The recent increase in blast/bombing incidents all over the world has pushed the development of effective strengthening approaches to enhance the blast resistance of existing civil infrastructures.Engineered geopolyme...The recent increase in blast/bombing incidents all over the world has pushed the development of effective strengthening approaches to enhance the blast resistance of existing civil infrastructures.Engineered geopolymer composite(EGC)is a promising material featured by eco-friendly,fast-setting and strain-hardening characteristics for emergent strengthening and construction.However,the fiber optimization for preparing EGC and its protective effect on structural elements under blast scenarios are uncertain.In this study,laboratory tests were firstly conducted to evaluate the effects of fiber types on the properties of EGC in terms of workability,dry shrinkage,and mechanical properties in compression,tension and flexure.The experimental results showed that EGC containing PE fiber exhibited suitable workability,acceptable dry shrinkage and superior mechanical properties compared with other types of fibers.After that,a series of field tests were carried out to evaluate the effectiveness of EGC retrofitting layer on the enhancement of blast performance of typical elements.The tests include autoclaved aerated concrete(AAC)masonry walls subjected to vented gas explosion,reinforced AAC panels subjected to TNT explosion and plain concrete slabs subjected to contact explosion.It was found that EGC could effectively enhance the blast resistance of structural elements in different scenarios.For AAC masonry walls and panels,with the existence of EGC,the integrity of specimens could be maintained,and their deflections and damage were significantly reduced.For plain concrete slabs,the EGC overlay could reduce the diameter and depth of the crater and spallation of specimens.展开更多
Nanotubes, such as boron nitride nanotubes (BNNTs) and carbon nanotubes (CNTs), exhibit excellent mechanical properties. In this work, high-quality BNNTs were synthesized by ball milling and annealing. Subsequently, w...Nanotubes, such as boron nitride nanotubes (BNNTs) and carbon nanotubes (CNTs), exhibit excellent mechanical properties. In this work, high-quality BNNTs were synthesized by ball milling and annealing. Subsequently, well-dispersed 3vol%BNNTs/Cu and 3vol%CNTs/Cu composites were successfully prepared using ball milling, spark plasma sintering, and followed by hot-rolling. Moreover, the mechanical properties and strengthening mechanisms of BNNTs/Cu and CNTs/Cu composites were compared and discussed in details. At 293 K,both BNNTs/Cu and CNTs/Cu composites exhibited similar ultimate tensile strength (UTS) of~404 MPa, which is approximately 170%higher than pure Cu. However, at 873 K, the UTS and yield strength of BNNTs/Cu are 27%and 29%higher than those of CNTs/Cu, respectively.This difference can be attributed to the stronger inter-walls shear resistance, higher thermomechanical stability of BNNTs, and stronger bonding at the BNNTs/Cu interface as compared to the CNTs/Cu interface. These findings provide valuable insights into the potential of BNNTs as an excellent reinforcement for metal matrix composites, particularly at high temperature.展开更多
{1012¯}twins were introduced into the magnesium(Mg)plate AZ31 via pre-rolling along its transverse direction.The plates,both with and without the pre-induced{1012¯}twins,were subjected to uniaxial tension al...{1012¯}twins were introduced into the magnesium(Mg)plate AZ31 via pre-rolling along its transverse direction.The plates,both with and without the pre-induced{1012¯}twins,were subjected to uniaxial tension along different directions.Using crystal plasticity modeling,we found that the strengthening effect of the pre-induced{1012¯}twins on the macroscopic flow stress primarily arised from the increased slip resistance caused by the boundaries,rather than the orientation hardening due to the twinning reorientation(although the latter did make its contribution in some specific loading directions).Besides,the pre-existing{1012¯}twins were found,by both experiments and simulation,to promote the activity of prismatic and pyramidal<c+a>in the parent matrix of the material.Further analysis showed that the enhanced non-basal slip activity is related to the{1012¯}twin boundaries’low micro Hall-Petch slope ratios of non-basal slips to basal slip.With the critical resolved shear stress(CRSS)obtained from crystal plasticity modeling and the orientation data from EBSD,a probability-based slip transfer model was proposed.The model predicts higher slip transfer probabilities and thus lower strain concentration tendencies at{1012¯}twin boundaries than that at grain boundaries,which agrees with the experimental observation that the strain localization was primarily associated with the latter.The present findings are helpful scientifically,in deepening our understanding of how the pre-induced{1012¯}twins affect the strength and slip activity of Mg alloys,and technologically,in guiding the design of the pre-strain protocol of Mg alloys.展开更多
Mg/Al bimetal combines the advantages of both aluminum and magnesium and has broad application prospects in automotive, aerospace,weapons, digital products and so on. The compound casting has the characteristics of lo...Mg/Al bimetal combines the advantages of both aluminum and magnesium and has broad application prospects in automotive, aerospace,weapons, digital products and so on. The compound casting has the characteristics of low cost, easy to achieve metallurgical combination and suitable for the preparation of complex bimetallic parts. However, bimetallic joint strength is low due to differences of physical properties between Al and Mg, oxide film on metallic surface and interfacial Al-Mg IMCs, which is closely related to the interfacial microstructure and properties. Therefore, how to control the interface of the bimetal to achieve performance enhancement is the focus and difficulty in this field. At present, there are mainly the following strengthening methods. First, the “zincate galvanizing” and “electrolytic polishing+anodic oxidation” technology were exert on the surface of Al alloy to remove and break the oxide film, which improved the wettability between Al and Mg. Second, the undesirable Al-Mg IMCs were reduce or elimination by adding the interlayers(Zn, Ni and Ni-Cu). Thirdly, the evolution process of interfacial microstructure was changed and fine strengthening phases were formed by adding Si element to Al alloy or rare earth element to Mg alloy. Fourthly, mechanical vibration and ultrasonic vibration were applied in the process of the filling and solidification to refine and homogenize the interfacial structure. Finally, some other methods, including secondary rolling, thermal modification, heat treatment and constructing exterior 3D morphology, also can be used to regulate the interfacial microstructure and compositions. The above strengthening methods can be used alone or in combination to achieve bimetallic strengthening. Finally, the future development direction of the Mg/Al bimetal is prospected, which provides some new ideas for the development and application of the Mg/Al bimetal.展开更多
