The micro arc oxidation(MAO)coatings with different concentrations of Ca,P and Zn elements are successfully formed on the titanium substrate at the different applied voltages.After MAO treatment,the MAO coating exhibi...The micro arc oxidation(MAO)coatings with different concentrations of Ca,P and Zn elements are successfully formed on the titanium substrate at the different applied voltages.After MAO treatment,the MAO coating exhibits the porous surface structure and composed of anatase and rutile TiO2 phases.Meanwhile,the average size and density of micro-pores on the MAO coatings have been modified via the adjusting the applied voltages.In addition,the contents of the incorporated elements such as Zn,Ca and P elements in the MAO coatings have been optimized.The bonding strength test results reveal that the MAO coating shows higher bonding strength,which is up to 45±5 MPa.Compared to the pure Ti plate,the MAO coating formed at 350 and 400 V show good apatite-inducing ability.Meanwhile,the MAO coating containing Zn,Ca and P elements have better antibacterial ability for E.coli and S.aureus.Thus,the incorporation of Zn,Ca and P elements was an effective method to improve the antibacterial ability.Moreover,the concentrations of Zn,Ca and P elements could be adjusted with the changing of the applied voltages.As a result,the enhancement of the antibacterial ability on the MAO coating surfaces was depended on the comprehensive effect of the incorporated elements and the surface property of MAO coatings.展开更多
Porous sintered Ti-Ag compacts with different Ag content were fabricated by powder metallurgy. The associated hydrothermal treatment and the effect on the apatite formation were studied. The results suggested that TiO...Porous sintered Ti-Ag compacts with different Ag content were fabricated by powder metallurgy. The associated hydrothermal treatment and the effect on the apatite formation were studied. The results suggested that TiO was generated under the condition of low vacuum (1 ×10^-2 Pa) during the process of burning out the spacer-holding particles. After hydrothermal treatment, a sub-microscale porous layer was formed at the pore wall surface of the samples. The apatite-inducing ability of hydrothermal treated porous sintered Ti-Ag compacts with different Ag content was evaluated in modified simulated body fluid (SBF). And the results proved that there is a clear correlation between the apatite-inducing ability and Ag content. The higher Ag content in porous leads to the decrease of Na+ ions and basic hydroxyl (OH)b amount, resulting in the decline of apatite-inducing ability in the first stage. However, their apatite-inducing ability was not significantly different from that of Ti after two weeks SBF immersing. Hence, the ionic activity should restore with the processing of SBF soaking, as the saturation of Ag effect.展开更多
基金This work was financially supported by Heilongjiang Provincial Youth Science Foundation(QC2013C043)National Basic Science Research Program(2012CB933900)the Fundamental Research Funds for the Central Universities(Grant no.HIT.NSRIF.2014002).
文摘The micro arc oxidation(MAO)coatings with different concentrations of Ca,P and Zn elements are successfully formed on the titanium substrate at the different applied voltages.After MAO treatment,the MAO coating exhibits the porous surface structure and composed of anatase and rutile TiO2 phases.Meanwhile,the average size and density of micro-pores on the MAO coatings have been modified via the adjusting the applied voltages.In addition,the contents of the incorporated elements such as Zn,Ca and P elements in the MAO coatings have been optimized.The bonding strength test results reveal that the MAO coating shows higher bonding strength,which is up to 45±5 MPa.Compared to the pure Ti plate,the MAO coating formed at 350 and 400 V show good apatite-inducing ability.Meanwhile,the MAO coating containing Zn,Ca and P elements have better antibacterial ability for E.coli and S.aureus.Thus,the incorporation of Zn,Ca and P elements was an effective method to improve the antibacterial ability.Moreover,the concentrations of Zn,Ca and P elements could be adjusted with the changing of the applied voltages.As a result,the enhancement of the antibacterial ability on the MAO coating surfaces was depended on the comprehensive effect of the incorporated elements and the surface property of MAO coatings.
基金supported by the National Basic Research Program of China("973 Program",Nos.2012CB619102 and 2012CB619100)National Science Fund for Distinguished Young Scholars(Grant No.51225101)+1 种基金the Fundamental Research Funds for the Central Universities(Nos.HEUCFZ1017 and HEUCFR1020)the Natural Science Foundation of Heilongjiang Province,China(No.ZD201012)
文摘Porous sintered Ti-Ag compacts with different Ag content were fabricated by powder metallurgy. The associated hydrothermal treatment and the effect on the apatite formation were studied. The results suggested that TiO was generated under the condition of low vacuum (1 ×10^-2 Pa) during the process of burning out the spacer-holding particles. After hydrothermal treatment, a sub-microscale porous layer was formed at the pore wall surface of the samples. The apatite-inducing ability of hydrothermal treated porous sintered Ti-Ag compacts with different Ag content was evaluated in modified simulated body fluid (SBF). And the results proved that there is a clear correlation between the apatite-inducing ability and Ag content. The higher Ag content in porous leads to the decrease of Na+ ions and basic hydroxyl (OH)b amount, resulting in the decline of apatite-inducing ability in the first stage. However, their apatite-inducing ability was not significantly different from that of Ti after two weeks SBF immersing. Hence, the ionic activity should restore with the processing of SBF soaking, as the saturation of Ag effect.