The reformation of (Bi,Pb)-2223 from the liquid or melt is very important for a melting process of (Bi,Pb)-2223 tape. By combination of quenching experiment with X-ray diffraction (XRD) analysis, the effect of cooling...The reformation of (Bi,Pb)-2223 from the liquid or melt is very important for a melting process of (Bi,Pb)-2223 tape. By combination of quenching experiment with X-ray diffraction (XRD) analysis, the effect of cooling rate on the evolution of three superconducting phases in the (Bi,Pb)-2223 core of Ag-sheathed tape was investigated. The results show that (Bi,Pb)-2223 reformation from the melt seems to experience different routes during slowly cooling at different rates. One is that (Bi,Pb)-2223 phase reformed directly from the melt, and no Bi-2212 participate in this process. The other is that (Bi,Pb)-2223 is converted from the intermediate product, Bi-2212, which formed from the melt during the first cooling stage. Due to the inherent sluggish formation kinetics of (Bi,Pb)-2223 from Bi-2212, only partial (Bi,Pb)-2223 can finally be reformed with the second route.展开更多
To reduce the production cost of Bi-2223 superconducting tapes, Bi-2223/Ag/Ni tapes were fabricated by the powder-in-tube process. The effect of heat treatment on the microstructure and critical current of the Bi-2223...To reduce the production cost of Bi-2223 superconducting tapes, Bi-2223/Ag/Ni tapes were fabricated by the powder-in-tube process. The effect of heat treatment on the microstructure and critical current of the Bi-2223/Ag/Ni tapes were studied. The phase compositions of the samples were characterized using XRD. The microstructure was observed using SEM. Experimental results indicate that higher temperature is more conducive to the formation of Bi-2223 phase at an atmosphere of 8.5% O 2 . After the two-step heat treatment, the critical current of samples is about 67.5 A.展开更多
The silver-sheathed Bi-Pb-Sr-Ca-Cu-O(Bi-2223) superconducting tapes have been fabricated by the powder-in-tube method. In the process,we investigated the effects of the particle size, rolling and pressing on Jc and fo...The silver-sheathed Bi-Pb-Sr-Ca-Cu-O(Bi-2223) superconducting tapes have been fabricated by the powder-in-tube method. In the process,we investigated the effects of the particle size, rolling and pressing on Jc and found that the Jc value can be a ffected greatly by the three factors.展开更多
The Bi-2223/Ag tapes were prepared with spray-died powders, which are of different particle sizes and phase assemblages by varying the annealing time in pure oxygen. Longer time annealing degraded the reactivity of pr...The Bi-2223/Ag tapes were prepared with spray-died powders, which are of different particle sizes and phase assemblages by varying the annealing time in pure oxygen. Longer time annealing degraded the reactivity of precursor powder, which in turn resulted in an incomplete conversion from precursors to Bi-2223, porosity core and misaligned grains in fully processed tapes. The best Jc in short pressed samples varied from 29.7 to 47kA/cm2 for the tapes made from different powders.展开更多
Diffusion bonding of multifilamentary Ag/Bi-2223 （ Bi2 Sr2 Ca2 Cu3Ox ） superconducting tapes has been performed successfally. Three types of joints, namely, with sih,er interlayer （type Ⅰ）, bonded directly （type...Diffusion bonding of multifilamentary Ag/Bi-2223 （ Bi2 Sr2 Ca2 Cu3Ox ） superconducting tapes has been performed successfally. Three types of joints, namely, with sih,er interlayer （type Ⅰ）, bonded directly （type Ⅱ）, with Bi-2212 （BizSr2Ca1 Cu2Ox ） powder interlayer or with Bi-2223 powder interlayer （type Ⅲ） were researched, respectively. The critical currents（ Ic ） of these joints were measured ond microstructures of the joints were evaluated by scanning electron microscope （SEM）. The result shows that type Ⅰ is non-superconducting joint with very low resistance, and type Ⅱ joint and type Ⅲ （with Bi-2212 or Bi-2223 ） joints are both of superconducting property. By comparing, type Ⅱ joint possesses most exceUent superconductivity, type Ⅲ joint with Bi-2223 powder interlayer takes the second place, and type ,任家烈 joint with Bi-2212 powder interlayer is least.展开更多
Ag-sheathed (Bi,Pb)(2)SoCa(2)Cu(3)O(x) tapes were prepared by the powder-in-tube method. The influences of rolling parameters on superconducting characteristics of Bi(2223)/Ag tapes were analyzed qualitatively with a ...Ag-sheathed (Bi,Pb)(2)SoCa(2)Cu(3)O(x) tapes were prepared by the powder-in-tube method. The influences of rolling parameters on superconducting characteristics of Bi(2223)/Ag tapes were analyzed qualitatively with a statistical method. The results demonstrate that roll diameter and reduction per pass significantly influence the properties of Bi(2223)/Ag superconducting tapes while roll speed does less and working friction the least. An optimized rolling process was therefore achieved according to the above results.展开更多
文摘The reformation of (Bi,Pb)-2223 from the liquid or melt is very important for a melting process of (Bi,Pb)-2223 tape. By combination of quenching experiment with X-ray diffraction (XRD) analysis, the effect of cooling rate on the evolution of three superconducting phases in the (Bi,Pb)-2223 core of Ag-sheathed tape was investigated. The results show that (Bi,Pb)-2223 reformation from the melt seems to experience different routes during slowly cooling at different rates. One is that (Bi,Pb)-2223 phase reformed directly from the melt, and no Bi-2212 participate in this process. The other is that (Bi,Pb)-2223 is converted from the intermediate product, Bi-2212, which formed from the melt during the first cooling stage. Due to the inherent sluggish formation kinetics of (Bi,Pb)-2223 from Bi-2212, only partial (Bi,Pb)-2223 can finally be reformed with the second route.
