A sieres of Ba 1- x Sr x Zr y Ti 1- y O 3(0≤ x ≤0.4, 0< y <0.3) solid solutions was synthesized by soft chemical method below 100 ℃. The XRD and cell parameters component figures of the series of the solid so...A sieres of Ba 1- x Sr x Zr y Ti 1- y O 3(0≤ x ≤0.4, 0< y <0.3) solid solutions was synthesized by soft chemical method below 100 ℃. The XRD and cell parameters component figures of the series of the solid solutions powder demonstrate that the compounds are mutually miscible in the solid solutions. Furthermore, the observation through a TEM showed that the product has a shape of uniform, substantially spherical particles with an average particle size of 60 nm in diameter. The result of prepared ceramics shows that after being adulterated with Sr 2+ and Zr 4+ in pure BaTiO 3 phase, the dielectric constant was increased eight times at room temperature, while the dielectric loss was decreased three times.展开更多
A series of Ba1-xSrxTi1-yZryO3 (0≤x≤0.5, 0≤y≤0.4) and Ba1-xZnxTi1-ySnyO3 (0≤x≤0.3, 0≤y≤0.3) solid solutions were synthesized by low-temperature/low-pressure hydrothermal method below 170℃, 0.8 MPa. XRD patter...A series of Ba1-xSrxTi1-yZryO3 (0≤x≤0.5, 0≤y≤0.4) and Ba1-xZnxTi1-ySnyO3 (0≤x≤0.3, 0≤y≤0.3) solid solutions were synthesized by low-temperature/low-pressure hydrothermal method below 170℃, 0.8 MPa. XRD pattern and cell parameters-composition figures of these prepared powders demonstrated that they are completely miscible solid solutions based on BaTiO3. Furthermore, TEM showed that they have a shape of uniform, substantially spherical particles with an average particle size of 70 nm in diameter. The sintered ceramics of those powders doped by Sr2+ and Zr4+ or Zn2+ and Sn4+ have dielectric constant twelve times higher than and dielectric loss 1/6 those of pure BaTiO3 phase at room temperature.展开更多
A series of Ba1-xSrxMyTi1-yO3 (M = Zr, Sn, 0≤x≤0.4, 0≤y≤0.3) solid solutions were synthesized with the soft chemical method below 100 ℃. XRD pattern and cell parameters-composition figures of the prepared powder ...A series of Ba1-xSrxMyTi1-yO3 (M = Zr, Sn, 0≤x≤0.4, 0≤y≤0.3) solid solutions were synthesized with the soft chemical method below 100 ℃. XRD pattern and cell parameters-composition figures of the prepared powder demonstrate that they are completely miscible solid solutions based on BaTiO3. Furthermore, TEM shows that they have a shape of uniform, substantially spherical particles with an average particle size of 70 nm in diameter. The sintered ceramics of the powder doped with Sr2+ and Zr4+ or Sn4+ have dielectric constant eight times higher and dielectric loss thirty per cent lower than those of pure BaTiO3 phase at room temperature.展开更多
文摘A sieres of Ba 1- x Sr x Zr y Ti 1- y O 3(0≤ x ≤0.4, 0< y <0.3) solid solutions was synthesized by soft chemical method below 100 ℃. The XRD and cell parameters component figures of the series of the solid solutions powder demonstrate that the compounds are mutually miscible in the solid solutions. Furthermore, the observation through a TEM showed that the product has a shape of uniform, substantially spherical particles with an average particle size of 60 nm in diameter. The result of prepared ceramics shows that after being adulterated with Sr 2+ and Zr 4+ in pure BaTiO 3 phase, the dielectric constant was increased eight times at room temperature, while the dielectric loss was decreased three times.
基金the Natural Science Foundation of Hebei Province, China (Grant No. 299078).
文摘A series of Ba1-xSrxTi1-yZryO3 (0≤x≤0.5, 0≤y≤0.4) and Ba1-xZnxTi1-ySnyO3 (0≤x≤0.3, 0≤y≤0.3) solid solutions were synthesized by low-temperature/low-pressure hydrothermal method below 170℃, 0.8 MPa. XRD pattern and cell parameters-composition figures of these prepared powders demonstrated that they are completely miscible solid solutions based on BaTiO3. Furthermore, TEM showed that they have a shape of uniform, substantially spherical particles with an average particle size of 70 nm in diameter. The sintered ceramics of those powders doped by Sr2+ and Zr4+ or Zn2+ and Sn4+ have dielectric constant twelve times higher than and dielectric loss 1/6 those of pure BaTiO3 phase at room temperature.
文摘A series of Ba1-xSrxMyTi1-yO3 (M = Zr, Sn, 0≤x≤0.4, 0≤y≤0.3) solid solutions were synthesized with the soft chemical method below 100 ℃. XRD pattern and cell parameters-composition figures of the prepared powder demonstrate that they are completely miscible solid solutions based on BaTiO3. Furthermore, TEM shows that they have a shape of uniform, substantially spherical particles with an average particle size of 70 nm in diameter. The sintered ceramics of the powder doped with Sr2+ and Zr4+ or Sn4+ have dielectric constant eight times higher and dielectric loss thirty per cent lower than those of pure BaTiO3 phase at room temperature.