Nanometer micro-porous Nix Zn (1-x )Fe2O4power was synthesized by hydrotherm al method.This is first time to apply template to the synthesis.The structure,characteristics and cry stal appearance are studied further by...Nanometer micro-porous Nix Zn (1-x )Fe2O4power was synthesized by hydrotherm al method.This is first time to apply template to the synthesis.The structure,characteristics and cry stal appearance are studied further by XRD,DSC,TEM,etc.It is found that nanome ter micro-porous crystal is well-crystallized,well-degree of dispers ion and smaller than 100nm in diameter.More over,tri-ethylamine can be used to b e a ideal template in this synthesis,and the first time it is reported in our co untry.The synthesis mechanism is also preliminary discussed in this pap er.展开更多
(ZrO2)1-x（Yb2O3）x （x=0.07, 0.09, 0.11） nanocrystallites were hydrothermally prepared in basic media by using co-precipitated Zr（OH）4 and Yb（OH）3 as precursor. The nanocrystallites have small particle sizes of ...(ZrO2)1-x（Yb2O3）x （x=0.07, 0.09, 0.11） nanocrystallites were hydrothermally prepared in basic media by using co-precipitated Zr（OH）4 and Yb（OH）3 as precursor. The nanocrystallites have small particle sizes of 5.87.5 nm, narrow size distribution, less agglomeration and high sinterability. The oxide-ionic conduction properties of the prepared ceramics were investigated by means of AC impedance spectroscope, oxygen concentration cell at 6001 000 ℃. The results show that the ceramic with x=0.09 is superior to the ceramics with x=0.07 and 0.11 in oxide-ionic conduction.展开更多
文摘Nanometer micro-porous Nix Zn (1-x )Fe2O4power was synthesized by hydrotherm al method.This is first time to apply template to the synthesis.The structure,characteristics and cry stal appearance are studied further by XRD,DSC,TEM,etc.It is found that nanome ter micro-porous crystal is well-crystallized,well-degree of dispers ion and smaller than 100nm in diameter.More over,tri-ethylamine can be used to b e a ideal template in this synthesis,and the first time it is reported in our co untry.The synthesis mechanism is also preliminary discussed in this pap er.
文摘(ZrO2)1-x（Yb2O3）x （x=0.07, 0.09, 0.11） nanocrystallites were hydrothermally prepared in basic media by using co-precipitated Zr（OH）4 and Yb（OH）3 as precursor. The nanocrystallites have small particle sizes of 5.87.5 nm, narrow size distribution, less agglomeration and high sinterability. The oxide-ionic conduction properties of the prepared ceramics were investigated by means of AC impedance spectroscope, oxygen concentration cell at 6001 000 ℃. The results show that the ceramic with x=0.09 is superior to the ceramics with x=0.07 and 0.11 in oxide-ionic conduction.