The kinetics of isothermal reduction of Ag2O with graphite under argon atmosphere for a non-activated sample and mechanically activated sample was investigated.It is found that Johnson-Mehl-Avrami model appropriately ...The kinetics of isothermal reduction of Ag2O with graphite under argon atmosphere for a non-activated sample and mechanically activated sample was investigated.It is found that Johnson-Mehl-Avrami model appropriately explained the thermal and mechanochemical synthesis of Ag from Ag2O＋ghraphite mixture.The process kinetics was investigated using the same approach for milled and unmilled samples.The results show that the Avrami exponent of mechanochemical reduction is higher than that of high temperature thermal reduction.Also,the mechanisms of nuclei growth in thermal and mechanochemical reduction are diffusion controlled and interface controlled,respectively.展开更多
The primary crystallization of the Ti40Zr25NisCu9Bc18 amorphous alloy was studied by isochronal differential scanning calorimetry （DSC）. The activation energy was determined by the Kissinger-Akahim-Sunose method. Tr...The primary crystallization of the Ti40Zr25NisCu9Bc18 amorphous alloy was studied by isochronal differential scanning calorimetry （DSC）. The activation energy was determined by the Kissinger-Akahim-Sunose method. Trying to analyze the crystallization kinetics of the Ti40Zr25NigCu9Be18 amorphous alloy by two different methods, it was found that the crystallization kinetics did not obey the Johnson-Mehl-Avrami equation. A modified method in consideration of the impingement effect was proposed to perform kinetic analysis of the isochronal crystallization of this alloy. The kinetic parameters were then obtained by the linear fitting method based on the modified kinetic equation. The results show that the isochronal crystallization kinetics of the amorphous Ti40Zr25Ni8CugBe18 alloy is heating rate dependent, and the discrepancy between the Johnson-Mehl-Avrami method and the modified method increases with the increase of heating rate.展开更多
文摘The kinetics of isothermal reduction of Ag2O with graphite under argon atmosphere for a non-activated sample and mechanically activated sample was investigated.It is found that Johnson-Mehl-Avrami model appropriately explained the thermal and mechanochemical synthesis of Ag from Ag2O＋ghraphite mixture.The process kinetics was investigated using the same approach for milled and unmilled samples.The results show that the Avrami exponent of mechanochemical reduction is higher than that of high temperature thermal reduction.Also,the mechanisms of nuclei growth in thermal and mechanochemical reduction are diffusion controlled and interface controlled,respectively.
基金supported by the National Natural Science Foundation of China (No50601011)the National Basic Research Priorities Program of China (No2007CB607603)+1 种基金the State Key Laboratory of Solidification Processing in NWPU (NoSKLSP200905)the Program for New Century Excellent Talents in Chinese Universities (NoNCET-06-0484)
文摘The primary crystallization of the Ti40Zr25NisCu9Bc18 amorphous alloy was studied by isochronal differential scanning calorimetry （DSC）. The activation energy was determined by the Kissinger-Akahim-Sunose method. Trying to analyze the crystallization kinetics of the Ti40Zr25NigCu9Be18 amorphous alloy by two different methods, it was found that the crystallization kinetics did not obey the Johnson-Mehl-Avrami equation. A modified method in consideration of the impingement effect was proposed to perform kinetic analysis of the isochronal crystallization of this alloy. The kinetic parameters were then obtained by the linear fitting method based on the modified kinetic equation. The results show that the isochronal crystallization kinetics of the amorphous Ti40Zr25Ni8CugBe18 alloy is heating rate dependent, and the discrepancy between the Johnson-Mehl-Avrami method and the modified method increases with the increase of heating rate.