Influences of POSS-E-GO Content on Mechanical Properties of Bio-based Epoxy/DOPO-POSS Nanocomposites

The bio-based epoxy nanocomposite(GAER/DOPO-POSS)was prepared from gallic epoxy resin(GAER)and polyhedral oligomeric silsesquioxane(which containing 9,10-dihydrogen-9-oxo-10-phosphorus-phenanthrene-10-oxide groups,called DOPO-POSS).The polyhedral oligomeric silsesquioxane containing epoxy groups(E-POSS)was grafted onto aminated graphene oxide(E-GO),then the novel POSS-E-GO was obtained.The POSS-E-GO was used as modifier for GAER/DOPO-POSS nanocomposite.The influences of POSS-E-GO content on mechanical properties,dynamic mechanical properties and thermal stability of GAER/DOPO-POSS nanocomposites were determined.The experimental results show that POSS-E-GO can significantly improve the toughness of the GAER/DOPO-POSS nanocomposite.When 0.5wt% POSS-E-GO was added in GAER/DOPO-POSS nanocomposite,the impact strength of the nanocomposite was 4.74 kJ/m^(2) higher than that in the absence of POSS-E-GO,meantime the initial thermal degradation temperature was 277℃.

A sustainable process to 100%bio-based nylons integrated chemical and biological conversion of lignocellulose

Considerable progress has been made in recent years to the development of sustainable polymers from bio-based feedstocks.In this study,100%bio-based nylons were prepared via an integrated chemical and biological process from lignocellulose.These novel nylons were obtained by the melt polymerization of 3-propyladipic acid derived from lignin and 1,5-pentenediamine/1,4-butanediamine derived from carbohydrate sugar.Central to the concept is a three-step noble metal free catalytic chemical funnelling sequence(Raney Ni mediated reductive catalytic fractionation-reductive funnelling-oxidative funnelling),which allowed for obtaining a single component 3-propyladipic acid from lignin with high efficiency.The structural and thermodynamic properties of the obtained nylons have been systematically investigated,and thus obtained transparent bio-based nylons exhibited higher Mw(>32,000)and excellent thermal stability(Td5%>265℃).Considering their moderate Tg and good melt strength,these transparent bio-based nylons could serve as promising functional additives or temperature-responsive materials.

Recyclable bio-based epoxy resin thermoset polymer from wood for circular economy

Due to their extraordinary durability and thermal stability,Epoxy Resin Thermosets(ERTs)are essential in various industries.However,their poor recyclability leads to unacceptable environmental pollution.In this study,Wu et al.successfully synthesized a completely bio-based ERT using lignocellulose-derived building blocks which exhibit outstanding thermal and mechanical properties.Remarkably,these bio-materials degrade via methanolysis without the need of any catalyst,presenting a smart and cost-effective recycling strategy.Furthermore,this approach could be employed for fabricating reusable composites comprising glass fiber and plant fiber,thereby expanding its applications in sustainable transportation,coatings,paints or biomedical devices.

Bio-based rejuvenators in asphalt pavements:A comprehensive review and analytical study

The pressing demand for sustainable advancements in road infrastructure has catalyzed extensive research into environmentally conscious alternatives for the maintenance and restoration of asphalt concrete pavements.This paper offers a comprehensive review and analysis of bio-based rejuvenators as a promising avenue for enhancing the longevity and sustainability of asphalt.Through a multifaceted exploration,it delves into various aspects of this innovative approach.Providing a thorough overview of bio-based rejuvenators,the study highlights their renewable and environmentally friendly characteristics.It conducts an in-depth examination of a wide spectrum of bio-derived materials,including vegetable oils,waste-derived bio-products,and biopolymers,through a comprehensive survey.The paper evaluates how bio-based rejuvenators enhance aged asphalt binders and mixes,effectively mitigating the adverse impacts of aging.Furthermore,it investigates how these rejuvenators address environmental concerns by identifying compatibility issues,assessing long-term performance,and evaluating economic feasibility.Finally,the paper outlines potential advancements and research pathways aimed at optimizing the utilization of bio-based rejuvenators in asphalt concrete,thereby contributing to the sustainable evolution of road infrastructure.

