The structure and magnetic properties of Fe76.5Si13.5B9Cu1 alloys with a nanocrystalline (NC) bcc Fe(Si) phase trom about 23 to 46 nm in diameter, which were first formed into amorphous ribbons and then annealed at va...The structure and magnetic properties of Fe76.5Si13.5B9Cu1 alloys with a nanocrystalline (NC) bcc Fe(Si) phase trom about 23 to 46 nm in diameter, which were first formed into amorphous ribbons and then annealed at various temperatures between 703 and 773 K, have been investigated. At annealing temperatures from 703 to 748 K, the single NC bcc(Si) phase is obtained in the crystallized alloys. The grain size and the Si-content in the NC bcc Fe(Si) phase for the alloys annealed at different temperatures are presented. The soft magnetic properties and the saturation magnetostriction for the alloys with the NC bcc Fe(Si) phase are also measured. The results show that, the saturation magnetizotion and the permeability are improved for the alloys with only the NC bcc Fe(Si) phase and become better with decreasing of the NC bcc phase size, and the saturation magnetostriction declines for the alloys with increasing Si-content in the NC bcc Fe(Si) phase.展开更多
用宽为20 mm、厚为25μm的Fe_(73.5)Cu_1Nb_3Si_(13.5)B_9非晶带材绕制成环形磁芯,将其经550℃×100 min晶化退火处理后制成纳米晶磁芯,研究了环氧树脂封装对纳米晶磁芯磁导率和伏安特性的影响。结果表明,与环氧树脂封装前相比,环...用宽为20 mm、厚为25μm的Fe_(73.5)Cu_1Nb_3Si_(13.5)B_9非晶带材绕制成环形磁芯,将其经550℃×100 min晶化退火处理后制成纳米晶磁芯,研究了环氧树脂封装对纳米晶磁芯磁导率和伏安特性的影响。结果表明,与环氧树脂封装前相比,环氧树脂封装后,纳米晶磁芯的磁导率μ、电感Ls、有效磁导率μe和品质因数Q减小;当励磁电流I小于800 m A时,感应电动势E减小,当励磁电流I大于800 m A时,感应电动势E增大。展开更多
文摘The structure and magnetic properties of Fe76.5Si13.5B9Cu1 alloys with a nanocrystalline (NC) bcc Fe(Si) phase trom about 23 to 46 nm in diameter, which were first formed into amorphous ribbons and then annealed at various temperatures between 703 and 773 K, have been investigated. At annealing temperatures from 703 to 748 K, the single NC bcc(Si) phase is obtained in the crystallized alloys. The grain size and the Si-content in the NC bcc Fe(Si) phase for the alloys annealed at different temperatures are presented. The soft magnetic properties and the saturation magnetostriction for the alloys with the NC bcc Fe(Si) phase are also measured. The results show that, the saturation magnetizotion and the permeability are improved for the alloys with only the NC bcc Fe(Si) phase and become better with decreasing of the NC bcc phase size, and the saturation magnetostriction declines for the alloys with increasing Si-content in the NC bcc Fe(Si) phase.
文摘用宽为20 mm、厚为25μm的Fe_(73.5)Cu_1Nb_3Si_(13.5)B_9非晶带材绕制成环形磁芯,将其经550℃×100 min晶化退火处理后制成纳米晶磁芯,研究了环氧树脂封装对纳米晶磁芯磁导率和伏安特性的影响。结果表明,与环氧树脂封装前相比,环氧树脂封装后,纳米晶磁芯的磁导率μ、电感Ls、有效磁导率μe和品质因数Q减小;当励磁电流I小于800 m A时,感应电动势E减小,当励磁电流I大于800 m A时,感应电动势E增大。