We report the design and analysis of a rod-type photonic crystal fiber with Er-Yb co-doped for the high power 1.5-μm band amplifier.The fiber structure is designed to be the 120-μm extreme large core diameter,300-μ...We report the design and analysis of a rod-type photonic crystal fiber with Er-Yb co-doped for the high power 1.5-μm band amplifier.The fiber structure is designed to be the 120-μm extreme large core diameter,300-μm inner cladding diameter,and 1.5-mm outer cladding diameter that ensure the single mode output during high power amplification.Both the continuous wave(CW) and pulsed amplification characteristics are analyzed based on the exact modeling and simulation under the designed geometry.The 4-mJ pulse energy and 400-kW peak power are obtained in theory,so the 1.5-μm band amplifier that achieves milojoule level pulse energy meanwhile keeping single mode is firstly designed.展开更多
Nanometer sized Au/TiO\-2 particles were synthesized by irradiation of a HAuCl\-4 solution containing colloidal TiO\-2 with light of wavelength (λ)>330 nm. The absorption maximum attributed to the surface plasmon ...Nanometer sized Au/TiO\-2 particles were synthesized by irradiation of a HAuCl\-4 solution containing colloidal TiO\-2 with light of wavelength (λ)>330 nm. The absorption maximum attributed to the surface plasmon band of gold was observed at 540 nm, a red shift of about 20 nm from the position in aqueous solution. The Au clusters are situated on the surface of TiO\-2 in terms of microcrystallite, which was confirmed by HRTEM, EDS and XRD. The electronic interfaction between the metal and the suport was discussed.展开更多
文摘We report the design and analysis of a rod-type photonic crystal fiber with Er-Yb co-doped for the high power 1.5-μm band amplifier.The fiber structure is designed to be the 120-μm extreme large core diameter,300-μm inner cladding diameter,and 1.5-mm outer cladding diameter that ensure the single mode output during high power amplification.Both the continuous wave(CW) and pulsed amplification characteristics are analyzed based on the exact modeling and simulation under the designed geometry.The 4-mJ pulse energy and 400-kW peak power are obtained in theory,so the 1.5-μm band amplifier that achieves milojoule level pulse energy meanwhile keeping single mode is firstly designed.
文摘Nanometer sized Au/TiO\-2 particles were synthesized by irradiation of a HAuCl\-4 solution containing colloidal TiO\-2 with light of wavelength (λ)>330 nm. The absorption maximum attributed to the surface plasmon band of gold was observed at 540 nm, a red shift of about 20 nm from the position in aqueous solution. The Au clusters are situated on the surface of TiO\-2 in terms of microcrystallite, which was confirmed by HRTEM, EDS and XRD. The electronic interfaction between the metal and the suport was discussed.