The performance of solid solution aging treatment on aluminum matrix composites prepared by powder metallurgy and reinforced with 6061 aluminum alloy powder as matrix;meanwhile, nano silicon carbide particles(nm Si Cp...The performance of solid solution aging treatment on aluminum matrix composites prepared by powder metallurgy and reinforced with 6061 aluminum alloy powder as matrix;meanwhile, nano silicon carbide particles(nm Si Cp), submicron silicon carbide particles(1 μm Si Cp) and Ti particles were studied. The Al/Si Cp composite powder was prepared by high-energy ball milling, and then cold-pressed, sintered, hotextruded, and then heat-treated with different solution temperatures and aging times for the extruded composites. Optical microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy(EDS), X-ray diffractometer(XRD) and extrusion testing were used to analyze and test the microstructure and mechanical properties of aluminum matrix composites. The results show that after the multi-stage solid solution at 530 ℃×2 h+535 ℃×2 h+540 ℃×2 h, the particles are mainly equiaxed grains and uniformly distributed. There is no reinforcement agglomeration, and the surface is dense and the insoluble phase is basically dissolved. In the matrix, the strengthening effect is good, and the hardness and compressive strength are 179.43 HV and 680.42 MPa, respectively. Under this solution process, when the aluminum matrix composites are aged at 170 ℃ for 10 h, the hardness and compressive strength can reach their peaks and increase to 195.82 HV and 721.48 MPa, respectively.展开更多
Microwave absorbing materials(MAMs)characterized by high absorption efficiency and good environmental tolerance are highly desirable in practical applications.Both silicon carbide and carbon are considered as stable M...Microwave absorbing materials(MAMs)characterized by high absorption efficiency and good environmental tolerance are highly desirable in practical applications.Both silicon carbide and carbon are considered as stable MAMs under some rigorous conditions,while their composites still fail to produce satisfactory microwave absorption performance regardless of the improvements as compared with the individuals.Herein,we have successfully implemented compositional and structural engineering to fabricate hollow Si C/C microspheres with controllable composition.The simultaneous modulation on dielectric properties and impedance matching can be easily achieved as the change in the composition of these composites.The formation of hollow structure not only favors lightweight feature,but also generates considerable contribution to microwave attenuation capacity.With the synergistic effect of composition and structure,the optimized SiC/C composite exhibits excellent performance,whose the strongest reflection loss intensity and broadest effective absorption reach-60.8 dB and 5.1 GHz,respectively,and its microwave absorption properties are actually superior to those of most SiC/C composites in previous studies.In addition,the stability tests of microwave absorption capacity after exposure to harsh conditions and Radar Cross Section simulation data demonstrate that hollow SiC/C microspheres from compositional and structural optimization have a bright prospect in practical applications.展开更多
Fiber-reinforced composites possess anisotropic mechanical and heat transfer properties due to their anisotropic fibers and structure distribution.In C/Si C composites,the out-of-plane thermal conductivity has mainly ...Fiber-reinforced composites possess anisotropic mechanical and heat transfer properties due to their anisotropic fibers and structure distribution.In C/Si C composites,the out-of-plane thermal conductivity has mainly been studied,whereas the in-plane thermal conductivity has received less attention due to their limited thickness.展开更多
In the present study,the unique three-dimensional graphene coated nickel(Ni/C)foam reinforced silicon carbide(Ni/C@SiC)composites were first obtained via the precursor impregnation and pyrolysis(PIP)processes.The micr...In the present study,the unique three-dimensional graphene coated nickel(Ni/C)foam reinforced silicon carbide(Ni/C@SiC)composites were first obtained via the precursor impregnation and pyrolysis(PIP)processes.The microstructure images indicated that the SiC fillers were successfully prepared in the skeleton pores of the Ni/C foam.The influence of the PIP cycles on the microwave absorption performances was researched,and the results indicated that after the primary PIP process,Ni/C@SiC-I possessed the optimal microwave absorbing performance with a minimum reflection loss(RL)of-25.87 d B at 5.28 GHz and 5.00 mm.Besides,the RL values could be below-10.00 dB from 5.88 GHz to 7.74 GHz when the corresponding matching thickness was 3.85 mm.However,the microwave absorption properties of Ni/C@SiC-II and Ni/C@SiC-Ⅲwere tremendously degraded as the PIP times increased.At last,the electromagnetic parameter,dielectric loss,attenuation constant as well as impedance matching coefficient were further investigated to analyze the absorbing mechanism,which opened a new path for the certain scientific evaluation of the absorbing materials and had extremely important to the defence technology.展开更多