Aqueous-phase reforming of hydroxyacetone solution to bio-based H_(2)over supported Pt catalysts

Aqueous-phase reforming(APR)is an attractive process to produce bio-based hydrogen from waste biomass streams,during which the catalyst stability is often challenged due to the harsh reaction conditions.In this work,three Pt-based catalysts supported on C,AlO(OH),and ZrO_(2)were investigated for the APR of hydroxyacetone solution in afixed bed reactor at 225℃and 35 bar.Among them,the Pt/C catalyst showed the highest turnover frequency for H_(2)production(TOF of 8.9 molH_(2)molPt^(-1)min^(-1))and the longest catalyst stability.Over the AlO(OH)and ZrO_(2)supported Pt catalysts,the side reactions consuming H_(2),formation of coke,and Pt sintering result in a low H_(2)production and the fast catalyst deactivation.The proposed reaction pathways suggest that a promising APR catalyst should reform all oxygenates in the aqueous phase,minimize the hydrogenation of the oxygenates,maximize the WGS reaction,and inhibit the condensation and coking reactions for maximizing the hydrogen yield and a stable catalytic performance.

Bio-inspired Hydroxyapatite/Gelatin Transparent Nanocomposites

Hydroxyapatite(HA)nanoparticles impart outstanding mechanical properties to organicinorganic nanocomposites in bone.Inspired by the composite structure of HA nanoparticles and collagen in bone,a high performance HA/gelatin nanocomposite was first developed.The nanocomposites have much better mechanical properties(elongation at break 29.9%,tensile strength 90.7 MPa,Young’s modulus 5.24 GPa)than pure gelatin films(elongation at break 9.3%,tensile strength 90.8 MPa,Young’s modulus 2.5 GPa).In addition,the composite films keep a high transmittance in visible wavelength range from 0%to 60%of the HA solid content.These differences in properties are attributed to the homogeneous distribution of HA nanoparticles in the gelatin polymer matrix and the strong interaction between the particle surfaces and the gelatin molecules.This protocol should be promising for HA-based nanocomposites with enhanced mechanical properties for biomedical applications.

Increasing the toughness while reducing the viscosity of carbon nanotube/ polyether imide/polyether ether ketone nanocomposites

Polyether ether ketone(PEEK)has good mechanical properties.However,its high viscosity when molten limits its use because it is hard to process.PEEK nanocomposites containing both carbon nanotubes(CNTs)and polyether imide(PEI)were pre-pared by a direct wet powder blending method using a vertical injection molding machine.The addition of an optimum amount of PEI lowered the viscosity of the molten PEEK by approximately 50%while producing an increase in the toughness of the nanocom-posites,whose strain to failure increased by 129%,and fracture energy increased by 97%.The uniformly dispersed CNT/PEI powder reduced the processing difficulty of PEEK nanocomposites without affecting the thermal resistance.This improvement of the strength and viscosity of PEEK facilitate its use in the preparation of thermoplastic composites.

Efficacy of graphene nanocomposites for air disinfection in dental clinics: A randomized controlled study

BACKGROUND Aerosols containing disease-causing microorganisms are produced during oral diagnosis and treatment can cause secondary contamination.AIM To investigate the use of graphene material for air disinfection in dental clinics by leveraging its adsorption and antibacterial properties.METHODS Patients who received ultrasonic cleaning at our hospital from April 2023 to April 2024.They were randomly assigned to three groups(n=20 each):Graphene nanocomposite material suction group(Group A),ordinary filter suction group(Group B),and no air suction device group(Group C).The air quality and air colony count in the clinic rooms were assessed before,during,and after the procedure.Additionally,bacterial colony counts were obtained from the air outlets of the suction devices and the filter screens in Groups A and B.RESULTS Before ultrasonic cleaning,no significant differences in air quality PM2.5 and colony counts were observed among the three groups.However,significant differences in air quality PM2.5 and colony counts were noted among the three groups during ultrasonic cleaning and after ultrasonic treatment.Additionally,the number of colonies on the exhaust port of the suction device and the surface of the filter were significantly lower in Group A than in Group B(P=0.000 and P=0.000,respectively).CONCLUSION Graphene nanocomposites can effectively sterilize the air in dental clinics by exerting their antimicrobial effects and may be used to reduce secondary pollution.

