Green light-emitting Ba2SiO4：Eu^2＋ phosphors co-doped with La or Y were synthesized by conventional solid-state reaction technique in reductive atmosphere（a mixture of 5% H2 and 95% N2）.The results showed that the...Green light-emitting Ba2SiO4：Eu^2＋ phosphors co-doped with La or Y were synthesized by conventional solid-state reaction technique in reductive atmosphere（a mixture of 5% H2 and 95% N2）.The results showed that the co-doping of La and Y could greatly enhance the fluorescence intensity of Ba2SiO4：Eu2＋ phosphors.The optimum doping concentration expressed by the x value in（Ba0.985-1.5xREx）2SiO4：0.03Eu^2＋（RE=La or Y） was determined to be of 0.05.The excitation and emission peaks of all as-synthesized phosphors were wide bands.The excitation bands ranged from 250 to 400 nm, which matched well with the wavelength of near ultraviolet white light-emitting diodes（LED） chip and could be used as a potential candidate for the fabrication of white LED.The emission bands from 450 to 550 nm were typical 5d-4f transition emission of Eu^2＋ and displayed un-symmetry profiles because of the two substitution sites of Ba^2＋ with Eu^2＋.展开更多
The Ba3Y2（BO3）4：Eu^3＋ phosphor was synthesized using a high temperature solid-state reaction method and the luminescent characteristics were investigated. The emission spectrum exhibited one strong red emission at...The Ba3Y2（BO3）4：Eu^3＋ phosphor was synthesized using a high temperature solid-state reaction method and the luminescent characteristics were investigated. The emission spectrum exhibited one strong red emission at 613 nm, corresponding to the electric dipole 5D0-TF2 transition of Eu^3＋, under 365 nm excitation. The excitation spectrum of 613 nm indicated that the Ba3Y2（BO3）n：Eu^3＋ phosphor was effectively excited by ultraviolet （UV） （254, 365 and 400 nm） and blue （470 nm） light. The effect of Eu^3＋ concentration on the 613 nm emission of the Ba3Y2（BO3）n：Eu^3＋ phosphor was measured. The results showed that the emission intensity increased with increasing Eu^3＋ concentration, and then decreased. The CIE color coordinates of Ba3Y2（BO3）4：Eu^3＋ phosphor were x=0.641 and y=0.359 at 15 mol.% Eu^3＋.展开更多
The luminescent properties of Eu^3＋doped Ca2SiO4 red phosphors synthesized by the flux fusion reaction method were investigated. It was found that the excitation spectrum included two regions： the weak excitation ba...The luminescent properties of Eu^3＋doped Ca2SiO4 red phosphors synthesized by the flux fusion reaction method were investigated. It was found that the excitation spectrum included two regions： the weak excitation band below 325 nm and strong narrow peaks above 325 nm. The main peak of the excitation band was located at 400 nm. The peaks located at 290 nm were assigned to the combination of the charge transfer transition of O-Eu, peaks above 325 nm （325, 385, 400, 470, 511, and 539 nm） were assigned to the f-f transitions of Eu^3＋. The emission spectrum was dominated by the red peak located at 612 nm due to the electric dipole transition of ^5D0-^7F2. In addition, the effects of the Eu^3＋ content and charge compensators of Li^＋, Na^＋, K^＋, and Cl^- ions on the emission intensity were investigated. The experiment results suggested that the strongest emission was obtained when the concentration of the Eu^3＋ ions was 0.3 mol^-1, and Li^＋ ions gave the best improvement to enhance the emission intensity. Ca2SiO4：Eu^3＋, Li^＋ was thus suitable for low-cost trichromatic white light emitting diodes （WLED） based on UV InGaN chip.展开更多
基金Program for Changjiang Scholars and Innovative Research Team in University (IRT0730)the Key Project of Department of Science and Technology of Jiangxi ProvinceProject of Education Department of Jiangxi
文摘Green light-emitting Ba2SiO4：Eu^2＋ phosphors co-doped with La or Y were synthesized by conventional solid-state reaction technique in reductive atmosphere（a mixture of 5% H2 and 95% N2）.The results showed that the co-doping of La and Y could greatly enhance the fluorescence intensity of Ba2SiO4：Eu2＋ phosphors.The optimum doping concentration expressed by the x value in（Ba0.985-1.5xREx）2SiO4：0.03Eu^2＋（RE=La or Y） was determined to be of 0.05.The excitation and emission peaks of all as-synthesized phosphors were wide bands.The excitation bands ranged from 250 to 400 nm, which matched well with the wavelength of near ultraviolet white light-emitting diodes（LED） chip and could be used as a potential candidate for the fabrication of white LED.The emission bands from 450 to 550 nm were typical 5d-4f transition emission of Eu^2＋ and displayed un-symmetry profiles because of the two substitution sites of Ba^2＋ with Eu^2＋.
基金Supported by Natural Science Foundation of Liaoning Province(20170540074)Start-up Funding for Doctoral Researchers of Dalian Polytechnic University(61020726)~~
基金Project supported by the Hebei Provincial Technology Development Foundation (51215103b)Science Foundation of Hebei University (2006Q06)
文摘The Ba3Y2（BO3）4：Eu^3＋ phosphor was synthesized using a high temperature solid-state reaction method and the luminescent characteristics were investigated. The emission spectrum exhibited one strong red emission at 613 nm, corresponding to the electric dipole 5D0-TF2 transition of Eu^3＋, under 365 nm excitation. The excitation spectrum of 613 nm indicated that the Ba3Y2（BO3）n：Eu^3＋ phosphor was effectively excited by ultraviolet （UV） （254, 365 and 400 nm） and blue （470 nm） light. The effect of Eu^3＋ concentration on the 613 nm emission of the Ba3Y2（BO3）n：Eu^3＋ phosphor was measured. The results showed that the emission intensity increased with increasing Eu^3＋ concentration, and then decreased. The CIE color coordinates of Ba3Y2（BO3）4：Eu^3＋ phosphor were x=0.641 and y=0.359 at 15 mol.% Eu^3＋.
基金supported by Jiangxi Provincial Department of Education (GJJ08344)
文摘The luminescent properties of Eu^3＋doped Ca2SiO4 red phosphors synthesized by the flux fusion reaction method were investigated. It was found that the excitation spectrum included two regions： the weak excitation band below 325 nm and strong narrow peaks above 325 nm. The main peak of the excitation band was located at 400 nm. The peaks located at 290 nm were assigned to the combination of the charge transfer transition of O-Eu, peaks above 325 nm （325, 385, 400, 470, 511, and 539 nm） were assigned to the f-f transitions of Eu^3＋. The emission spectrum was dominated by the red peak located at 612 nm due to the electric dipole transition of ^5D0-^7F2. In addition, the effects of the Eu^3＋ content and charge compensators of Li^＋, Na^＋, K^＋, and Cl^- ions on the emission intensity were investigated. The experiment results suggested that the strongest emission was obtained when the concentration of the Eu^3＋ ions was 0.3 mol^-1, and Li^＋ ions gave the best improvement to enhance the emission intensity. Ca2SiO4：Eu^3＋, Li^＋ was thus suitable for low-cost trichromatic white light emitting diodes （WLED） based on UV InGaN chip.