High toughness and reliable three-dimensional needled C/SiC composites were fabricated by chemical vapor infiltration (CVI). An approach to analyze the tensile behaviors at room temperature and the damage accumulati...High toughness and reliable three-dimensional needled C/SiC composites were fabricated by chemical vapor infiltration (CVI). An approach to analyze the tensile behaviors at room temperature and the damage accumulation of the composites by means of acoustic emission was researched. Also the fracture morphology was examined by S-4700 SEM after tensile tests to prove the damage mechanism. The results indicate that the cumulative energy of acoustic emission (AE) signals can be used to monitor and evaluate the damage evolution in ceramic-matrix composites. The initiation of room-temperature tensile damage in C/SiC composites occurred with the growth of micro-cracks in the matrix at the stress level about 40% of the ultimate fracture stress. The level 70% of the fracture stress could be defined as the critical damage strength.展开更多
The 3D fine-woven punctured C/C-(PyC/SiC/TaC)composites,composed of PyC/SiC/TaC interphases and pyrocarbon (PyC)matrix,were synthesized by isothermal chemical vapor infiltration(ICVI)methods.The alternating layers and...The 3D fine-woven punctured C/C-(PyC/SiC/TaC)composites,composed of PyC/SiC/TaC interphases and pyrocarbon (PyC)matrix,were synthesized by isothermal chemical vapor infiltration(ICVI)methods.The alternating layers and the structure of these composites were examined by polarized light microscopy(PLM),X-ray diffractometry(XRD)and scanning electron microscopy(SEM).It is found that the PyC matrix has rough laminar(RL)structure,the TaC layer has NaCl-type cubic structure,and the SiC layer has few wurtzite type 10H-SiC besidesβ-SiC structure.The effects of fiber coating and the bulk density on the tensile and flexural properties of composites along X or Y and Z direction were investigated.It is shown that fiber coated 3D woven punctured C/C composites have good tensile and flexural strength,and the maximum of flexural strength is 375 MPa in X or Y direction at density of 1.89 g/cm 3 ,which is about three times higher than that of samples without TaC/SiC fiber coating.The flexural strength and bending strength increase with increasing the density of the composites.The analysis of fracture surfaces reveals that fibers and fiber bundles are pulled out in composites,indicating that the composite exhibits a non-linear failure behavior through propagation and deflection of the cracks.展开更多
基金the Key Projects of Equipment Pre-research Foundation of the Ministry of Equipment Development of the Central Military Commission of China (No.6140922010201)the Key R&D Plan of Zhenjiang in 2018(No.GY2018021)。
文摘The performance of solid solution aging treatment on aluminum matrix composites prepared by powder metallurgy and reinforced with 6061 aluminum alloy powder as matrix;meanwhile, nano silicon carbide particles(nm Si Cp), submicron silicon carbide particles(1 μm Si Cp) and Ti particles were studied. The Al/Si Cp composite powder was prepared by high-energy ball milling, and then cold-pressed, sintered, hotextruded, and then heat-treated with different solution temperatures and aging times for the extruded composites. Optical microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy(EDS), X-ray diffractometer(XRD) and extrusion testing were used to analyze and test the microstructure and mechanical properties of aluminum matrix composites. The results show that after the multi-stage solid solution at 530 ℃×2 h+535 ℃×2 h+540 ℃×2 h, the particles are mainly equiaxed grains and uniformly distributed. There is no reinforcement agglomeration, and the surface is dense and the insoluble phase is basically dissolved. In the matrix, the strengthening effect is good, and the hardness and compressive strength are 179.43 HV and 680.42 MPa, respectively. Under this solution process, when the aluminum matrix composites are aged at 170 ℃ for 10 h, the hardness and compressive strength can reach their peaks and increase to 195.82 HV and 721.48 MPa, respectively.
基金supported by the National Natural Science Foundation of China(No.21676065 and No.52373262)China Postdoctoral Science Foundation(2021MD703944,2022T150782).
文摘Microwave absorbing materials(MAMs)characterized by high absorption efficiency and good environmental tolerance are highly desirable in practical applications.Both silicon carbide and carbon are considered as stable MAMs under some rigorous conditions,while their composites still fail to produce satisfactory microwave absorption performance regardless of the improvements as compared with the individuals.Herein,we have successfully implemented compositional and structural engineering to fabricate hollow Si C/C microspheres with controllable composition.The simultaneous modulation on dielectric properties and impedance matching can be easily achieved as the change in the composition of these composites.The formation of hollow structure not only favors lightweight feature,but also generates considerable contribution to microwave attenuation capacity.With the synergistic effect of composition and structure,the optimized SiC/C composite exhibits excellent performance,whose the strongest reflection loss intensity and broadest effective absorption reach-60.8 dB and 5.1 GHz,respectively,and its microwave absorption properties are actually superior to those of most SiC/C composites in previous studies.In addition,the stability tests of microwave absorption capacity after exposure to harsh conditions and Radar Cross Section simulation data demonstrate that hollow SiC/C microspheres from compositional and structural optimization have a bright prospect in practical applications.