Assembly of functional carboxymethyl cellulose/polyethylene oxide/anatase TiO_(2) nanocomposites and tuning the dielectric relaxation, optical, and photoluminescence performances

Nanocomposite films consisting of carboxymethyl cellulose,polyethylene oxide(CMC/PEO),and anatase titanium diox-ide(TO)were produced by the use of sol-gel and solution casting techniques.TiO2 nanocrystals were effectively incorporated into CMC/PEO polymers,as shown by X-ray diffraction(XRD)and attenuated total reflectance fourier transform infrared(ATR-FTIR)analysis.The roughness growth is at high levels of TO nanocrystals(TO NCs),which means increasing active sites and defects in CMC/PEO.In differential scanning calorimetry(DSC)thermograms,the change in glass transition temperature(Tg)val-ues verifies that the polymer blend interacts with TO NCs.The increment proportions of TO NCs have a notable impact on the dielectric performances of the nanocomposites,as observed.The electrical properties of the CMC/PEO/TO nanocomposite undergo significant changes.The nanocomposite films exhibit a red alteration in the absorption edge as the concentration of TO NCs increases in the polymer blend.The decline in the energy gap is readily apparent as the weight percentage of TO NCs increases.The photoluminescence(PL)emission spectra indicate that the sites of the luminescence peak maximums show slight variation;peaks get wider,while their intensities decrease dramatically as the concentration of TO increases.These nanocomposite materials show potential for multifunctional applications including optoelectronics,antireflection coatings,pho-tocatalysis,light emitting diodes,and solid polymer electrolytes.

Photocatalytic ozonation-based degradation of phenol by ZnO—TiO_(2)nanocomposites in spinning disk reactor

Spinning disk reactor(SDR)has emerged as a novel process intensification photocatalytic reactor,and it has higher mass transfer efficiency and photon utilization for the degradation of toxic organic pollutants by advanced oxidation processes(AOPs).In this study,ZnO—TiO_(2)nanocomposites were prepared by solgel method,and coated on the disk of SDR by impregnation-pull-drying-calcination method.The performance of catalyst was characterized by X-ray diffraction,scanning electron microscope,X-ray photoelectron spectroscopy,photoluminescence and ultraviolet—visible diffuse reflectance spectroscopy.Photocatalytic ozonation in SDR was used to remove phenol,and various factors on degradation effect were studied in detail.The results showed that the rate of degradation and mineralization reached 100%and 83.4%under UV light irradiation after 50 min,compared with photocatalysis and ozonation,the removal rate increased by 69.3%and 34.7%,and mineralization rate increased by 56.7%and 62.9%,which indicated that the coupling of photocatalysis and ozonation had a synergistic effect.The radical capture experiments demonstrated that the active species such as photogenerated holes(h^(+)),hydroxyl radicals(·OH),superoxide radical(·O_(2)-)were responsible for phenol degradation,and·OH played a leading role in the degradation process,while h+and·O_(2)^(-)played a non-leading role.

Phase field model for electric-thermal coupled discharge breakdown of polyimide nanocomposites under high frequency electrical stress

In contrast to conventional transformers, power electronic transformers, as an integral component of new energy power system, are often subjected to high-frequency and transient electrical stresses, leading to heightened concerns regarding insulation failures. Meanwhile, the underlying mechanism behind discharge breakdown failure and nanofiller enhancement under high-frequency electrical stress remains unclear. An electric-thermal coupled discharge breakdown phase field model was constructed to study the evolution of the breakdown path in polyimide nanocomposite insulation subjected to high-frequency stress. The investigation focused on analyzing the effect of various factors, including frequency, temperature, and nanofiller shape, on the breakdown path of Polyimide(PI) composites. Additionally, it elucidated the enhancement mechanism of nano-modified composite insulation at the mesoscopic scale. The results indicated that with increasing frequency and temperature, the discharge breakdown path demonstrates accelerated development, accompanied by a gradual dominance of Joule heat energy. This enhancement is attributed to the dispersed electric field distribution and the hindering effect of the nanosheets. The research findings offer a theoretical foundation and methodological framework to inform the optimal design and performance management of new insulating materials utilized in high-frequency power equipment.

