Effects of B addition on glass forming ability and thermal behavior of FePC-based bulk metallic glasses

The FePC-based bulk metallic glasses（BMGs）have been demonstrated to possess high plasticity and good soft magnetic properties.However,the relatively poor glass forming ability（GFA）and thermal stabilities limited their application in industries.The effects of microalloying with B in FePC-based BMGs on the GFA and thermal behaviors were systematically investigated.It was found that a small amount of B addition can dramatically enhance the GFA of FePC-based BMGs,which in turn leads to the critical maximum diameter up to 2 mm for full glass formation even using low cost raw materials.The underlying mechanism of the enhancement of GFA from the competing crystalline phase with amorphous phase,the average thermal expansion coefficient and dynamic viscosity were discussed in detail.

Equilibrium Crystallization Temperature of Syndiotactic Polystyrene γ Form

The crystallization behavior of syndiotactic polystyrene（s PS） γ form undergoing annealing at various temperatures was investigated using the thermodynamic phase diagram based on Strobl＇s crystallization theory. On the basis of the differential scanning calorimetric results, it was observed that γ form melt-recrystallization occurred at a higher temperature with the increasing lamellar thickness, which resulted from the pre-annealing at the elevating temperature after acetone induced crystallization. Further temperature dependent small-angle X-ray scattering（SAXS） measurement revealed the evolution of the γ form lamellae upon heating until phase transition, involving three different regimes： lamellae stable region（25-90 °C）, melt-recrystallization region（90-185 °C） and pre-phase transition region（185-195 °C）. As a result, recrystallization line, equilibrium recrystallization line and melting line were developed for the s PS γ form crystallization process. Since the melt of γ form involved a γ-to-α/β form phase transition, the melting line was also denoted as the phase transition line in this special case. Therefore, the equilibrium crystallization temperature and melting（phase transition） temperatures were determined at around 390 and 220 °C on the basis of the thermodynamic phase diagram of the s PS γ form.