The Ba3Y2（BO3）4：Eu^3＋ phosphor was synthesized using a high temperature solid-state reaction method and the luminescent characteristics were investigated. The emission spectrum exhibited one strong red emission at...The Ba3Y2（BO3）4：Eu^3＋ phosphor was synthesized using a high temperature solid-state reaction method and the luminescent characteristics were investigated. The emission spectrum exhibited one strong red emission at 613 nm, corresponding to the electric dipole 5D0-TF2 transition of Eu^3＋, under 365 nm excitation. The excitation spectrum of 613 nm indicated that the Ba3Y2（BO3）n：Eu^3＋ phosphor was effectively excited by ultraviolet （UV） （254, 365 and 400 nm） and blue （470 nm） light. The effect of Eu^3＋ concentration on the 613 nm emission of the Ba3Y2（BO3）n：Eu^3＋ phosphor was measured. The results showed that the emission intensity increased with increasing Eu^3＋ concentration, and then decreased. The CIE color coordinates of Ba3Y2（BO3）4：Eu^3＋ phosphor were x=0.641 and y=0.359 at 15 mol.% Eu^3＋.展开更多
Long-lasting phosphor Y2O2S ： Eu^3＋ , Mg^2＋ , Ti^4＋ was synthesized by a flux method and their luminescence properties were investigated. The result indicates that the unit cell parameter c is linearly increased w...Long-lasting phosphor Y2O2S ： Eu^3＋ , Mg^2＋ , Ti^4＋ was synthesized by a flux method and their luminescence properties were investigated. The result indicates that the unit cell parameter c is linearly increased with the increase of Eu2O3 content in Y2O2S： Eu^3＋ （0.01 ≤ x ≤0.10）. On the other hand, the change of unit cell parameter a is not linear dependence. In the Y2O2S： Eu^3 ＋ crystal structure, Eu^3＋ ions only replaced Y^3 ＋ ions＇ places in which it posited center position of c axis. With the increase of Eu2O3 content, the position of the strongest emission peak changed from 540 nm （5D1→^ 7F2 transition） to 626 nm （^5Do→^7TF2 transition）, and the maximum intensity was obtained when x = 0.09 in Y2O2S： Eu^3＋ （0.01 ≤x ≤0.10）. This is due to the environment of trivalent europium in the crystal structure of Y2O2S. Doping with Mg^2＋ or Ti^4＋. ions alone cannot get the good long-lasting afterglow effect, whereas co-doping with Mg^2 ＋ and Ti^4 ＋ ions and excited with 365 nm ultraviolet light, a strong thermoluminesence peak appeared, red and orange long-lasting phosphorescence （LLP） was also observed and the phosphorescence lasted nearly 3 h in the light perception of the dark-adapted human eye （0.32 mcd·m^-2）. Thus the LLP mechanism was analyzed.展开更多
The effects of CuO and H3BO3 additions on the low-temperature sintering,microstructure,and microwave dielectric properties of Ba2Ti3Nb4O18 ceramics were investigated.The addition of less amount of CuO （ 〈1 wt%） con...The effects of CuO and H3BO3 additions on the low-temperature sintering,microstructure,and microwave dielectric properties of Ba2Ti3Nb4O18 ceramics were investigated.The addition of less amount of CuO （ 〈1 wt%） considerably facilitated the densification of Ba2Ti3Nb4O18 ceramics.Appropriate addition of H3BO3 （ 〈3.5 wt%） remarkably improved the microwave dielectric properties of ceramics.The addition of H3BO3 and CuO successfully reduced the sintering temperature of Ba2Ti3Nb4O18 ceramics from 1300 to 1050 ℃.Ba2Ti3Nb4O18 ceramics sintered at 1 050 ℃ for 4 h with the addition of 1.0 wt% CuO and 3.5 wt% H3BO3 exhibited good microwave dielectric properties：er=33.74,Q？f=13 812 GHz,and tf=-5.35 ppm/°C at about 5.0 GHz.展开更多
基金Project supported by the Hebei Provincial Technology Development Foundation (51215103b)Science Foundation of Hebei University (2006Q06)
文摘The Ba3Y2（BO3）4：Eu^3＋ phosphor was synthesized using a high temperature solid-state reaction method and the luminescent characteristics were investigated. The emission spectrum exhibited one strong red emission at 613 nm, corresponding to the electric dipole 5D0-TF2 transition of Eu^3＋, under 365 nm excitation. The excitation spectrum of 613 nm indicated that the Ba3Y2（BO3）n：Eu^3＋ phosphor was effectively excited by ultraviolet （UV） （254, 365 and 400 nm） and blue （470 nm） light. The effect of Eu^3＋ concentration on the 613 nm emission of the Ba3Y2（BO3）n：Eu^3＋ phosphor was measured. The results showed that the emission intensity increased with increasing Eu^3＋ concentration, and then decreased. The CIE color coordinates of Ba3Y2（BO3）4：Eu^3＋ phosphor were x=0.641 and y=0.359 at 15 mol.% Eu^3＋.
文摘Long-lasting phosphor Y2O2S ： Eu^3＋ , Mg^2＋ , Ti^4＋ was synthesized by a flux method and their luminescence properties were investigated. The result indicates that the unit cell parameter c is linearly increased with the increase of Eu2O3 content in Y2O2S： Eu^3＋ （0.01 ≤ x ≤0.10）. On the other hand, the change of unit cell parameter a is not linear dependence. In the Y2O2S： Eu^3 ＋ crystal structure, Eu^3＋ ions only replaced Y^3 ＋ ions＇ places in which it posited center position of c axis. With the increase of Eu2O3 content, the position of the strongest emission peak changed from 540 nm （5D1→^ 7F2 transition） to 626 nm （^5Do→^7TF2 transition）, and the maximum intensity was obtained when x = 0.09 in Y2O2S： Eu^3＋ （0.01 ≤x ≤0.10）. This is due to the environment of trivalent europium in the crystal structure of Y2O2S. Doping with Mg^2＋ or Ti^4＋. ions alone cannot get the good long-lasting afterglow effect, whereas co-doping with Mg^2 ＋ and Ti^4 ＋ ions and excited with 365 nm ultraviolet light, a strong thermoluminesence peak appeared, red and orange long-lasting phosphorescence （LLP） was also observed and the phosphorescence lasted nearly 3 h in the light perception of the dark-adapted human eye （0.32 mcd·m^-2）. Thus the LLP mechanism was analyzed.
文摘The effects of CuO and H3BO3 additions on the low-temperature sintering,microstructure,and microwave dielectric properties of Ba2Ti3Nb4O18 ceramics were investigated.The addition of less amount of CuO （ 〈1 wt%） considerably facilitated the densification of Ba2Ti3Nb4O18 ceramics.Appropriate addition of H3BO3 （ 〈3.5 wt%） remarkably improved the microwave dielectric properties of ceramics.The addition of H3BO3 and CuO successfully reduced the sintering temperature of Ba2Ti3Nb4O18 ceramics from 1300 to 1050 ℃.Ba2Ti3Nb4O18 ceramics sintered at 1 050 ℃ for 4 h with the addition of 1.0 wt% CuO and 3.5 wt% H3BO3 exhibited good microwave dielectric properties：er=33.74,Q？f=13 812 GHz,and tf=-5.35 ppm/°C at about 5.0 GHz.