Removal of Dye Using Lignin-Based Biochar/Poly(ester amide urethane)Nanocomposites from Contaminated Wastewater

The pursuit of incorporating eco-friendly reinforcing agents in polymer composites has accentuated the exploration of various natural biomass-derived materials.The burgeoning environmental crisis spurred by the discharge of synthetic dyes into wastewater has catalyzed the search for effective and sustainable treatment technologies.Among the various sorbent materials explored,biochar,being renewable,has gained prominence due to its excellent adsorption properties and environmental sustainability.It has also emerged as a focal point for its potential to replace other conventional reinforcing agents,viz.,fumed silica,aluminum oxide,treated clays,etc.This study introduces a novel class of polymer nanocomposites comprising of lignin-based biochar particles and poly(ester amide urethane)matrix via a feasible method.The structural evaluation of these nanocomposites was accomplished using Fourier-transform infrared spectroscopy,X-ray photoelectron spectroscopy,and powder X-ray diffraction.The polymer nanocomposites exhibited superior mechanical properties with an increment in tensile strength factor by 45%in comparison to its pristine matrix,along with an excellent toughness value of 90.22 MJm^(−3)at a low loading amount of only 1 wt%.The composites showed excellent improvement in thermal properties with a sharp rise in the glass transition temperature(Tg)value from−28.15℃to 84℃,while also championing sustainability through inherent biodegradability attributes.Beyond their structural prowess,these polymer nanocomposites demonstrated excellent potential as adsorbents,displaying efficient removal of malachite green and tartrazine dyes from aqueous systems with a removal efficiency of 87.25%and 73.98%,respectively.The kinetics study revealed the pseudo second order model to be the precision tool to assess the dye removal study.Complementing this,the Langmuir adsorption isotherm provided a framework to assess the sorption features of the polymer nanocomposites.Overall,these renewable biochar integrated polymer matrices boast remarkable recovery capabilities up to seven cycles of usage with an excellent dye recovery percentage of 95.21%for the last cycle,thereby defining sustainability as well as economic feasibility.

Mechanism for thermite reactions of aluminum/iron-oxide nanocomposites based on residue analysis

Sol-gel method was employed to combine Al and iron-oxide to form nanocomposites （nano-Al/xero-Fe2O3 and micro-Al/xero-Fe2O3）. SEM, EDS and XRD analyses were used to characterize the nanocomposites and the results indicated that nano-Al and micro-Al were compactly wrapped by amorphous iron-oxide nanoparticles （about 20 nm）, respectively. The iron-oxide showed the mass ratio of Fe to O as similar as that in Fe2O3. Thermal analyses were performed on two nanocomposites, and four simple mixtures （nano-Al＋xero-Fe2O3, nano-Al＋micro-Fe2O3, micro-Al＋xero-Fe2O3, and micro-Al＋micro-Fe2O3） were also analyzed. There were not apparent distinctions in the reactions of thermites fueled by nano-Al. For thermites fueled by micro-Al, the DSC peak temperatures of micro-Al/Xero-Fe2O3 were advanced by 68.1 ℃ and 76.8 ℃ compared with micro-Al＋xero-Fe2O3 and micro-Al＋micro-Fe2O3, respectively. Four thermites, namely, nano-Al/xero-Fe2O3, nano-Al＋micro-Fe2O3, micro-Al/xero-Fe2O3, and micro-Al＋micro-Fe2O3, were heated from ambient temperature to 1020 ℃, during which the products at 660 ℃ and 1020 ℃ were collected and analyzed by XRD. Crystals of Fe, FeAl2O4, Fe3O4,α-Fe2O3, Al,γ-Fe2O3, Al2.667O4, FeO andα-Al2O3 were indexed in XRD patterns. For each thermite, according to the specific products, the possible equations were given. Based on the principle of the minimum free energy, the most reasonable equations were inferred from the possible reactions.