Solid solution strengthening(SSS)is one of the main contributions to the desired tensile properties of nickel-based superalloys for turbine blades and disks.The value of SSS can be calculated by using Fleischer’s and...Solid solution strengthening(SSS)is one of the main contributions to the desired tensile properties of nickel-based superalloys for turbine blades and disks.The value of SSS can be calculated by using Fleischer’s and Labusch’s theories,while the model parameters are incorporated without fitting to experimental data of complex alloys.In thiswork,four diffusionmultiples consisting of multicomponent alloys and pure Niare prepared and characterized.The composition and microhardness of singleγphase regions in samples are used to quantify the SSS.Then,Fleischer’s and Labusch’s theories are examined based on high-throughput experiments,respectively.The fitted solid solution coefficients are obtained based on Labusch’s theory and experimental data,indicating higher accuracy.Furthermore,six machine learning algorithms are established,providing a more accurate prediction compared with traditional physical models and fitted physical models.The results show that the coupling of highthroughput experiments and machine learning has great potential in the field of performance prediction and alloy design.展开更多
The aim of this study is to investigate the influence of fiber reinforcement polymer (FRP) on shear behavior of reinforcement concrete (RC) beams with various guidelines. The FRP thickness, beam depth and concrete str...The aim of this study is to investigate the influence of fiber reinforcement polymer (FRP) on shear behavior of reinforcement concrete (RC) beams with various guidelines. The FRP thickness, beam depth and concrete strength at ultimate load are considered as main strength parameters. A finite element (FE) by using ANSYS computer program was used to analyze the reinforced concrete beams. The numerical models were used to investigate the effect of beam depth, concrete strength, CFRP sheet configuration, and CFRP sheet thickness on the behavior of reinforced concrete beams strengthened with CFRP sheets compared with different guidelines. The results from ACI guideline show little difference compared with FE, which make it suitable for RC beams strengthened with FRP sheets.展开更多
Precipitation strengthening is a key strategy for improving the overall mechanical properties of Mg alloys. In Mg-Al alloys, basal precipitates are known to strengthen against twinning, resulting in an increase in the...Precipitation strengthening is a key strategy for improving the overall mechanical properties of Mg alloys. In Mg-Al alloys, basal precipitates are known to strengthen against twinning, resulting in an increase in the critical resolved shear stress(CRSS) necessary for continued deformation. Although several models have been proposed to quantify the influence of precipitate shape, size, and distribution on the CRSS, the accuracy, scope, and applicability of these models has not been fully assessed. Accordingly, the objectives of this study are:(i)to analyze the accuracy of analytical models proposed in the literature for precipitation strengthening against twin thickening and propagation(in Mg-Al alloys) using phase-field(PF) simulations,(ii) to propose modifications to these model forms to better capture the observed trends in the PF data, and(iii) to subsequently test the predictiveness of the extended models in extrapolating to experimental strengthening data.First, using an atomistically-informed phase-field method, the interactions between migrating twin boundaries(during the propagation and thickening stages) and basal plates are simulated for different precipitate sizes and arrangements. In general, comparison of the increase in CRSS determined from the PF simulations and the predictions from four precipitation strengthening models reveals that modifications are necessary to the model forms to extend their applicability to precipitation strengthening against both twin thickening and propagation. A subsequent comparison between predictions from the extended models and experimental strengthening data for peak age-hardened samples reveals that the(extended) single dislocation and dislocation wall models provide reasonably accurate values of the increase in CRSS.Ultimately, the results presented here help elucidate the fidelity and applicability of the various hardening models in predicting precipitation strenghtening effects in technologically important alloys.展开更多
The low-cost Fe-Cu,Fe-Ni,and Cu-based high-entropy alloys exhibit a widespread utilization prospect.However,these potential applications have been limited by their low strength.In this study,a novel Fe_(31)Cu_(31)Ni_(...The low-cost Fe-Cu,Fe-Ni,and Cu-based high-entropy alloys exhibit a widespread utilization prospect.However,these potential applications have been limited by their low strength.In this study,a novel Fe_(31)Cu_(31)Ni_(28)Al_(4)Ti_(3)Co_(3) immiscible high-entropy alloy(HEA)was developed.After vacuum arc melting and copper mold suction casting,this HEA exhibits a unique phase separation microstructure,which consists of striped Cu-rich regions and Fe-rich region.Further magnification of the striped Cu-rich region reveals that it is composed of a Cu-rich dot-like phase and a Fe-rich region.The aging alloy is further strengthened by a L1_(2)-Ni_(3)(AlTi)nanoprecipitates,achieving excellent yield strength(1185 MPa)and uniform ductility(~8.8%).The differential distribution of the L1_(2) nanoprecipitate in the striped Cu-rich region and the external Fe-rich region increased the strength difference between these two regions,which increased the strain gradient and thus improved hetero-deformation induced(HDI)hardening.This work provides a new route to improve the HDI hardening of Fe-Cu alloys.展开更多
Solid solution-strengthened copper alloys have the advantages of a simple composition and manufacturing process,high mechanical and electrical comprehensive performances,and low cost;thus,they are widely used in high-...Solid solution-strengthened copper alloys have the advantages of a simple composition and manufacturing process,high mechanical and electrical comprehensive performances,and low cost;thus,they are widely used in high-speed rail contact wires,electronic component connectors,and other devices.Overcoming the contradiction between low alloying and high performance is an important challenge in the development of solid solution-strengthened copper alloys.Taking the typical solid solution-strengthened alloy Cu-4Zn-1Sn as the research object,we proposed using the element In to replace Zn and Sn to achieve low alloying in this work.Two new alloys,Cu-1.5Zn-1Sn-0.4In and Cu-1.5Zn-0.9Sn-0.6In,were designed and prepared.The total weight percentage content of alloying elements decreased by 43%and 41%,respectively,while the product of ultimate tensile strength(UTS)and electrical conductivity(EC)of the annealed state increased by 14%and 15%.After cold rolling with a 90%reduction,the UTS of the two new alloys reached 576 and 627MPa,respectively,the EC was 44.9%IACS and 42.0%IACS,and the product of UTS and EC(UTS×EC)was 97%and 99%higher than that of the annealed state alloy.The dislocations proliferated greatly in cold-rolled alloys,and the strengthening effects of dislocations reached 332 and 356 MPa,respectively,which is the main reason for the considerable improvement in mechanical properties.展开更多
