Ferroelectric Ba0.7Sr0.3TiO3（BST） and partially Pb^2＋ substituted for Ba^2＋ ceramics （Ba0.7-xPbx）Sr0.3TiO3 （x=0.1-0.4, BPST） were prepared by using conventional solid-reaction method. XRD analysis shows that t...Ferroelectric Ba0.7Sr0.3TiO3（BST） and partially Pb^2＋ substituted for Ba^2＋ ceramics （Ba0.7-xPbx）Sr0.3TiO3 （x=0.1-0.4, BPST） were prepared by using conventional solid-reaction method. XRD analysis shows that the samples microstructure changes from cubic phase to tetragonal one with the Pb^2＋ content increasing. ESEM analysis shows that the Pb^2＋ substituted samples have a denser and more uniform surface morphology than that of pure BST. Measured electrical properties suggest that the Pb^2＋ substitution for Ba^2＋ in the BST system enhances the ferroelectric performance obviously when x=0.2. In addition, the substitution increases the samples Curie temperature （To） r （Ba0.5Pb0.2）Sr0.3TiO3 ceramic has good ferroelectric properties measured at a maximal electric field of 30 kV/cm under the condition of room temperature. The corresponding saturated polarization （Ps）, remnant polarization （Pr） and coercive field （Ec） is respectively 15.687 μC/cm^2, 8.100 μ C/cm^2 and 6.611 kV/cm. The measured Tc of （Ba0.5Pb0.2）Sr0.3TiO3 is 117 ℃.展开更多
基金Funded by the National Natural Science Foundation of China (No. 60571009)
文摘Ferroelectric Ba0.7Sr0.3TiO3（BST） and partially Pb^2＋ substituted for Ba^2＋ ceramics （Ba0.7-xPbx）Sr0.3TiO3 （x=0.1-0.4, BPST） were prepared by using conventional solid-reaction method. XRD analysis shows that the samples microstructure changes from cubic phase to tetragonal one with the Pb^2＋ content increasing. ESEM analysis shows that the Pb^2＋ substituted samples have a denser and more uniform surface morphology than that of pure BST. Measured electrical properties suggest that the Pb^2＋ substitution for Ba^2＋ in the BST system enhances the ferroelectric performance obviously when x=0.2. In addition, the substitution increases the samples Curie temperature （To） r （Ba0.5Pb0.2）Sr0.3TiO3 ceramic has good ferroelectric properties measured at a maximal electric field of 30 kV/cm under the condition of room temperature. The corresponding saturated polarization （Ps）, remnant polarization （Pr） and coercive field （Ec） is respectively 15.687 μC/cm^2, 8.100 μ C/cm^2 and 6.611 kV/cm. The measured Tc of （Ba0.5Pb0.2）Sr0.3TiO3 is 117 ℃.