BiB3O6 (BIBO) single crystals with sizes of 44 mm × 24 mm × 10 mm and weight of 24.7 g have been successfully grown by the top-seeded method. In this note, the preparation of seed, the growth of crystal and ...BiB3O6 (BIBO) single crystals with sizes of 44 mm × 24 mm × 10 mm and weight of 24.7 g have been successfully grown by the top-seeded method. In this note, the preparation of seed, the growth of crystal and some problems encountered are reported. The lattice parameters of BIBO are a =7.1203(7)A, b = 4.9948(7)A, c = 6.5077(7)A, β= 105.586(8) ", V=222.93(5)A3, which were determined by BRUKER-P4 four-circle diffractometer. BIBO is biaxial crystal and the relative orientation of (X, Y, Z) with regard to (a, b, c) is: X|| b, (Y, c) =47.2°, (Z, a) = 31.6°, determined by the X-ray analysis combined with polarized microscopy. The second-harmonic-generation (SHG) conversion efficiency of the sample for 1.064 μm light is up to 67.7%. We have also obtained the third harmonic generation (THG) of 1.064 μm, namely, 1.064 μm + 0.532 μn →0.355 μm. BIBO crystal is free of moisture and hygroscopy.展开更多
A design of laser-diode array (LDA) end-pumped Nd:YVO4 laser that generates simultaneously wavelengths of 1064 nm and 1342 nm is presented, and by using type-I critical phase matching (CPM) of BiB3O6, 593.5 nm continu...A design of laser-diode array (LDA) end-pumped Nd:YVO4 laser that generates simultaneously wavelengths of 1064 nm and 1342 nm is presented, and by using type-I critical phase matching (CPM) of BiB3O6, 593.5 nm continuous-wave (CW) laser is obtained with intracavity sum-frequency mixing. The maximum laser output power can reach 3.63 W with the pump power of 27.5 W. The optical-to-optical conversion efficiency is up to 13.2%, which is the highest value at 593.5 nm by the intracavity sum-frequency Nd:YVO4 laser according to the reported data.展开更多
Transparent Nd : BiB3O6 crystal has been grown by top-seeded method. The refraction indices of the crystal were measured and the parameters of chromatic dispersion were fitted. The room temperature absorption spectra ...Transparent Nd : BiB3O6 crystal has been grown by top-seeded method. The refraction indices of the crystal were measured and the parameters of chromatic dispersion were fitted. The room temperature absorption spectra of the crystal have been measured and compared with that of 0.2 mol/L NdCI3 solution. According to Judd-Ofelt (JO) theory, the spectral strength parameters Ω2 = 0.1776×10-20 cm2, Ω4 = 0.1282×10-20 cm2 and Ω6 = 0.1357×10-20 cm2 of Nd3+ ion were fitted. The radiative transition probabilities AJ,(?), oscillator strengths fJ,(?), radiative lifetime T and the branching ratio β(?) have all been calculated. Based on these parameters, the properties and application perspective are discussed.展开更多
基金This work was supported by the State Key Program of China.
文摘BiB3O6 (BIBO) single crystals with sizes of 44 mm × 24 mm × 10 mm and weight of 24.7 g have been successfully grown by the top-seeded method. In this note, the preparation of seed, the growth of crystal and some problems encountered are reported. The lattice parameters of BIBO are a =7.1203(7)A, b = 4.9948(7)A, c = 6.5077(7)A, β= 105.586(8) ", V=222.93(5)A3, which were determined by BRUKER-P4 four-circle diffractometer. BIBO is biaxial crystal and the relative orientation of (X, Y, Z) with regard to (a, b, c) is: X|| b, (Y, c) =47.2°, (Z, a) = 31.6°, determined by the X-ray analysis combined with polarized microscopy. The second-harmonic-generation (SHG) conversion efficiency of the sample for 1.064 μm light is up to 67.7%. We have also obtained the third harmonic generation (THG) of 1.064 μm, namely, 1.064 μm + 0.532 μn →0.355 μm. BIBO crystal is free of moisture and hygroscopy.
基金supported by the Foundamental Research Program of the Commission of Science Technology and Industry for National Defense of China (No.A3620060122)
文摘A design of laser-diode array (LDA) end-pumped Nd:YVO4 laser that generates simultaneously wavelengths of 1064 nm and 1342 nm is presented, and by using type-I critical phase matching (CPM) of BiB3O6, 593.5 nm continuous-wave (CW) laser is obtained with intracavity sum-frequency mixing. The maximum laser output power can reach 3.63 W with the pump power of 27.5 W. The optical-to-optical conversion efficiency is up to 13.2%, which is the highest value at 593.5 nm by the intracavity sum-frequency Nd:YVO4 laser according to the reported data.
基金the National Natural Science Foundation of China (Grant No. 59823003).
文摘Transparent Nd : BiB3O6 crystal has been grown by top-seeded method. The refraction indices of the crystal were measured and the parameters of chromatic dispersion were fitted. The room temperature absorption spectra of the crystal have been measured and compared with that of 0.2 mol/L NdCI3 solution. According to Judd-Ofelt (JO) theory, the spectral strength parameters Ω2 = 0.1776×10-20 cm2, Ω4 = 0.1282×10-20 cm2 and Ω6 = 0.1357×10-20 cm2 of Nd3+ ion were fitted. The radiative transition probabilities AJ,(?), oscillator strengths fJ,(?), radiative lifetime T and the branching ratio β(?) have all been calculated. Based on these parameters, the properties and application perspective are discussed.