Labor education is an essential component of college and university education that can help students to develop a strong work ethic,acquire practical skills,and better understand the value of work.Strengthening labor ...Labor education is an essential component of college and university education that can help students to develop a strong work ethic,acquire practical skills,and better understand the value of work.Strengthening labor education for college and university students is an urgent need of the high-quality development of the society and the internal requirement of promoting the all-round development of individuals.This study analyzes the importance of strengthening labor education for college and university students in the new era and proposes four practical pathways which draw on labor courses and campus activities,social practices,scientific research projects,and internships.After implementing these pathways,a survey of 967 students showed that students’understanding and awareness of labor was deepened,their hands-on skills and interests in science and labor practices were improved,and they became more cordially respectful to the working class.Taken together,the exploration and practice of these pathways helps college and university students to recognize their abilities,strengths,and interests,and guides them to form good labor habits that permeate all aspects of their studies and lives.展开更多
The aerospace and military sectors have widely used AA7075, a type of 7075 aluminum alloy, due to its exceptional mechanical performance. Selective laser melting (SLM) is a highly effective method for producing intric...The aerospace and military sectors have widely used AA7075, a type of 7075 aluminum alloy, due to its exceptional mechanical performance. Selective laser melting (SLM) is a highly effective method for producing intricate metallic components, particularly in the case of aluminum alloys like Al-Si-Mg. Nevertheless, the production of high-strength AA7075 by SLM is challenging because of its susceptibility to heat cracking and elemental vaporization. In this study, AA7075 powders were mechanically mixed with SiC and TiC particles. Subsequently, this new type of AA7075 powder was effectively utilized in green laser printing to create solid components with fine-grain strengthening microstructures consisting of equiaxial grains. These as-printed parts exhibit a tensile strength of up to 350 MPa and a ductility exceeding 2.1%. Hardness also increases with the increasing content of mixed powder, highlighting the essential role of SiC and TiC in SLM for improved hardness and tensile strength performance. .展开更多
Precipitation strengthening is a crucial microscopic mechanism for enhancing the strength of magnesium alloys. In order to elucidate the influence of precipitation on the microscopic deformation mechanisms and macrosc...Precipitation strengthening is a crucial microscopic mechanism for enhancing the strength of magnesium alloys. In order to elucidate the influence of precipitation on the microscopic deformation mechanisms and macroscopic mechanical response of magnesium alloys under cyclic loading conditions, we employed a crystal plasticity model to analyze the stress-strain curves, specific crystal plane diffraction intensities, and the temporal evolution of various microscopic deformation mechanisms and twinning volume fractions for an extruded magnesium alloy, AXM10304, containing coherent precipitates. The research findings indicate that precipitation does not fundamentally alter the microscopic mechanisms of this alloy. However, it hinders twinning during the compression stage, mildly promotes detwinning during the tension stage, and enhances tension secondary hardening by elevating the difficulty of activation of the prismatic slip.展开更多
The effects of large cold deformation after solution treatment on the precipitation characteristic and deformation strength of 2024 and 7A04 Al alloys were investigated.The tensile property tests indicate that the age...The effects of large cold deformation after solution treatment on the precipitation characteristic and deformation strength of 2024 and 7A04 Al alloys were investigated.The tensile property tests indicate that the ageing response of the 2024 aluminum alloy is accelerated when treated by cold deformation after solution treatment,and the tensile strength is increased to about 140 MPa while the elongation still keeps above 8%.However,compared with the 2024 alloys,although the aging response of the cold deformed 7A04 aluminum alloy is accelerated,the tensile strength has not changed obviously and the elongation is even decreased drastically.The results of TEM observation show that the S’ phase inside the dislocation cells and at the boundaries of the dislocation cells of the 2024 aluminum alloy has a uniform distribution.But in 7A04 aluminum alloy the club-shaped η’ phase forms at the boundaries of dislocation cells even on dislocation lines,while there still exists small spheric G.P zone in the region with less dislocation.In addition the precipitates in 7A04 alloy with cold rolling present more obvious tendency of growth and coarsening than those without cold rolling.It is indicated that the coherent strain energy of the cylinder formed G.P zones with matrix in the 2024 alloy is smaller than that of the spherical G.P zone in 7A04 alloy,for which a different distribution of precipitates and different effect of strengthening are caused in artificial ageing after resolution treatment and large cold deformation.展开更多
The integral impeller and blisk of an aero-engine are high performance parts with complex structure and made of difficult-to-cut materials. The blade surfaces of the integral impeller and blisk are functional surfaces...The integral impeller and blisk of an aero-engine are high performance parts with complex structure and made of difficult-to-cut materials. The blade surfaces of the integral impeller and blisk are functional surfaces for power transmission, and their surface integrity has signif- icant effects on the aerodynamic efficiency and service life of an aero-engine. Thus, it is indispensable to finish and strengthen the blades before use. This paper presents a comprehensive literature review of studies on finishing and strengthening technologies for the impeller and blisk of aero-engines. The review includes independent and inte- grated finishing and strengthening technologies and dis- cusses advanced rotational abrasive flow machining with back-pressure used for finishing the integral impeller and blisk. A brief assessment of future research problems and directions is also presented.展开更多
