A new heat resisting phenol-starch moulding material (PF2C4) was prepared.Its typical raw materials formulation, preparative technology and moulding technology were determined.The method of its quatity control was put...A new heat resisting phenol-starch moulding material (PF2C4) was prepared.Its typical raw materials formulation, preparative technology and moulding technology were determined.The method of its quatity control was put forward and its properties and economic advantage were analyzed. The results show that typical raw materials formulation(mass percent)of the product is phenol-starch is phenol starch resin∶hexamethylene-tetramine∶wood flour∶calcium carbonate∶magnesium oxide∶zinc stearate∶stearic acid∶Oil Aniline Black∶ultramarine=37.0∶6.4∶30.0∶24.0∶0.6∶0.6∶0.4∶0.5∶0.5.The preparative technological parameters of the product were mixed time ≥60?min, temperature of the working roller 90—100?℃, temperature of the idle roller 145—155?℃, distance of the two rollers 2.0—2.5?mm, warm-up time 4—5?min.combining batch time≥45?min.The moulding, technological parameters of the product were preheating temperature 100—110?℃, preheating time 10—15?min, moulding pressure≥25?MPa, moulding temperature 180—185?℃, moulding time 0.8—1.0?min·mm -1 , exhaust ≥3 times. The quality of the product was controlled by bright outward appearance of sheet material of moulding material and Raschig flow property 80—120?mm of moulding material.The properties of the product came up to the national standard of raw heat resisting phenol-for maldehyde material (PF2C4), specifically its heat properties (thermal deformation temperature 174?℃) and electric properties (insulating resistance 6.0×10 12 ?Ω, dielectric strength 6.7?MV·m -1 , dielectric loss tangent 0.03)surpassed greatly the national standard.It showed very good electric properties in moist environment.By comparison with raw heat resisting thermoplastic phenol-formaldehyde moulding material(PF2C4),the cost of raw materials consumption reduced by is 20.9%.展开更多
在含有高得率浆(HY P)的造纸生产过程中,瑞典中部大学(Mid Sweden University)已经研究出了一系列关于在用高得率浆抄纸的压榨和干燥中改变目前标准条件(即温度和水分含量)而得到的积极影响。目前,用淀粉/羧甲基纤维素(CMC)进行纤维表...在含有高得率浆(HY P)的造纸生产过程中,瑞典中部大学(Mid Sweden University)已经研究出了一系列关于在用高得率浆抄纸的压榨和干燥中改变目前标准条件(即温度和水分含量)而得到的积极影响。目前,用淀粉/羧甲基纤维素(CMC)进行纤维表面改性已经研究成功,结果显示,采用低电耗(大约600k W·h/t)生产的HTCTMP在最佳抄造条件下用来抄纸,成纸的强度指标能够提高数个百分点。展开更多
文摘A new heat resisting phenol-starch moulding material (PF2C4) was prepared.Its typical raw materials formulation, preparative technology and moulding technology were determined.The method of its quatity control was put forward and its properties and economic advantage were analyzed. The results show that typical raw materials formulation(mass percent)of the product is phenol-starch is phenol starch resin∶hexamethylene-tetramine∶wood flour∶calcium carbonate∶magnesium oxide∶zinc stearate∶stearic acid∶Oil Aniline Black∶ultramarine=37.0∶6.4∶30.0∶24.0∶0.6∶0.6∶0.4∶0.5∶0.5.The preparative technological parameters of the product were mixed time ≥60?min, temperature of the working roller 90—100?℃, temperature of the idle roller 145—155?℃, distance of the two rollers 2.0—2.5?mm, warm-up time 4—5?min.combining batch time≥45?min.The moulding, technological parameters of the product were preheating temperature 100—110?℃, preheating time 10—15?min, moulding pressure≥25?MPa, moulding temperature 180—185?℃, moulding time 0.8—1.0?min·mm -1 , exhaust ≥3 times. The quality of the product was controlled by bright outward appearance of sheet material of moulding material and Raschig flow property 80—120?mm of moulding material.The properties of the product came up to the national standard of raw heat resisting phenol-for maldehyde material (PF2C4), specifically its heat properties (thermal deformation temperature 174?℃) and electric properties (insulating resistance 6.0×10 12 ?Ω, dielectric strength 6.7?MV·m -1 , dielectric loss tangent 0.03)surpassed greatly the national standard.It showed very good electric properties in moist environment.By comparison with raw heat resisting thermoplastic phenol-formaldehyde moulding material(PF2C4),the cost of raw materials consumption reduced by is 20.9%.
文摘在含有高得率浆(HY P)的造纸生产过程中,瑞典中部大学(Mid Sweden University)已经研究出了一系列关于在用高得率浆抄纸的压榨和干燥中改变目前标准条件(即温度和水分含量)而得到的积极影响。目前,用淀粉/羧甲基纤维素(CMC)进行纤维表面改性已经研究成功,结果显示,采用低电耗(大约600k W·h/t)生产的HTCTMP在最佳抄造条件下用来抄纸,成纸的强度指标能够提高数个百分点。