Nano-composite, perovskite Ba(1- x - y)Sr(x)TiFe(y)O3, denoted as (BSTFe) in powder form was derived via sol-gel (SG) method followed by sintering at fixed temperature 750℃ for one hour. The chemical composition, mor...Nano-composite, perovskite Ba(1- x - y)Sr(x)TiFe(y)O3, denoted as (BSTFe) in powder form was derived via sol-gel (SG) method followed by sintering at fixed temperature 750℃ for one hour. The chemical composition, morphology and structure of the powder samples were investigated by using X-ray diffraction (XRD), transmission electron microscope (TEM) and scanning electron microscope (SEM). The XRD characterization indicates formation of a cubic crystalline phase in the pure BST. A well defined perovskite phase with nano-crystallite sizes equal to about 34 nm was achieved from XRD for B10ST3F sample, while TEM study confirmed the obtained XRD results giving the following crystallite size value about 33.75 nm for the same sample. The dielectric A.C. conductivity was evaluated as a function of temperature and frequency ranging from 42 Hz up to 1 MHz.展开更多
The structural, dielectric and magnetic properties of pure and Fe-Co co-doped Ba0.9Sr0.1TiO3, (Ba(1-x)SrxTiO3, where (x = 0.10) and (Ba0.9Sr0.1Ti(1-x-y)FexCoyO3), where (x = 0.1, y = 0) and (x = 0 and y = 0.10) and (x...The structural, dielectric and magnetic properties of pure and Fe-Co co-doped Ba0.9Sr0.1TiO3, (Ba(1-x)SrxTiO3, where (x = 0.10) and (Ba0.9Sr0.1Ti(1-x-y)FexCoyO3), where (x = 0.1, y = 0) and (x = 0 and y = 0.10) and (x = 0.5, y = 0.5) in powder form, abbreviated as (BST) and (BST10FO), (BST10CO) and (BST5F5CO), respectively were prepared by a modified sol gel technique. Crystallization, surface morphology and electrical behavior of BST are improved by Fe3+ and Co2+ ions with optimized grain size. Phase identification by using X-ray diffraction and surface morphology will be studied by using transmission electron microscope (TEM) and scanning electron microscope imaging (SEM). Phase identification by using X-ray diffraction and surface morphology evaluation by using transmission electron microscope (TEM) and scanning electron microscope imaging (SEM) will be studied. The nano-scale presence and the formation of the tetragonal perovskite phase as well as the crystallinity were detected using the mentioned techniques. The dielectric properties of the prepared samples have been investigated as a function of temperature and frequency. The dielectric measurements are carried out in the frequency range of 42 Hz - 1 MHz, at temperature ranging between 25°C and 250°C. The results showed an abrupt decrease in the dielectric permittivity by increasing the frequency range. The magnetic hysteresis loop confirmed enhancement in the magnetization properties by co-doping with Fe3+-Co2+ ions. An increase in the saturation of the magnetization at room temperature was detected by decreasing the crystallite sizes of the prepared samples.展开更多
文摘Nano-composite, perovskite Ba(1- x - y)Sr(x)TiFe(y)O3, denoted as (BSTFe) in powder form was derived via sol-gel (SG) method followed by sintering at fixed temperature 750℃ for one hour. The chemical composition, morphology and structure of the powder samples were investigated by using X-ray diffraction (XRD), transmission electron microscope (TEM) and scanning electron microscope (SEM). The XRD characterization indicates formation of a cubic crystalline phase in the pure BST. A well defined perovskite phase with nano-crystallite sizes equal to about 34 nm was achieved from XRD for B10ST3F sample, while TEM study confirmed the obtained XRD results giving the following crystallite size value about 33.75 nm for the same sample. The dielectric A.C. conductivity was evaluated as a function of temperature and frequency ranging from 42 Hz up to 1 MHz.
文摘The structural, dielectric and magnetic properties of pure and Fe-Co co-doped Ba0.9Sr0.1TiO3, (Ba(1-x)SrxTiO3, where (x = 0.10) and (Ba0.9Sr0.1Ti(1-x-y)FexCoyO3), where (x = 0.1, y = 0) and (x = 0 and y = 0.10) and (x = 0.5, y = 0.5) in powder form, abbreviated as (BST) and (BST10FO), (BST10CO) and (BST5F5CO), respectively were prepared by a modified sol gel technique. Crystallization, surface morphology and electrical behavior of BST are improved by Fe3+ and Co2+ ions with optimized grain size. Phase identification by using X-ray diffraction and surface morphology will be studied by using transmission electron microscope (TEM) and scanning electron microscope imaging (SEM). Phase identification by using X-ray diffraction and surface morphology evaluation by using transmission electron microscope (TEM) and scanning electron microscope imaging (SEM) will be studied. The nano-scale presence and the formation of the tetragonal perovskite phase as well as the crystallinity were detected using the mentioned techniques. The dielectric properties of the prepared samples have been investigated as a function of temperature and frequency. The dielectric measurements are carried out in the frequency range of 42 Hz - 1 MHz, at temperature ranging between 25°C and 250°C. The results showed an abrupt decrease in the dielectric permittivity by increasing the frequency range. The magnetic hysteresis loop confirmed enhancement in the magnetization properties by co-doping with Fe3+-Co2+ ions. An increase in the saturation of the magnetization at room temperature was detected by decreasing the crystallite sizes of the prepared samples.