Preparation of three-dimensional interconnected mesoporous anatase TiO_2-SiO_2 nanocomposites with high photocatalytic activities

In this article, we report the preparation of a three-dimensional（3D） interconnected mesoporous anatase TiO2-SiO2 nanocomposite. The nanocomposite was obtained by using an ordered two-dimensional（2D） hexagonal mesoporous anatase 70 TiO2-30 SiO2-950 nanocomposite（crystallized at 950 °C for 2 h） as a precursor, NaO H as an etchant of SiO2 via a ＂creating mesopores in the pore walls＂ approach. Our strategy adopts mild conditions of creating pores such as diluted NaO H solution, appropriate temperature and solid/liquid ratio, etc. aiming at ensuring the integrities of mesopores architecture and anatase nanocrystals. XRD, TEM and N2 sorption techniques have been used to systematically investigate the physico-chemical properties of the nanocomposites. The results show that the intrawall mesopores are highly dense and uniform（average pore size 3.6 nm）, and highly link the initial mesochannels in a 3D manner while retaining mesostructural integrity. There is no significant change to either crystallinity or size of the anatase nanocrystals before and after creating the intrawall mesopores. The photocatalytic degradation rates of rhodamine B（RhB, 0.303 min^–1） and methylene blue（MB, 0.757 min^–1） dyes on the resultant nanocomposite are very high, which are 5.1 and 5.3 times that of the precursor; even up to 16.5 and 24.1 times that of Degussa P25 photocatalyst, respectively. These results clearly demonstrate that the 3D interconnected mesopores structure plays an overwhelming role to the increments of activities. The 3D mesoporous anatase TiO2-SiO2 nanocomposite exhibits unexpected-high degradation activities to RhB and MB in the mesoporous metal oxide-based materials reported so far. Additionally, the nanocomposite is considerably stable and reusable. We believe that this method would pave the way for the preparation of other 3D highly interconnected mesoporous metal oxide-based materials with ultra-high performance.

Structural and mechanical properties of CuZr/AlN nanocomposites

Powder metallurgy method was used to prepare copper alloy nanocomposites （CuZr/AlN） with high strength and conductivity. Optical microscopy, high-resolution transmission electron microscopy and other methods were adopted to study the impact of different sintering technologies on the structural and mechanical properties as well as the impact of solution and aging treatments on the mechanical properties of CuZr/AlN. The result shows that the specimen has a dense structure, and the size of the crystal grain is around 0.2 μm. The Brinell hardness of the specimen increases with the increase in re-pressing pressure and sintering temperature. The Brinell hardness of specimen also increases with the increase in zirconium content. However, above 0.5%（mass fraction） of zirconium content, the Brinell hardness of the nanocomposites is reduced. The buckling strength of the specimens increases with the increase in re-pressing pressure and sintering temperature. The buckling strength is the highest when the zirconium content is 0.5%. The Brinell hardness is lower after solution and aging treatments at 900 ℃. The Brinell hardness of the CuZr/AlN series specimen after the aging treatment at 500 ℃ or 600 ℃ increases. The specimen was also over aged at 700 ℃.

Urchin-like CoCu Bimetallic Nanocomposites for Catalytic Hydrogenolysis of Glycerol to Propanediols

Bimetallic CoCu nanocomposites were synthesized in polyol by using Ru as heterogeneous nucleation agent and stearic acid as surfactant, and their catalytic properties were investi- gated by hydrogenolysis of glycerol to propanediols. It was found that the surfactant could induce Co nanocrystals to form nanowires as structure-directing agent, while it＇s ineffective for Cu because only spherical Cu particles were produced under the same condition. When Co2＋ and Cu2＋ coexist in polyol, Cu2＋ is firstly reduced and forms the spherical particles, and then the Cu particles afford surface for the subsequential reduction of Co2＋ and growth of Co nanocrystals to form the nanorods, obtaining the urchin-like CoCu nanocomposites. The catalytic performance in selective hydrogenolysis of glycerol to propanediols proposed that the CoCu urchin-like nanocomposites was superior to the Co nanowires possibly due to that the synergistic effect between Co and Cu component promoted conversion of glyc- erol and obtained the higher propanediol yields based on the specific surface areas of the catalysts.

