A new group of lead-free piezoelectric ceramics,（Bi0.5 Na0.5）1-x（BaaSrb）xTiO3（abbreviated as BNBST[100x-100a/100b],0〈x〈1,a＋b=1）,was synthesized.The ceramics were prepared by conventional ceramic sintering tec...A new group of lead-free piezoelectric ceramics,（Bi0.5 Na0.5）1-x（BaaSrb）xTiO3（abbreviated as BNBST[100x-100a/100b],0〈x〈1,a＋b=1）,was synthesized.The ceramics were prepared by conventional ceramic sintering technique,and the ceramics with density of 95% of the theoretical one can be sintered without the atmosphere control during the sintering process.The results of the X-ray diffraction（XRD） data show that the ceramics possess a single perovskite phase.The measurements of dielectric and piezoelectric properties reveal that the ceramics provide relatively high piezoelectric charge constant d33 and high planar electromechanical coupling factor kp.For the BNBST6-95/5 ceramics,d33 is equal to 170pC/N,and kp is equal to 32.0%.The fabrication technique for these ceramics is conventional and stable.展开更多
The microstructures and electrical properties of Bi0.5（Na1-x-yKxLiy）0.5TiO3 lead-free piezoelectric ceramics were studied.These ceramics were prepared by conventional ceramic technique.XRD analysis reveals that the ...The microstructures and electrical properties of Bi0.5（Na1-x-yKxLiy）0.5TiO3 lead-free piezoelectric ceramics were studied.These ceramics were prepared by conventional ceramic technique.XRD analysis reveals that the ceramics possess almost pure perovskite phase when y≤0.2.The SEM results show that,with more amounts of Li＋,the crystalline grain growing speed is accelerated,and the sintering temperature can effectively be decreased.The measurements of piezoelectric properties indicate that the ceramics with relatively low amount of Li＋ and high amount of K＋ have comparatively large piezoelectricity.The dielectric measurements show that the ceramics have properties like relaxor ferroelectrics and diffuse phase transition（DPT） at Td and Tc,respectively.The results of ferroelectric measurements reveal the system has relatively higher remanent polarization Pr（27.6 μC/cm2） and lower coercive field Ec（37.5 kV/cm）.展开更多
文摘A new group of lead-free piezoelectric ceramics,（Bi0.5 Na0.5）1-x（BaaSrb）xTiO3（abbreviated as BNBST[100x-100a/100b],0〈x〈1,a＋b=1）,was synthesized.The ceramics were prepared by conventional ceramic sintering technique,and the ceramics with density of 95% of the theoretical one can be sintered without the atmosphere control during the sintering process.The results of the X-ray diffraction（XRD） data show that the ceramics possess a single perovskite phase.The measurements of dielectric and piezoelectric properties reveal that the ceramics provide relatively high piezoelectric charge constant d33 and high planar electromechanical coupling factor kp.For the BNBST6-95/5 ceramics,d33 is equal to 170pC/N,and kp is equal to 32.0%.The fabrication technique for these ceramics is conventional and stable.
基金Supported by Program for New Century Excellent Talents in University(No.NCET-07-0329)
文摘The microstructures and electrical properties of Bi0.5（Na1-x-yKxLiy）0.5TiO3 lead-free piezoelectric ceramics were studied.These ceramics were prepared by conventional ceramic technique.XRD analysis reveals that the ceramics possess almost pure perovskite phase when y≤0.2.The SEM results show that,with more amounts of Li＋,the crystalline grain growing speed is accelerated,and the sintering temperature can effectively be decreased.The measurements of piezoelectric properties indicate that the ceramics with relatively low amount of Li＋ and high amount of K＋ have comparatively large piezoelectricity.The dielectric measurements show that the ceramics have properties like relaxor ferroelectrics and diffuse phase transition（DPT） at Td and Tc,respectively.The results of ferroelectric measurements reveal the system has relatively higher remanent polarization Pr（27.6 μC/cm2） and lower coercive field Ec（37.5 kV/cm）.