A near eutectic Al−12.6Si alloy was developed with 0.0wt%,2.0wt%,4.0wt%,and 6.0wt%Al−5Ti−1B master alloy.The micro-structural morphology,hardness,tensile strength,elongation,and fracture behaviour of the alloys were s...A near eutectic Al−12.6Si alloy was developed with 0.0wt%,2.0wt%,4.0wt%,and 6.0wt%Al−5Ti−1B master alloy.The micro-structural morphology,hardness,tensile strength,elongation,and fracture behaviour of the alloys were studied.The unmodified Al−12.6Si al-loy has an irregular needle and plate-like eutectic silicon(ESi)and coarse polygonal primary silicon(PSi)particles in the matrix-likeα-Al phase.The P_(Si),E_(Si),andα-Al morphology and volume fraction were changed due to the addition of the Al−5Ti−1B master alloy.The hardness,UTS,and elongation improved due to the microstructural modification.Nano-sized in-situ Al3Ti particles and ex-situ TiB_(2)particles caused the mi-crostructural modification.The fracture images of the developed alloys exhibit a ductile and brittle mode of fracture at the same time.The Al−5Ti−1B modified alloys have a more ductile mode of fracture and more dimples compared to the unmodified alloy.展开更多
基金The authors would also like to thank NIT,Durgapur RIG#2 project for financial support and the Director of National In-stitute of Technology Durgapur,India,for his continuous en-couragement.
文摘A near eutectic Al−12.6Si alloy was developed with 0.0wt%,2.0wt%,4.0wt%,and 6.0wt%Al−5Ti−1B master alloy.The micro-structural morphology,hardness,tensile strength,elongation,and fracture behaviour of the alloys were studied.The unmodified Al−12.6Si al-loy has an irregular needle and plate-like eutectic silicon(ESi)and coarse polygonal primary silicon(PSi)particles in the matrix-likeα-Al phase.The P_(Si),E_(Si),andα-Al morphology and volume fraction were changed due to the addition of the Al−5Ti−1B master alloy.The hardness,UTS,and elongation improved due to the microstructural modification.Nano-sized in-situ Al3Ti particles and ex-situ TiB_(2)particles caused the mi-crostructural modification.The fracture images of the developed alloys exhibit a ductile and brittle mode of fracture at the same time.The Al−5Ti−1B modified alloys have a more ductile mode of fracture and more dimples compared to the unmodified alloy.