tempera...Aim To investigate the multiple melting behavior of polyamide 6(PA 6) in polyamide 6/linear low density polyethylene blends crystallized from the crystal amorphous state. Methods\ The effects of annealing temperature, annealing time, heating rate, and the step wise annealing were measured by DSC. Results and Conclusion\ There exists a critical heating rate affecting the middle temperature melting peak. When annealed at the temperature close to the melting peak, the main melting peak of PA 6 shifted to a higher temperature. Within a short time, annealing time has much effect on neat PA 6 but little effect on PA 6 in the blends. Addition of PE results in a decreasing in the height of melting peak. These phenomenon show that the melting behavior of PA 6 was affected by PE, compatibilizer, as well as thermal treatment.展开更多
Local annealing of amorphous NiTi thin films was performed by using an Nd：YAG 1064 nm wavelength pulsed laser beam. Raw samples produced by simultaneous sputter deposition from elemental Ni and Ti targets onto unheat...Local annealing of amorphous NiTi thin films was performed by using an Nd：YAG 1064 nm wavelength pulsed laser beam. Raw samples produced by simultaneous sputter deposition from elemental Ni and Ti targets onto unheated Si （100） and Silica （111） substrates were used for annealing. Delicate treatment with 15.92 W/mm^2 power density resulted in crystallization of small spots; while 16.52 and 17.51 W/mm^2 power densities caused ablation of the amorphous layer. Optical microscopy, scanning electron microscopy, X-ray diffraction and atomic force microscopy were performed to characterize the microstructure and surface morphology of the amorphous/crystallized spot patterns.展开更多
The nano-crystalline materials with many special and super magnetic properties could be synthesized by fractional crystallization of amorphous alloys. Since this new method for preparation of nano-crystalline material...The nano-crystalline materials with many special and super magnetic properties could be synthesized by fractional crystallization of amorphous alloys. Since this new method for preparation of nano-crystalline materials was introduced, the crystallization kinetics of amorphous alloys has been studied in more and more intensive investigations. So far, almost all experiments on the crystallization kinetics are conducted by differential展开更多
A novel way of producing superhydrophobic surfaces by applying a self-assembled monolayer(SAM)to silicon micro/nano-textured surfaces is presented in this paper.The micro/nano-textured surfaces on silicon substrates w...A novel way of producing superhydrophobic surfaces by applying a self-assembled monolayer(SAM)to silicon micro/nano-textured surfaces is presented in this paper.The micro/nano-textured surfaces on silicon substrates were generated by the aluminum-induced crystallization(AIC)of amorphous silicon(a-Si)technique.Octadecyltrichlorosilane(OTS)SAMs were then applied to the textured surfaces by dip coating.The topography and wetting properties of the resulting surfaces were characterized using scanning electron microscopy(SEM)and a video-based contact angle measurement system.The results show that by introducing OTS SAMs on the silicon micro/nano-textured surfaces,superhydrophobic surfaces with water contact angles(WCAs)of 155°were obtained,as compared to the WCAs of OTS-modified smooth silicon surfaces of about 112°.Surface topography was found to directly influence the WCA as predicted by the Cassie-Baxter model.展开更多
文摘The crystallization behaviour of the laser synthesized nanometric amorphous Si3N4 powders with the particle size of 15 nm in diameter has been studied between 1200° and 1700℃ by XRD,TEM and FTIR techniques. A small amount of β-Si3N4 formed at 1250℃ and increased slowly until the α- β transformation happened at 1700℃, whereas α-Si3N4 appeared at 1300℃ andincreased rapidly between 1500-1600℃. The formation of β phase at the lower temperature was caused by the nitridation of free Si due to the preexisted β-nuclei in the Si3N4 particles, whereasthe α phase was formed by solid crystallization from the amorphous matrix. There were α and β SiC formed at 1700℃ due to the presence of Sio and Co gases in the system. FTIR analysis shows that two new IR absorption at 1356 and 1420 cm-1, and an overall strong absorption in wide wavenumber range resulted from the powders annealed at 1600 and 1700℃ respectively
文摘The homogeneous plastic flow of fully amorphous and partially crystallized Zr(41.2)Ti(13.8)Cu(12.5)Ni(10)Be(22.5) bulk metallic glass (Vitl) has been investigated by compression tests at high temperatures in supercooled liquid region. Experimental results show that at sufficiently low strain rates, the supercooled liquid of the fully amorphous alloy reveals Newtonian flow with a linear relationship between the flow stress and strain rate. As the strain rate is increased, a transition from linear Newtonian to nonlinear flow is detected, which can be explained by the transition state theory. Over the entire strain rate interval investigated, however, only nonlinear flow is present in the partially crystallized alloy, and the flow stress for each strain rate is much higher. It is found that the strain rate-stress relationship for the partially crystaltized alloy at the given temperature of 646 K also obeys the sinh law derived from the transition state theory, similar to that of the initial homogeneous amorphous alloy. Thus, it is proposed that the flow behavior of the nanocrystalline/amorphous composite at 646 K is mainly controlled by the viscous flow of the remaining supercooled liquid.
