Structural integrity procedures were used to demonstrate the fitness for the purpose of engineering components transmitting loads. The prediction of the fracture strength of titanium alloys containing sharp notches th...Structural integrity procedures were used to demonstrate the fitness for the purpose of engineering components transmitting loads. The prediction of the fracture strength of titanium alloys containing sharp notches through the damage model depends on the un-notched strength and the critical length of the damage zone ahead of the notch. In general, the critical length of the damage zone depends on the material, specimen, and size of the sharp notch. Modifications were made in one of the stress fracture criteria known as the average stress criterion for accurate prediction of notched tensile strength of titanium alloy specimen containing sharp notches. To examine the adequacy of these modifications, fracture data of center-cracked titanium alloys with various thicknesses are considered. The notched （fracture） strength estimates are found to be close to the test results. The modified average stress criterion is very simple to predict the notched tensile strength.展开更多
一般认为绝热剪切现象在宏观上表现为材料动态本构失稳,即热软化大于应变硬化.本文采用帽型受迫剪切试样研究TA2钛合金的动态力学特性和本构失稳过程.首先对剪切区加载应力状态进行理论和数值分析,通过合理设计帽型试样,剪切区变形可近...一般认为绝热剪切现象在宏观上表现为材料动态本构失稳,即热软化大于应变硬化.本文采用帽型受迫剪切试样研究TA2钛合金的动态力学特性和本构失稳过程.首先对剪切区加载应力状态进行理论和数值分析,通过合理设计帽型试样,剪切区变形可近似按剪切状态处理;结合二维数字图像相关法(two-dimensional digital image correlation,DIC-2D)直接测试试样剪切区应变演化,给出帽型受迫剪切实验的等效应力-应变响应曲线.进一步,利用Hopkinson压杆对TA2钛合金开展动态压缩及帽型剪切对比试验研究,比较压缩、剪切试验得到的等效应力-应变曲线,采用"冻结"试样方法分析试样中绝热剪切局域化演化过程,探讨不同加载状态下TA2钛合金的绝热剪切破坏现象及其动态力学响应特性.实验结果表明,在塑性变形初始阶段,动态压缩及剪切加载下的等效应力-应变曲线符合较好,但随塑性损伤发展及绝热剪切带形成,两者出现分离,表明损伤及绝热剪切演化过程与应力状态相关.剪切试样实验得到的本构"软化"特性能够反映绝热剪切带起始、破坏演化过程的力学响应特性,而在动态压缩实验中,即使试样中已出现双锥形的绝热剪切带及局部裂纹分布,其表观等效应力-应变曲线并不出现软化特征,动态压缩实验无法得到关于绝热剪切起始、发展以及破坏的本构软化响应特性.展开更多
文摘Structural integrity procedures were used to demonstrate the fitness for the purpose of engineering components transmitting loads. The prediction of the fracture strength of titanium alloys containing sharp notches through the damage model depends on the un-notched strength and the critical length of the damage zone ahead of the notch. In general, the critical length of the damage zone depends on the material, specimen, and size of the sharp notch. Modifications were made in one of the stress fracture criteria known as the average stress criterion for accurate prediction of notched tensile strength of titanium alloy specimen containing sharp notches. To examine the adequacy of these modifications, fracture data of center-cracked titanium alloys with various thicknesses are considered. The notched （fracture） strength estimates are found to be close to the test results. The modified average stress criterion is very simple to predict the notched tensile strength.
文摘一般认为绝热剪切现象在宏观上表现为材料动态本构失稳,即热软化大于应变硬化.本文采用帽型受迫剪切试样研究TA2钛合金的动态力学特性和本构失稳过程.首先对剪切区加载应力状态进行理论和数值分析,通过合理设计帽型试样,剪切区变形可近似按剪切状态处理;结合二维数字图像相关法(two-dimensional digital image correlation,DIC-2D)直接测试试样剪切区应变演化,给出帽型受迫剪切实验的等效应力-应变响应曲线.进一步,利用Hopkinson压杆对TA2钛合金开展动态压缩及帽型剪切对比试验研究,比较压缩、剪切试验得到的等效应力-应变曲线,采用"冻结"试样方法分析试样中绝热剪切局域化演化过程,探讨不同加载状态下TA2钛合金的绝热剪切破坏现象及其动态力学响应特性.实验结果表明,在塑性变形初始阶段,动态压缩及剪切加载下的等效应力-应变曲线符合较好,但随塑性损伤发展及绝热剪切带形成,两者出现分离,表明损伤及绝热剪切演化过程与应力状态相关.剪切试样实验得到的本构"软化"特性能够反映绝热剪切带起始、破坏演化过程的力学响应特性,而在动态压缩实验中,即使试样中已出现双锥形的绝热剪切带及局部裂纹分布,其表观等效应力-应变曲线并不出现软化特征,动态压缩实验无法得到关于绝热剪切起始、发展以及破坏的本构软化响应特性.
基金supported by High-tech 863 Program under the project of “Development of a 4 500 m deep manned submersible” (Project No. 2009AA093303)Fourth Term of “333 Engineering” Program of Jiangsu Province under the project of “Fatigue and fracture performance of domestically produced high strength titanium alloys for the 4 500 m deep manned pressure hull” (Project No.BRA2011116)