MCrAlY(M=Ni and/or Co)overlay coating is widely used as a protective coating against high temperature oxidation and corrosion.However,due to its big difference in chemical composition with the underlying superalloy,el...MCrAlY(M=Ni and/or Co)overlay coating is widely used as a protective coating against high temperature oxidation and corrosion.However,due to its big difference in chemical composition with the underlying superalloy,elements interdiffusion occurs inevitably.One of the direct results is the formation of interdiffusion zone(IDZ)and secondary reaction zone(SRZ)with a high density of fine topological closed-packed phases(TCPs),weakening dramatically the mechanical properties of the alloy substrate.It is by now the main problem of modern high-temperature metallic coatings,but there are still hardly any reports studying the formation,growth and transformation of IDZ and SRZ in deep,as well as the precipitation of TCPs.In this work,a typical NiCrAlY coating is deposited by arc ion plating on a single-crystal superalloy N5.Elements interdiffusion between them and its relationship on microstructure were clarified.Cr rather than Al from the coating diffuses into the alloy at high temperatures and segregates immediately beneath their interface,contributing largely to the formation of IDZ.Simultaneously,diffusion of Ni from the deep alloy to IDZ leads to the formation and continuous expansion of SRZ.展开更多
基金the National Natural Science Foundation of China Nos.51671053 and 51801021the Ministry of Industry and Information Technology Project No.MJ-2017-J-99)。
文摘MCrAlY(M=Ni and/or Co)overlay coating is widely used as a protective coating against high temperature oxidation and corrosion.However,due to its big difference in chemical composition with the underlying superalloy,elements interdiffusion occurs inevitably.One of the direct results is the formation of interdiffusion zone(IDZ)and secondary reaction zone(SRZ)with a high density of fine topological closed-packed phases(TCPs),weakening dramatically the mechanical properties of the alloy substrate.It is by now the main problem of modern high-temperature metallic coatings,but there are still hardly any reports studying the formation,growth and transformation of IDZ and SRZ in deep,as well as the precipitation of TCPs.In this work,a typical NiCrAlY coating is deposited by arc ion plating on a single-crystal superalloy N5.Elements interdiffusion between them and its relationship on microstructure were clarified.Cr rather than Al from the coating diffuses into the alloy at high temperatures and segregates immediately beneath their interface,contributing largely to the formation of IDZ.Simultaneously,diffusion of Ni from the deep alloy to IDZ leads to the formation and continuous expansion of SRZ.