There are two kinds of internationally recognized approaches in terms of lightweight design.One is based on fatigue accumulated damage theory to achieve better reliability by optimal structural design; another is to u...There are two kinds of internationally recognized approaches in terms of lightweight design.One is based on fatigue accumulated damage theory to achieve better reliability by optimal structural design; another is to use high performance lightweight materials.The former method takes very few considerations on the structural strengthening effects caused by the massive small loads in service.In order to ensure safety,the design is usually conservative,but the strength potential of the component is not fully exerted.In the latter method,cost is the biggest obstacle to lightweight materials in automotive applications.For the purpose of light weighting design on a fuel cell vehicle,the new design method is applied on drive shafts.The method is based on the low amplitude load strengthening characteristics of the material,and allows the stress,corresponding to test load,to enter into the strengthened range of the material.Under this condition,the light weighting design should assure that the reliability of the shaft is not impaired,even maximizes the strength potential of machine part in order to achieve the weight reduction and eventually to reduce the cost.At last,the feasibility of the design is verified by means of strength analysis and modal analysis based on the CAD model of light weighted shaft.The design applies to the load case of half shaft in independent axle,also provides technological reference for the structural lightweight design of vehicles and other machineries.展开更多
It is known that the strength of alloys can be successfully improved by rapid solidification. The paper presents a process where Cu-Cr-Sn-Zn lead frame alloy is produced by rapid solidification and aging. The microcry...It is known that the strength of alloys can be successfully improved by rapid solidification. The paper presents a process where Cu-Cr-Sn-Zn lead frame alloy is produced by rapid solidification and aging. The microcrystalline structure of rapidly solidified Cu-Cr-Sn-Zn alloy is smaller grain structure examined by optical metallography. The effects of aging processes on the microstructure and properties of the lead frame alloy were investigated. Aged at 500℃ for 15 min the fine coherent precipitates Cr distribute in Cu matrix observed by transmission electron microscopy and the properties of hardness and electrical conductivity properties can reach 178HV and 61%IACS, respectively.展开更多
The microstructure of dislocation in two kinds of ahiminum-lithium alloys 2090 and 2090 + Ce was observed by means of TEM technology. The contributions of δ' and T1 precipitates to strength were separately calculat...The microstructure of dislocation in two kinds of ahiminum-lithium alloys 2090 and 2090 + Ce was observed by means of TEM technology. The contributions of δ' and T1 precipitates to strength were separately calculated by using the results of quantitative metallography and analysis of micro-deformation behavior; the co-strengthening effect of δ' and T1 precipitates was studied. The results show that the adding relationship of co-strengthening of δ' and T1 is in accordance with q = 1.4 form at the near peak-aged condition, i.e., △τ^1.4δ = △τ^1.4δ+ △τ^1.4T1, but the adding relationship is approximately a linear relation (q = 1) at the under-aged condition and becomes the parabola form when over-aged (q = 2). The adding relationship of co-strengthening contribution of δ' and T1 is obviously dependent on aging time.展开更多
Lightweight design requires an accurate life prediction for structures and components under service loading histories. However, predicted life with the existing methods seems too conservative in some cases, leading to...Lightweight design requires an accurate life prediction for structures and components under service loading histories. However, predicted life with the existing methods seems too conservative in some cases, leading to a heavy structure. Because these methods are established on the basis that load cycles would only cause fatigue damage, ignore the strengthening effect of loads. Based on Palmgren-Miner Rule (PMR), this paper introduces a new method for fatigue life prediction under service loadings by taking into account the strengthening effect of loads below the fatigue limit. In this method, the service loadings are classified into three categories: damaging load, strengthening load and none-effect load, and the process for fatigue life prediction is divided into two stages: stage I and stage II, according to the best strengthening number of cycles. During stage I, fatigue damage is calculated considering both the strengthening and damaging effect of load cycles. While during stage II, only the damaging effect is considered. To validate this method, fatigue lives of automobile half shaft and torsion beam rear axle are calculated based on the new method and traditional methods, such as PMR and Modified Miner Rule (MMR), and fatigue tests of the two components are conducted under service loading histories. The tests results show that the percentage errors of the predicted life with the new method to mean life of tests for the two components are –3.78% and –1.76% separately, much lesser than that with PMR and MMR. By considering the strengthening effect of loads below the fatigue limit, the new method can significantly improve the accuracy for fatigue life prediction. Thus lightweight design can be fully realized in the design stage.展开更多
The microstructure and strengthening mechanisms of as-cast Mg-6Al-6Nd alloy were studied. The results show that the addition of 6 wt.% Nd into Mg-6Al alloy leads to the precipitation of Al11Nd3 and Al2Nd phases and de...The microstructure and strengthening mechanisms of as-cast Mg-6Al-6Nd alloy were studied. The results show that the addition of 6 wt.% Nd into Mg-6Al alloy leads to the precipitation of Al11Nd3 and Al2Nd phases and decrease in the content of Al solid soluted in Mg-Al matrix. The volume fractions of Al11Nd3 and Al2Nd phases are 3.64% and 0.34%, respectively. Compared with Mg-6Al alloy, the ultimate strength, yielding strength, and elongation of Mg-6Al-6Nd alloy at room temperature and 175℃ are enhanced in some degrees. The strengthening mechanisms of Mg-6Al-6Nd alloy are mainly composed of solid solution strengthening of Al solid soluted in Mg-Al matrix and grain refmement strengthening, dispersion strengthening, and composite strengthening brought by the precipitation of Al11Nd3 phase. The composite strengthening includes the load transfer from the matrix to Al11Nd3 phase and the enhancement of dislocation density due to the geometrical mismatch and thermal mismatch between the matrix and Al11Nd3 phase.展开更多
基金National Natural Science Foundation of China(Grant Nos.51908188 and 51938011).