文摘Bulk amorphous crystal and microcrystal for Pr60Cu(20-x)Ni10Al10Fex (x = 0, 8, 15, 20) with the diameter ofΦ2 ~ 6 mm were manufactured by electric arc smelting, high frequency heating and copper mold upper suction casting, and its structure was analyzed by X-ray diffract meter. It showed soft magnetic characteristic gradually when Fe content in it was up to 8% . The material was applied to magnetic-electric sensor as key component, output signal of which was measured with the change of Fe content. It shows that the signal changes from weak to strong with the increase of Fe content and presents the largest peak value when Fe is replaced by Cu completely.
基金financial support of the National Natural Science Foundation of China (No. 50371072)the Hunan Provincial Natural Science Foundation (No. 09JJ3086)
文摘The powders of pure Al, Fe, and Zr for preparing Al78Fe20Zr2 were subject to a high-energy planetary ball milling.The microstructure evolution of the mixtures at the different intervals of milling was characterized by X-ray diffraction（XRD）, transmission electron microscopy（TEM） and differential scanning calorimetry（DSC）.It was found that a nearly complete amorphization could be achieved in the mixtures after ball milling for 23 h.Further ball milling led to the crystallization of the amorphous powders.A long time ball milling, e.g., 160 h, led to a complete crystallization of the amorphous powders and the formation of Al3Zr and Al13Fe4.The crystallization products caused by ball milling are almost the same as that produced by isothermal annealing of the amorphous powders in vacuum at 800 K for 1 h.
文摘Aim To investigate the multiple melting behavior of polyamide 6(PA 6) in polyamide 6/linear low density polyethylene blends crystallized from the crystal amorphous state. Methods\ The effects of annealing temperature, annealing time, heating rate, and the step wise annealing were measured by DSC. Results and Conclusion\ There exists a critical heating rate affecting the middle temperature melting peak. When annealed at the temperature close to the melting peak, the main melting peak of PA 6 shifted to a higher temperature. Within a short time, annealing time has much effect on neat PA 6 but little effect on PA 6 in the blends. Addition of PE results in a decreasing in the height of melting peak. These phenomenon show that the melting behavior of PA 6 was affected by PE, compatibilizer, as well as thermal treatment.
文摘Local annealing of amorphous NiTi thin films was performed by using an Nd：YAG 1064 nm wavelength pulsed laser beam. Raw samples produced by simultaneous sputter deposition from elemental Ni and Ti targets onto unheated Si （100） and Silica （111） substrates were used for annealing. Delicate treatment with 15.92 W/mm^2 power density resulted in crystallization of small spots; while 16.52 and 17.51 W/mm^2 power densities caused ablation of the amorphous layer. Optical microscopy, scanning electron microscopy, X-ray diffraction and atomic force microscopy were performed to characterize the microstructure and surface morphology of the amorphous/crystallized spot patterns.
文摘The nano-crystalline materials with many special and super magnetic properties could be synthesized by fractional crystallization of amorphous alloys. Since this new method for preparation of nano-crystalline materials was introduced, the crystallization kinetics of amorphous alloys has been studied in more and more intensive investigations. So far, almost all experiments on the crystallization kinetics are conducted by differential
基金This material is based on work supported by the US National Science Foundation under Grant Nos.CMMI-0600642 and CMMI-0645040.
文摘A novel way of producing superhydrophobic surfaces by applying a self-assembled monolayer(SAM)to silicon micro/nano-textured surfaces is presented in this paper.The micro/nano-textured surfaces on silicon substrates were generated by the aluminum-induced crystallization(AIC)of amorphous silicon(a-Si)technique.Octadecyltrichlorosilane(OTS)SAMs were then applied to the textured surfaces by dip coating.The topography and wetting properties of the resulting surfaces were characterized using scanning electron microscopy(SEM)and a video-based contact angle measurement system.The results show that by introducing OTS SAMs on the silicon micro/nano-textured surfaces,superhydrophobic surfaces with water contact angles(WCAs)of 155°were obtained,as compared to the WCAs of OTS-modified smooth silicon surfaces of about 112°.Surface topography was found to directly influence the WCA as predicted by the Cassie-Baxter model.