Sol-gel process was adopted to prepare BiFeO3 films.BiFeO3 films were deposited on LaNiO3 coated Si（100） substrates annealed at 500 and 550 ℃,respectively.The X-ray diffraction results reveal that BiFeO3 film has a...Sol-gel process was adopted to prepare BiFeO3 films.BiFeO3 films were deposited on LaNiO3 coated Si（100） substrates annealed at 500 and 550 ℃,respectively.The X-ray diffraction results reveal that BiFeO3 film has a rhombohedrally distorted perovskite structure with space group R3c.The film annealed at 500 ℃ has larger remnant polarization（Pr） of 35.3 μC/cm2.For the film annealed at 550 ℃,smaller remnant polarization of Pr=4.8 μC/cm^2 is observed for its low breakdown electric field.Lower leakage conduction is observed in the film annealed at 500 ℃ at low applied field.展开更多
基金Funded by the National Natural Science Foundation of China(No.10874075)the Key Program of Hubei Province Education Committee(No. D20082203)
文摘Sol-gel process was adopted to prepare BiFeO3 films.BiFeO3 films were deposited on LaNiO3 coated Si（100） substrates annealed at 500 and 550 ℃,respectively.The X-ray diffraction results reveal that BiFeO3 film has a rhombohedrally distorted perovskite structure with space group R3c.The film annealed at 500 ℃ has larger remnant polarization（Pr） of 35.3 μC/cm2.For the film annealed at 550 ℃,smaller remnant polarization of Pr=4.8 μC/cm^2 is observed for its low breakdown electric field.Lower leakage conduction is observed in the film annealed at 500 ℃ at low applied field.