Developing polydopamine modified molybdenum disulfide/epoxy resin powder coatings with enhanced anticorrosion performance and wear resistance on magnesium lithium alloys

Epoxy resin powder coating has been successfully applied on the corrosion protection of magnesium lithium alloys.However,poor wear resistance and microcracks formed during the solidification have limited it extensive application.There are limited approaches to exploit such anti-corrosion and mechanical properties of magnesium lithium alloys.Herein,the epoxy resin powder coating with polydopamine modified molybdenum disulfide(MoS_(2)@PDA-EP powder coating with 0,0.1,0.2,0.5,1.0 wt.%loading)was well prepared by melt extrusion to investigate its anticorrosion performance and wear resistance.The results revealed that the addition of MoS_(2)@PDA enhanced the adhesion strength between coatings and alloys,wear resistance and corrosion protection of the powder coatings.Among them,the optimum was obtained by 0.2 wt.%MoS_(2)@PDA-EP powder coating which could be attributed to well dispersion and efficient adhesion with coating matrix.To conclude,MoS_(2)@PDA-EP powder coating is meaningfully beneficial for the anticorrosive and wear performance improvement of magnesium lithium alloys.

Effect of low curing temperature on the anticorrosion performance of composite coatings reinforced with modified Fe_(3)O_(4)

In this manuscript,the neat epoxy(EP)and functionalized Fe_(3)O_(4)(G-Fe_(3)O_(4))reinforced epoxy(G-Fe_(3)O_(4)/EP)coatings were cured under different temperatures,and the effect of the low curing temperature on the anticorrosion performance was investigated.The experimental results show that the epoxy-amine ring-open addition reaction mainly exists in the curing process,and the activation energies of the reaction for the two coatings are 55.84 and 53.29 kJ/mol,respectively.For the coatings cured at the low temperature,almost no pores could be detected on the fracture surface,but the presentence of the rough regions reflects the poor curing state.As compared with the samples cured at the high temperature,the anticorrosion performance of the coatings with the low curing temperature is worse,and the decrease rate of the anticorrosion performance is slower,because of the poor curing state and low adhesion obtained at the low temperature.

Densification and anticorrosion performances of vacuum evaporated aluminium coatings on NdFeB magnets

Al coated NdFeB magnets obtained by vacuum evaporation technique were densified by high energy ball milling method.The surface morphology,metal composition and micro structure of the coatings were characterized by scanning electron microscopy,X-ray diffraction and X-ray photoelectron spectroscopy,respectively.The anticorrosive properties were investigated by potentiodynamic polarization curves and neutral salt spray test.The pores in the Al coatings of columnar crystals(Al) induced by the evaporation technique,were apparently filled in the following ball milling process,leading to the densification of Al coatings and the evident improvement of the anticorrosive performances.When treated with ball milling for 30 min,the sample achieves the best anticorrosive performances with the self-corrosion potential of-0.87 V,self-corrosion current density of 1.65 μA/cm^(2) and the neutral salt spray(NSS) time of 144 h(red rust).The improvement of the anticorro sive performances of vacuum evaporated Al coating mainly lies in the densification effect of the coating,which depends on different loading conditions of ball milling process.

Enhanced Anticorrosion Properties of Epoxy Coatings from Al and Zn Based Pigments

Anticorrosion epoxy coatings from Al and Zn based pigments were synthesized by adjusting their volume ratios, aiming at their increasing anticorrosion performances. The anticorrosion properties were examined via elec- trochemical impedance spectroscopy, Tafel polarization curve analysis and salt spray test. The coating morphologies before and after the salt spray tests were studied via scanning electron microscopy（SEM）. The elemental and chemical compositions of the corroded surfaces of the coatings were analyzed by means of X-ray photoelectron spectroscopy（XPS）. The results indicate that the coating composed of Al/Zn at 10：1（volume ratio） displays the maximum anticorrosion performances, which are superior to those of pristine Al or Zn based pigment.