基金supported by the National Natural Science Foundation of China(Grant Nos.52276086 and 52130604)the Basic Research Program of China(Grant No.514010303-102)the K.C.Wong Education Foundation。
文摘Fiber-reinforced composites possess anisotropic mechanical and heat transfer properties due to their anisotropic fibers and structure distribution.In C/Si C composites,the out-of-plane thermal conductivity has mainly been studied,whereas the in-plane thermal conductivity has received less attention due to their limited thickness.
基金supported by the Fundamental Research Funds for the Central Universities (Grant No. D5000210522 and D5000200408)Jiangsu Planned Projects for Postdoctoral Research Funds, National Natural Science Foundation of China [grant number 51772151]+2 种基金Natural Science Foundation of Shaanxi Province (Grant No. 2021JQ-117)Basic Research Programs of Taicang (Grant No.TC2020JC10)Natural Science Foundation of Shandong Province (Grant No. ZR2020QE180)
文摘In the present study,the unique three-dimensional graphene coated nickel(Ni/C)foam reinforced silicon carbide(Ni/C@SiC)composites were first obtained via the precursor impregnation and pyrolysis(PIP)processes.The microstructure images indicated that the SiC fillers were successfully prepared in the skeleton pores of the Ni/C foam.The influence of the PIP cycles on the microwave absorption performances was researched,and the results indicated that after the primary PIP process,Ni/C@SiC-I possessed the optimal microwave absorbing performance with a minimum reflection loss(RL)of-25.87 d B at 5.28 GHz and 5.00 mm.Besides,the RL values could be below-10.00 dB from 5.88 GHz to 7.74 GHz when the corresponding matching thickness was 3.85 mm.However,the microwave absorption properties of Ni/C@SiC-II and Ni/C@SiC-Ⅲwere tremendously degraded as the PIP times increased.At last,the electromagnetic parameter,dielectric loss,attenuation constant as well as impedance matching coefficient were further investigated to analyze the absorbing mechanism,which opened a new path for the certain scientific evaluation of the absorbing materials and had extremely important to the defence technology.
基金the National Natural Science Foundation of China(No.90405015)the National Young Elitist Foundation of China(No.50425208)the Doctorate Foundation of Northwestern Polytechnical University(No.CX200406)
文摘High toughness and reliable three-dimensional needled C/SiC composites were fabricated by chemical vapor infiltration (CVI). An approach to analyze the tensile behaviors at room temperature and the damage accumulation of the composites by means of acoustic emission was researched. Also the fracture morphology was examined by S-4700 SEM after tensile tests to prove the damage mechanism. The results indicate that the cumulative energy of acoustic emission (AE) signals can be used to monitor and evaluate the damage evolution in ceramic-matrix composites. The initiation of room-temperature tensile damage in C/SiC composites occurred with the growth of micro-cracks in the matrix at the stress level about 40% of the ultimate fracture stress. The level 70% of the fracture stress could be defined as the critical damage strength.
基金Project(50872154)supported by the National Natural Science Foundation of ChinaProject(20080431029)supported by China Postdoctoral Science FoundationProject supported by the Postdoctoral Science Foundation of Central South University,China
文摘The 3D fine-woven punctured C/C-(PyC/SiC/TaC)composites,composed of PyC/SiC/TaC interphases and pyrocarbon (PyC)matrix,were synthesized by isothermal chemical vapor infiltration(ICVI)methods.The alternating layers and the structure of these composites were examined by polarized light microscopy(PLM),X-ray diffractometry(XRD)and scanning electron microscopy(SEM).It is found that the PyC matrix has rough laminar(RL)structure,the TaC layer has NaCl-type cubic structure,and the SiC layer has few wurtzite type 10H-SiC besidesβ-SiC structure.The effects of fiber coating and the bulk density on the tensile and flexural properties of composites along X or Y and Z direction were investigated.It is shown that fiber coated 3D woven punctured C/C composites have good tensile and flexural strength,and the maximum of flexural strength is 375 MPa in X or Y direction at density of 1.89 g/cm 3 ,which is about three times higher than that of samples without TaC/SiC fiber coating.The flexural strength and bending strength increase with increasing the density of the composites.The analysis of fracture surfaces reveals that fibers and fiber bundles are pulled out in composites,indicating that the composite exhibits a non-linear failure behavior through propagation and deflection of the cracks.