文摘The recent increase in blast/bombing incidents all over the world has pushed the development of effective strengthening approaches to enhance the blast resistance of existing civil infrastructures.Engineered geopolymer composite(EGC)is a promising material featured by eco-friendly,fast-setting and strain-hardening characteristics for emergent strengthening and construction.However,the fiber optimization for preparing EGC and its protective effect on structural elements under blast scenarios are uncertain.In this study,laboratory tests were firstly conducted to evaluate the effects of fiber types on the properties of EGC in terms of workability,dry shrinkage,and mechanical properties in compression,tension and flexure.The experimental results showed that EGC containing PE fiber exhibited suitable workability,acceptable dry shrinkage and superior mechanical properties compared with other types of fibers.After that,a series of field tests were carried out to evaluate the effectiveness of EGC retrofitting layer on the enhancement of blast performance of typical elements.The tests include autoclaved aerated concrete(AAC)masonry walls subjected to vented gas explosion,reinforced AAC panels subjected to TNT explosion and plain concrete slabs subjected to contact explosion.It was found that EGC could effectively enhance the blast resistance of structural elements in different scenarios.For AAC masonry walls and panels,with the existence of EGC,the integrity of specimens could be maintained,and their deflections and damage were significantly reduced.For plain concrete slabs,the EGC overlay could reduce the diameter and depth of the crater and spallation of specimens.
基金financially supported by the National Natural Science Foundation of China (No.52171144)。
文摘Nanotubes, such as boron nitride nanotubes (BNNTs) and carbon nanotubes (CNTs), exhibit excellent mechanical properties. In this work, high-quality BNNTs were synthesized by ball milling and annealing. Subsequently, well-dispersed 3vol%BNNTs/Cu and 3vol%CNTs/Cu composites were successfully prepared using ball milling, spark plasma sintering, and followed by hot-rolling. Moreover, the mechanical properties and strengthening mechanisms of BNNTs/Cu and CNTs/Cu composites were compared and discussed in details. At 293 K,both BNNTs/Cu and CNTs/Cu composites exhibited similar ultimate tensile strength (UTS) of~404 MPa, which is approximately 170%higher than pure Cu. However, at 873 K, the UTS and yield strength of BNNTs/Cu are 27%and 29%higher than those of CNTs/Cu, respectively.This difference can be attributed to the stronger inter-walls shear resistance, higher thermomechanical stability of BNNTs, and stronger bonding at the BNNTs/Cu interface as compared to the CNTs/Cu interface. These findings provide valuable insights into the potential of BNNTs as an excellent reinforcement for metal matrix composites, particularly at high temperature.
基金supported by the National Natural Science Foundation of China(grant numbers 51801147,51790482,51722104,51625103,and 51621063)the National Key Re-search and Development Program of China(grant number 2017YFB0702301)the International Joint Laboratory for Micro/Nano Manufacturing and Measurement Technologies.
文摘{1012¯}twins were introduced into the magnesium(Mg)plate AZ31 via pre-rolling along its transverse direction.The plates,both with and without the pre-induced{1012¯}twins,were subjected to uniaxial tension along different directions.Using crystal plasticity modeling,we found that the strengthening effect of the pre-induced{1012¯}twins on the macroscopic flow stress primarily arised from the increased slip resistance caused by the boundaries,rather than the orientation hardening due to the twinning reorientation(although the latter did make its contribution in some specific loading directions).Besides,the pre-existing{1012¯}twins were found,by both experiments and simulation,to promote the activity of prismatic and pyramidal<c+a>in the parent matrix of the material.Further analysis showed that the enhanced non-basal slip activity is related to the{1012¯}twin boundaries’low micro Hall-Petch slope ratios of non-basal slips to basal slip.With the critical resolved shear stress(CRSS)obtained from crystal plasticity modeling and the orientation data from EBSD,a probability-based slip transfer model was proposed.The model predicts higher slip transfer probabilities and thus lower strain concentration tendencies at{1012¯}twin boundaries than that at grain boundaries,which agrees with the experimental observation that the strain localization was primarily associated with the latter.The present findings are helpful scientifically,in deepening our understanding of how the pre-induced{1012¯}twins affect the strength and slip activity of Mg alloys,and technologically,in guiding the design of the pre-strain protocol of Mg alloys.
基金the supports provided by the National Natural Science Foundation of China (Grant Nos.52271102,52075198 and 52205359)the China Post-doctoral Science Foundation (Grant No.2021M691112)the Analytical and Testing Center,HUST。
文摘Mg/Al bimetal combines the advantages of both aluminum and magnesium and has broad application prospects in automotive, aerospace,weapons, digital products and so on. The compound casting has the characteristics of low cost, easy to achieve metallurgical combination and suitable for the preparation of complex bimetallic parts. However, bimetallic joint strength is low due to differences of physical properties between Al and Mg, oxide film on metallic surface and interfacial Al-Mg IMCs, which is closely related to the interfacial microstructure and properties. Therefore, how to control the interface of the bimetal to achieve performance enhancement is the focus and difficulty in this field. At present, there are mainly the following strengthening methods. First, the “zincate galvanizing” and “electrolytic polishing+anodic oxidation” technology were exert on the surface of Al alloy to remove and break the oxide film, which improved the wettability between Al and Mg. Second, the undesirable Al-Mg IMCs were reduce or elimination by adding the interlayers(Zn, Ni and Ni-Cu). Thirdly, the evolution process of interfacial microstructure was changed and fine strengthening phases were formed by adding Si element to Al alloy or rare earth element to Mg alloy. Fourthly, mechanical vibration and ultrasonic vibration were applied in the process of the filling and solidification to refine and homogenize the interfacial structure. Finally, some other methods, including secondary rolling, thermal modification, heat treatment and constructing exterior 3D morphology, also can be used to regulate the interfacial microstructure and compositions. The above strengthening methods can be used alone or in combination to achieve bimetallic strengthening. Finally, the future development direction of the Mg/Al bimetal is prospected, which provides some new ideas for the development and application of the Mg/Al bimetal.
