The ac conductivity of the bulk amorphous chalcogenide system (As2Te3)100-xGex (where x=0,5,10,15 and 25 at. pct) was investigated at variable frequencies ranging from 50 Hz to 100 kHz and at different temperatures ra...The ac conductivity of the bulk amorphous chalcogenide system (As2Te3)100-xGex (where x=0,5,10,15 and 25 at. pct) was investigated at variable frequencies ranging from 50 Hz to 100 kHz and at different temperatures ranging from 3O to 160℃. lt was found that at a fixed temperature, where n <1 and decreases with temperature. The complex impedence Z was measured over the same frequency and temperature ranges. All samples give a semicircle arc originating at the origin point. This indicates that each composition can be described only by one resistance R and one capacity C, both parallelly combined. The centre below the real axis indicates the relaxation behaviour of the system. The activation energies for conduction were calculated.展开更多
This paper reports the formation and some properties of a new class of chalcohalide glasses in the As2Tef iodide systems. The As2Te3-Pb12, As2Te3-HgI2, As2Te3-CitI and As2Te3-AgI systems can form stable bulk glasses i...This paper reports the formation and some properties of a new class of chalcohalide glasses in the As2Tef iodide systems. The As2Te3-Pb12, As2Te3-HgI2, As2Te3-CitI and As2Te3-AgI systems can form stable bulk glasses in wide composition regions ?and no bulk glass formation was found in the As2Te3-TH sys-tem. As2Te3-based glasses have glass transition tempera-展开更多
文摘The ac conductivity of the bulk amorphous chalcogenide system (As2Te3)100-xGex (where x=0,5,10,15 and 25 at. pct) was investigated at variable frequencies ranging from 50 Hz to 100 kHz and at different temperatures ranging from 3O to 160℃. lt was found that at a fixed temperature, where n <1 and decreases with temperature. The complex impedence Z was measured over the same frequency and temperature ranges. All samples give a semicircle arc originating at the origin point. This indicates that each composition can be described only by one resistance R and one capacity C, both parallelly combined. The centre below the real axis indicates the relaxation behaviour of the system. The activation energies for conduction were calculated.
文摘This paper reports the formation and some properties of a new class of chalcohalide glasses in the As2Tef iodide systems. The As2Te3-Pb12, As2Te3-HgI2, As2Te3-CitI and As2Te3-AgI systems can form stable bulk glasses in wide composition regions ?and no bulk glass formation was found in the As2Te3-TH sys-tem. As2Te3-based glasses have glass transition tempera-