基金financially supported by the National High Technology Research and Development Program(863program)(No.2009AA03Z202)the Fundamental Research Funds for the Central Universities(No.N100423006and No.N110823001)
文摘To reduce the production cost of Bi-2223 superconducting tapes, Bi-2223/Ag/Ni tapes were fabricated by the powder-in-tube process. The effect of heat treatment on the microstructure and critical current of the Bi-2223/Ag/Ni tapes were studied. The phase compositions of the samples were characterized using XRD. The microstructure was observed using SEM. Experimental results indicate that higher temperature is more conducive to the formation of Bi-2223 phase at an atmosphere of 8.5% O 2 . After the two-step heat treatment, the critical current of samples is about 67.5 A.
文摘The silver-sheathed Bi-Pb-Sr-Ca-Cu-O(Bi-2223) superconducting tapes have been fabricated by the powder-in-tube method. In the process,we investigated the effects of the particle size, rolling and pressing on Jc and found that the Jc value can be a ffected greatly by the three factors.
文摘The Bi-2223/Ag tapes were prepared with spray-died powders, which are of different particle sizes and phase assemblages by varying the annealing time in pure oxygen. Longer time annealing degraded the reactivity of precursor powder, which in turn resulted in an incomplete conversion from precursors to Bi-2223, porosity core and misaligned grains in fully processed tapes. The best Jc in short pressed samples varied from 29.7 to 47kA/cm2 for the tapes made from different powders.
基金Acknowledgement This research is supported by the National Natural Science Foundation of China （grant No. 50575114 and No. 50635050） and by Beijing Natural Science Foundation （grant No. 3052010） and by China Postdoctoral Science Foundation （ grant No. 20080430360）.
文摘Diffusion bonding of multifilamentary Ag/Bi-2223 （ Bi2 Sr2 Ca2 Cu3Ox ） superconducting tapes has been performed successfally. Three types of joints, namely, with sih,er interlayer （type Ⅰ）, bonded directly （type Ⅱ）, with Bi-2212 （BizSr2Ca1 Cu2Ox ） powder interlayer or with Bi-2223 powder interlayer （type Ⅲ） were researched, respectively. The critical currents（ Ic ） of these joints were measured ond microstructures of the joints were evaluated by scanning electron microscope （SEM）. The result shows that type Ⅰ is non-superconducting joint with very low resistance, and type Ⅱ joint and type Ⅲ （with Bi-2212 or Bi-2223 ） joints are both of superconducting property. By comparing, type Ⅱ joint possesses most exceUent superconductivity, type Ⅲ joint with Bi-2223 powder interlayer takes the second place, and type ,任家烈 joint with Bi-2212 powder interlayer is least.
文摘Ag-sheathed (Bi,Pb)(2)SoCa(2)Cu(3)O(x) tapes were prepared by the powder-in-tube method. The influences of rolling parameters on superconducting characteristics of Bi(2223)/Ag tapes were analyzed qualitatively with a statistical method. The results demonstrate that roll diameter and reduction per pass significantly influence the properties of Bi(2223)/Ag superconducting tapes while roll speed does less and working friction the least. An optimized rolling process was therefore achieved according to the above results.
基金National High Technology Research and Development Program(863 program)(2009AA03Z202)Fundamental Research Funds for the Central Universities(N100423006,N110823001,N100123003)