基金supported by National Science and Technology Major Project (J2019-IV-0003-0070)the Natural Science Foundation of China (91860105,52074366)+4 种基金China Postdoctoral Science Foundation (2019M662799)Natural Science Foundation of Hunan Province of China (2021JJ40757)the Science and Technology Innovation Program of Hunan Province (2021RC3131)Changsha Municipal Natural Science Foundation (kq2014126)Project Supported by State Key Laboratory of Powder Metallurgy,Central South University,Changsha,China.
文摘Solid solution strengthening(SSS)is one of the main contributions to the desired tensile properties of nickel-based superalloys for turbine blades and disks.The value of SSS can be calculated by using Fleischer’s and Labusch’s theories,while the model parameters are incorporated without fitting to experimental data of complex alloys.In thiswork,four diffusionmultiples consisting of multicomponent alloys and pure Niare prepared and characterized.The composition and microhardness of singleγphase regions in samples are used to quantify the SSS.Then,Fleischer’s and Labusch’s theories are examined based on high-throughput experiments,respectively.The fitted solid solution coefficients are obtained based on Labusch’s theory and experimental data,indicating higher accuracy.Furthermore,six machine learning algorithms are established,providing a more accurate prediction compared with traditional physical models and fitted physical models.The results show that the coupling of highthroughput experiments and machine learning has great potential in the field of performance prediction and alloy design.
文摘The aim of this study is to investigate the influence of fiber reinforcement polymer (FRP) on shear behavior of reinforcement concrete (RC) beams with various guidelines. The FRP thickness, beam depth and concrete strength at ultimate load are considered as main strength parameters. A finite element (FE) by using ANSYS computer program was used to analyze the reinforced concrete beams. The numerical models were used to investigate the effect of beam depth, concrete strength, CFRP sheet configuration, and CFRP sheet thickness on the behavior of reinforced concrete beams strengthened with CFRP sheets compared with different guidelines. The results from ACI guideline show little difference compared with FE, which make it suitable for RC beams strengthened with FRP sheets.
基金fully funded by the U.S.Dept.of Energy,Office of Basic Energy Sciences Project FWP 06SCPE401supported by the U.S.Department of Energy National Nuclear Security Administration under Contract No.89233218CNA000001。
文摘Precipitation strengthening is a key strategy for improving the overall mechanical properties of Mg alloys. In Mg-Al alloys, basal precipitates are known to strengthen against twinning, resulting in an increase in the critical resolved shear stress(CRSS) necessary for continued deformation. Although several models have been proposed to quantify the influence of precipitate shape, size, and distribution on the CRSS, the accuracy, scope, and applicability of these models has not been fully assessed. Accordingly, the objectives of this study are:(i)to analyze the accuracy of analytical models proposed in the literature for precipitation strengthening against twin thickening and propagation(in Mg-Al alloys) using phase-field(PF) simulations,(ii) to propose modifications to these model forms to better capture the observed trends in the PF data, and(iii) to subsequently test the predictiveness of the extended models in extrapolating to experimental strengthening data.First, using an atomistically-informed phase-field method, the interactions between migrating twin boundaries(during the propagation and thickening stages) and basal plates are simulated for different precipitate sizes and arrangements. In general, comparison of the increase in CRSS determined from the PF simulations and the predictions from four precipitation strengthening models reveals that modifications are necessary to the model forms to extend their applicability to precipitation strengthening against both twin thickening and propagation. A subsequent comparison between predictions from the extended models and experimental strengthening data for peak age-hardened samples reveals that the(extended) single dislocation and dislocation wall models provide reasonably accurate values of the increase in CRSS.Ultimately, the results presented here help elucidate the fidelity and applicability of the various hardening models in predicting precipitation strenghtening effects in technologically important alloys.
基金Projects(52001083,52171111,U2141207)supported by the National Natural Science Foundation of ChinaProject(LH2020E060)supported by the Natural Science Foundation of Heilongjiang,China。
文摘The low-cost Fe-Cu,Fe-Ni,and Cu-based high-entropy alloys exhibit a widespread utilization prospect.However,these potential applications have been limited by their low strength.In this study,a novel Fe_(31)Cu_(31)Ni_(28)Al_(4)Ti_(3)Co_(3) immiscible high-entropy alloy(HEA)was developed.After vacuum arc melting and copper mold suction casting,this HEA exhibits a unique phase separation microstructure,which consists of striped Cu-rich regions and Fe-rich region.Further magnification of the striped Cu-rich region reveals that it is composed of a Cu-rich dot-like phase and a Fe-rich region.The aging alloy is further strengthened by a L1_(2)-Ni_(3)(AlTi)nanoprecipitates,achieving excellent yield strength(1185 MPa)and uniform ductility(~8.8%).The differential distribution of the L1_(2) nanoprecipitate in the striped Cu-rich region and the external Fe-rich region increased the strength difference between these two regions,which increased the strain gradient and thus improved hetero-deformation induced(HDI)hardening.This work provides a new route to improve the HDI hardening of Fe-Cu alloys.
