In order to prevent BaMgAl10O17∶Eu （BAM） phosphor from thermal degradation, MgF2-coatings on the surface of BAM were prepared by a sol-gel process. The coatings were characterized by X-ray photoelectron spectroscop...In order to prevent BaMgAl10O17∶Eu （BAM） phosphor from thermal degradation, MgF2-coatings on the surface of BAM were prepared by a sol-gel process. The coatings were characterized by X-ray photoelectron spectroscopy and scanning electron microscopy. The results indicate that BAM is successfully coated with homogenous, close MgF2 coatings. The photoluminescence and anti-thermal degradation properties of coated BAM were investigated under 254 and 147 nm excitations. The optimum anti-thermal degradation properties are obtained at the mass ratio of MgF2 to BAM 0.2% under 254 nm excitation and 0.5% under 147 nm excitation, respectively. It is considered that trace MgO formed after baked would cause different optimum coating thicknesses under 254 and 147 nm excitations.展开更多
基金Project(50272026) supported by the NSFC Project(2003AA324020) supported by the Hi tech Research and Develop ment Program of China
文摘In order to prevent BaMgAl10O17∶Eu （BAM） phosphor from thermal degradation, MgF2-coatings on the surface of BAM were prepared by a sol-gel process. The coatings were characterized by X-ray photoelectron spectroscopy and scanning electron microscopy. The results indicate that BAM is successfully coated with homogenous, close MgF2 coatings. The photoluminescence and anti-thermal degradation properties of coated BAM were investigated under 254 and 147 nm excitations. The optimum anti-thermal degradation properties are obtained at the mass ratio of MgF2 to BAM 0.2% under 254 nm excitation and 0.5% under 147 nm excitation, respectively. It is considered that trace MgO formed after baked would cause different optimum coating thicknesses under 254 and 147 nm excitations.