Preparation and Flame Retardancy of Polyurethane/POSS Nanocomposites

Polyurethane/polyhedral oligomeric sisesquioxane （PU/POSS） nanocomposites were syn- thesized via polymerization utilizing the compatibility between POSS nanopartieles and 4J-diphenyl methylene diisocyanate. Scanning electron microscope images and Fourier transform infrared spectra revealed that POSS nanoparticles were dispersed in PU matrix. Thermal gravimetric analysis was employed to investigate the thermal decomposition be- havior of PU/POSS nanocomposites at elevated temperatures. Then fire performance was evaluated by limiting oxygen index, underwriters laboratories 94 testing and char residue morphology. These results showed that the addition of POSS promoted the formation of char residues which were covered on the surface of polymer composites, leading to the ira-provement of thermal stability and flame retardancy.

Flexible Tactile Electronic Skin Sensor with 3D Force Detection Based on Porous CNTs/PDMS Nanocomposites

Flexible tactile sensors have broad applications in human physiological monitoring,robotic operation and human-machine interaction.However,the research of wearable and flexible tactile sensors with high sensitivity,wide sensing range and ability to detect three-dimensional(3D)force is still very challenging.Herein,a flexible tactile electronic skin sensor based on carbon nanotubes(CNTs)/polydimethylsiloxane(PDMS)nanocomposites is presented for 3D contact force detection.The 3D forces were acquired from combination of four specially designed cells in a sensing element.Contributed from the double-sided rough porous structure and specific surface morphology of nanocomposites,the piezoresistive sensor possesses high sensitivity of 12.1 kPa?1 within the range of 600 Pa and 0.68 kPa?1 in the regime exceeding 1 kPa for normal pressure,as well as 59.9 N?1 in the scope of<0.05 N and>2.3 N?1 in the region of<0.6 N for tangential force with ultra-low response time of 3.1 ms.In addition,multi-functional detection in human body monitoring was employed with single sensing cell and the sensor array was integrated into a robotic arm for objects grasping control,indicating the capacities in intelligent robot applications.

Sandwich-Like Fe&TiO2@C Nanocomposites Derived from MXene/Fe-MOFs Hybrids for Electromagnetic Absorption

Electromagnetic pollution has been causing a series of problems in people’s life,and electromagnetic absorbers with lightweight and broad absorbing bandwidth properties are widely desired.In this work,novel sandwich-like 2D laminated Fe&TiO2 nanoparticles@C nanocomposites were rationally designed and successfully developed from the MXene–MOFs hybrids.The formation of Fe and rutile-TiO2 nanoparticles sandwiched by the two-dimensional carbon nanosheets provided strong electromagnetic energy attenuation and good impedance matching for electromagnetic wave(EMW)absorption.As expected,the nanocomposites achieved a broad effective absorption bandwidth of 6.5 GHz at a thickness of only 1.6 mm and the minimum reflection loss(RL)value of−51.8 dB at 6.6 GHz with a thickness of 3 mm.This work not only provides a good design and fabricating concept for the laminated metal and functional nanoparticles@C nanocomposites with good EMW absorption,but also offers an important guideline to fabricate various two-dimensional nanocomposites derived from the MXene precursors.

Synthesis, properties, and applications of graphene oxide/reduced graphene oxide and their nanocomposites

Thanks to their remarkable mechanical, electrical, thermal, and barrier properties, graphene-based nanocomposites have been a hot area of research in the past decade. Because of their simple top-down synthesis, graphene oxide (GO) and reduced graphene oxide (rGO) have opened new possibilities for gas barrier, membrane separation, and stimuli-response characteristics in nanocomposites. Herein, we review the synthesis techniques most commonly used to produce these graphene derivatives, discuss how synthesis affects their key material properties, and highlight some examples of nanocomposites with unique and impressive properties. We specifically highlight their performances in separation applications, stimuli-responsive materials, anti-corrosion coatings, and energy storage. Finally, we discuss the outlook and remaining challenges in the field of practical industrial-scale production and use of graphene-derivative-based polymer nanocomposites.