基金financially supported by the National Key Research and Development Program of China(No.2021YFB3803101)the National Natural Science Foundation of China(Nos.52022011,51974028,and 52090041)+1 种基金the Xiaomi Young Scholars ProgramChina National Postdoctoral Program for Innovative Talents(No.BX20230042)。
文摘Solid solution-strengthened copper alloys have the advantages of a simple composition and manufacturing process,high mechanical and electrical comprehensive performances,and low cost;thus,they are widely used in high-speed rail contact wires,electronic component connectors,and other devices.Overcoming the contradiction between low alloying and high performance is an important challenge in the development of solid solution-strengthened copper alloys.Taking the typical solid solution-strengthened alloy Cu-4Zn-1Sn as the research object,we proposed using the element In to replace Zn and Sn to achieve low alloying in this work.Two new alloys,Cu-1.5Zn-1Sn-0.4In and Cu-1.5Zn-0.9Sn-0.6In,were designed and prepared.The total weight percentage content of alloying elements decreased by 43%and 41%,respectively,while the product of ultimate tensile strength(UTS)and electrical conductivity(EC)of the annealed state increased by 14%and 15%.After cold rolling with a 90%reduction,the UTS of the two new alloys reached 576 and 627MPa,respectively,the EC was 44.9%IACS and 42.0%IACS,and the product of UTS and EC(UTS×EC)was 97%and 99%higher than that of the annealed state alloy.The dislocations proliferated greatly in cold-rolled alloys,and the strengthening effects of dislocations reached 332 and 356 MPa,respectively,which is the main reason for the considerable improvement in mechanical properties.
基金supported by Research Project of Henan Provincial Social Science Circles Federation(SKL-2023-1059)Higher Education Research Project of Henan Association of Higher Education(2021SXHLX175)Research Projects from Xinxiang Municipal Social Science Circles Federation(SKL-2023-126 and SKL-2023-136).
文摘Labor education is an essential component of college and university education that can help students to develop a strong work ethic,acquire practical skills,and better understand the value of work.Strengthening labor education for college and university students is an urgent need of the high-quality development of the society and the internal requirement of promoting the all-round development of individuals.This study analyzes the importance of strengthening labor education for college and university students in the new era and proposes four practical pathways which draw on labor courses and campus activities,social practices,scientific research projects,and internships.After implementing these pathways,a survey of 967 students showed that students’understanding and awareness of labor was deepened,their hands-on skills and interests in science and labor practices were improved,and they became more cordially respectful to the working class.Taken together,the exploration and practice of these pathways helps college and university students to recognize their abilities,strengths,and interests,and guides them to form good labor habits that permeate all aspects of their studies and lives.
文摘The aerospace and military sectors have widely used AA7075, a type of 7075 aluminum alloy, due to its exceptional mechanical performance. Selective laser melting (SLM) is a highly effective method for producing intricate metallic components, particularly in the case of aluminum alloys like Al-Si-Mg. Nevertheless, the production of high-strength AA7075 by SLM is challenging because of its susceptibility to heat cracking and elemental vaporization. In this study, AA7075 powders were mechanically mixed with SiC and TiC particles. Subsequently, this new type of AA7075 powder was effectively utilized in green laser printing to create solid components with fine-grain strengthening microstructures consisting of equiaxial grains. These as-printed parts exhibit a tensile strength of up to 350 MPa and a ductility exceeding 2.1%. Hardness also increases with the increasing content of mixed powder, highlighting the essential role of SiC and TiC in SLM for improved hardness and tensile strength performance. .
文摘Precipitation strengthening is a crucial microscopic mechanism for enhancing the strength of magnesium alloys. In order to elucidate the influence of precipitation on the microscopic deformation mechanisms and macroscopic mechanical response of magnesium alloys under cyclic loading conditions, we employed a crystal plasticity model to analyze the stress-strain curves, specific crystal plane diffraction intensities, and the temporal evolution of various microscopic deformation mechanisms and twinning volume fractions for an extruded magnesium alloy, AXM10304, containing coherent precipitates. The research findings indicate that precipitation does not fundamentally alter the microscopic mechanisms of this alloy. However, it hinders twinning during the compression stage, mildly promotes detwinning during the tension stage, and enhances tension secondary hardening by elevating the difficulty of activation of the prismatic slip.
基金Project(50571069) supported by NSFC and Project(05A061) education department of Hunan province,China
文摘The effects of large cold deformation after solution treatment on the precipitation characteristic and deformation strength of 2024 and 7A04 Al alloys were investigated.The tensile property tests indicate that the ageing response of the 2024 aluminum alloy is accelerated when treated by cold deformation after solution treatment,and the tensile strength is increased to about 140 MPa while the elongation still keeps above 8%.However,compared with the 2024 alloys,although the aging response of the cold deformed 7A04 aluminum alloy is accelerated,the tensile strength has not changed obviously and the elongation is even decreased drastically.The results of TEM observation show that the S’ phase inside the dislocation cells and at the boundaries of the dislocation cells of the 2024 aluminum alloy has a uniform distribution.But in 7A04 aluminum alloy the club-shaped η’ phase forms at the boundaries of dislocation cells even on dislocation lines,while there still exists small spheric G.P zone in the region with less dislocation.In addition the precipitates in 7A04 alloy with cold rolling present more obvious tendency of growth and coarsening than those without cold rolling.It is indicated that the coherent strain energy of the cylinder formed G.P zones with matrix in the 2024 alloy is smaller than that of the spherical G.P zone in 7A04 alloy,for which a different distribution of precipitates and different effect of strengthening are caused in artificial ageing after resolution treatment and large cold deformation.
基金Supported by Science Fund for Creative Research Groups of NSFC(51621064)National Natural Science Foundation of China(Grant No.51475074,11302043)the Fundamental Research Funds for the Central Universities(DUT15QY37)
文摘The integral impeller and blisk of an aero-engine are high performance parts with complex structure and made of difficult-to-cut materials. The blade surfaces of the integral impeller and blisk are functional surfaces for power transmission, and their surface integrity has signif- icant effects on the aerodynamic efficiency and service life of an aero-engine. Thus, it is indispensable to finish and strengthen the blades before use. This paper presents a comprehensive literature review of studies on finishing and strengthening technologies for the impeller and blisk of aero-engines. The review includes independent and inte- grated finishing and strengthening technologies and dis- cusses advanced rotational abrasive flow machining with back-pressure used for finishing the integral impeller and blisk. A brief assessment of future research problems and directions is also presented.
