Ba0.95Ce0.8Ho0.2O3-a was prepared by high temperature solid-state reaction. X-ray diffraction （XRD） pattern showed that the material was of a single perovskite-type orthorhombic phase. Using the material as solid el...Ba0.95Ce0.8Ho0.2O3-a was prepared by high temperature solid-state reaction. X-ray diffraction （XRD） pattern showed that the material was of a single perovskite-type orthorhombic phase. Using the material as solid electrolyte and porous platinum as electrodes, the measurements of ionic transport number and conductivity of Ba0.95Ce0.8Ho0.2O3-a were performed by gas concentration cell and ac impedance spectroscopy methods in the temperature range of 600---1000 ℃in wet hydrogen, dry and wet air respectively. Ionic conduction of the material was investigated and compared with that of BaCe0.8Ho0.2O3-a. The results indicated that Ba0.95Ce0.8Ho0.2O3-a was a pure protonic conductor with the protonic transport number of 1 during 600---700℃ in wet hydrogen, a mixed conductor of protons and electrons with the protonic transport number of 0.97--0.93 in 800---1000 ℃. But BaCe0.8Ho0.2O3-a was almost a pure protonic conductor with the protonic transport number of 1 in 600---900 ℃ and 0.99 at 1000 ℃ in wet hydrogen. In dry air and in the temperature range of 600---1000 ℃, they were both mixed conductors of oxide ions and electronic holes, and the oxide-ionic transport numbers were 0.24--0.33 and 0.17--0.30 respectively. In wet air and in the temperature range of 600---1000 ℃, they were both mixed conductors of protons, oxide ions and electronic holes, the protonic transport numbers were 0.11--0.00 and 0.09--0.01 respectively, and the oxide-ionic transport numbers were 0.41--0.33 and 0.27--0.30 respectively. Protonic conductivity of Ba0.95Ce0.8Ho0.2O3-a in both wet hydrogen and wet air was higher than that of BaCe0.8Ho0.2O3-a in 600--- 800 ℃, but lower in 900--1000 ℃. Oxide-ionic conductivity of the material was higher than that of BaCe0.8Ho0.2O3-a in both dry air and wet air in 600---1000 ℃.展开更多
基金Project supported by theNat-ional Natural Science Foundation of China （No. 20171034） and the Natural Science Foundation of Education Department of Jiangsu Province （No. 07KJB 150126）.
文摘Ba0.95Ce0.8Ho0.2O3-a was prepared by high temperature solid-state reaction. X-ray diffraction （XRD） pattern showed that the material was of a single perovskite-type orthorhombic phase. Using the material as solid electrolyte and porous platinum as electrodes, the measurements of ionic transport number and conductivity of Ba0.95Ce0.8Ho0.2O3-a were performed by gas concentration cell and ac impedance spectroscopy methods in the temperature range of 600---1000 ℃in wet hydrogen, dry and wet air respectively. Ionic conduction of the material was investigated and compared with that of BaCe0.8Ho0.2O3-a. The results indicated that Ba0.95Ce0.8Ho0.2O3-a was a pure protonic conductor with the protonic transport number of 1 during 600---700℃ in wet hydrogen, a mixed conductor of protons and electrons with the protonic transport number of 0.97--0.93 in 800---1000 ℃. But BaCe0.8Ho0.2O3-a was almost a pure protonic conductor with the protonic transport number of 1 in 600---900 ℃ and 0.99 at 1000 ℃ in wet hydrogen. In dry air and in the temperature range of 600---1000 ℃, they were both mixed conductors of oxide ions and electronic holes, and the oxide-ionic transport numbers were 0.24--0.33 and 0.17--0.30 respectively. In wet air and in the temperature range of 600---1000 ℃, they were both mixed conductors of protons, oxide ions and electronic holes, the protonic transport numbers were 0.11--0.00 and 0.09--0.01 respectively, and the oxide-ionic transport numbers were 0.41--0.33 and 0.27--0.30 respectively. Protonic conductivity of Ba0.95Ce0.8Ho0.2O3-a in both wet hydrogen and wet air was higher than that of BaCe0.8Ho0.2O3-a in 600--- 800 ℃, but lower in 900--1000 ℃. Oxide-ionic conductivity of the material was higher than that of BaCe0.8Ho0.2O3-a in both dry air and wet air in 600---1000 ℃.