基金supported by National Natural Science Foundation of China (Grant No. 50875173)Shanghai Municipal Education Commission Key Foundation of China (Grant No. 09ZZ157)Shanghai Leading Academic Discipline Project of China (Grant No. J50503)
文摘There are two kinds of internationally recognized approaches in terms of lightweight design.One is based on fatigue accumulated damage theory to achieve better reliability by optimal structural design; another is to use high performance lightweight materials.The former method takes very few considerations on the structural strengthening effects caused by the massive small loads in service.In order to ensure safety,the design is usually conservative,but the strength potential of the component is not fully exerted.In the latter method,cost is the biggest obstacle to lightweight materials in automotive applications.For the purpose of light weighting design on a fuel cell vehicle,the new design method is applied on drive shafts.The method is based on the low amplitude load strengthening characteristics of the material,and allows the stress,corresponding to test load,to enter into the strengthened range of the material.Under this condition,the light weighting design should assure that the reliability of the shaft is not impaired,even maximizes the strength potential of machine part in order to achieve the weight reduction and eventually to reduce the cost.At last,the feasibility of the design is verified by means of strength analysis and modal analysis based on the CAD model of light weighted shaft.The design applies to the load case of half shaft in independent axle,also provides technological reference for the structural lightweight design of vehicles and other machineries.
基金supported by the Startup Foundationfor Doctor Scientific Research in Henan University of Sci-ence and Technology (No. 20061009) the Special Fundfor Important Forepart Research in Henan University ofScience and Technology (No. 2008ZD003)the Na-tional Natural Science Foundation of China under grantNo. 50771042.
文摘It is known that the strength of alloys can be successfully improved by rapid solidification. The paper presents a process where Cu-Cr-Sn-Zn lead frame alloy is produced by rapid solidification and aging. The microcrystalline structure of rapidly solidified Cu-Cr-Sn-Zn alloy is smaller grain structure examined by optical metallography. The effects of aging processes on the microstructure and properties of the lead frame alloy were investigated. Aged at 500℃ for 15 min the fine coherent precipitates Cr distribute in Cu matrix observed by transmission electron microscopy and the properties of hardness and electrical conductivity properties can reach 178HV and 61%IACS, respectively.
文摘The microstructure of dislocation in two kinds of ahiminum-lithium alloys 2090 and 2090 + Ce was observed by means of TEM technology. The contributions of δ' and T1 precipitates to strength were separately calculated by using the results of quantitative metallography and analysis of micro-deformation behavior; the co-strengthening effect of δ' and T1 precipitates was studied. The results show that the adding relationship of co-strengthening of δ' and T1 is in accordance with q = 1.4 form at the near peak-aged condition, i.e., △τ^1.4δ = △τ^1.4δ+ △τ^1.4T1, but the adding relationship is approximately a linear relation (q = 1) at the under-aged condition and becomes the parabola form when over-aged (q = 2). The adding relationship of co-strengthening contribution of δ' and T1 is obviously dependent on aging time.
基金Supported by National High Technology Research and Development Program of China (Grant No.2011AA11A265)National Natural Science Foundation of China (Grant Nos.50875173,51105241)Shanghai Municipal Natural Science Foundation of China (Grant No.11ZR1414700)
文摘Lightweight design requires an accurate life prediction for structures and components under service loading histories. However, predicted life with the existing methods seems too conservative in some cases, leading to a heavy structure. Because these methods are established on the basis that load cycles would only cause fatigue damage, ignore the strengthening effect of loads. Based on Palmgren-Miner Rule (PMR), this paper introduces a new method for fatigue life prediction under service loadings by taking into account the strengthening effect of loads below the fatigue limit. In this method, the service loadings are classified into three categories: damaging load, strengthening load and none-effect load, and the process for fatigue life prediction is divided into two stages: stage I and stage II, according to the best strengthening number of cycles. During stage I, fatigue damage is calculated considering both the strengthening and damaging effect of load cycles. While during stage II, only the damaging effect is considered. To validate this method, fatigue lives of automobile half shaft and torsion beam rear axle are calculated based on the new method and traditional methods, such as PMR and Modified Miner Rule (MMR), and fatigue tests of the two components are conducted under service loading histories. The tests results show that the percentage errors of the predicted life with the new method to mean life of tests for the two components are –3.78% and –1.76% separately, much lesser than that with PMR and MMR. By considering the strengthening effect of loads below the fatigue limit, the new method can significantly improve the accuracy for fatigue life prediction. Thus lightweight design can be fully realized in the design stage.
基金supported by the Major State Basic Research Development Program of China (No.2007CB613706)the Project of Key Disciplines Development "Resources, Environment and Recycling Economy" Interdisciplinary under the Jurisdiction of Beijing Municipality (No.0330005412901)the Project Sponsored by the Scientific Research Foundation for Doctoral Teachers, Beijing University of Technology (No.X0104001200905)
文摘The microstructure and strengthening mechanisms of as-cast Mg-6Al-6Nd alloy were studied. The results show that the addition of 6 wt.% Nd into Mg-6Al alloy leads to the precipitation of Al11Nd3 and Al2Nd phases and decrease in the content of Al solid soluted in Mg-Al matrix. The volume fractions of Al11Nd3 and Al2Nd phases are 3.64% and 0.34%, respectively. Compared with Mg-6Al alloy, the ultimate strength, yielding strength, and elongation of Mg-6Al-6Nd alloy at room temperature and 175℃ are enhanced in some degrees. The strengthening mechanisms of Mg-6Al-6Nd alloy are mainly composed of solid solution strengthening of Al solid soluted in Mg-Al matrix and grain refmement strengthening, dispersion strengthening, and composite strengthening brought by the precipitation of Al11Nd3 phase. The composite strengthening includes the load transfer from the matrix to Al11Nd3 phase and the enhancement of dislocation density due to the geometrical mismatch and thermal mismatch between the matrix and Al11Nd3 phase.