The microstructure of Mg-8Zn-4Al-1Ca aged alloy was investigated by TEM and HRTEM. The results show that the hardening produced in the Mg-8Zn-4Al-1Ca alloy is considerably higher than that in the Mg-8Zn-4A1 alloy. A d...The microstructure of Mg-8Zn-4Al-1Ca aged alloy was investigated by TEM and HRTEM. The results show that the hardening produced in the Mg-8Zn-4Al-1Ca alloy is considerably higher than that in the Mg-8Zn-4A1 alloy. A dense dispersion of disc-like Ca2Mg6Zn3 precipitates are formed in Mg-8Zn-4Al-1Ca alloy aged at 160 ℃ for 16 h. In addition, the lattice distortions, honeycomb-looking Moir＆#233; fringes, edge dislocations and dislocation loop also exist in the microstructure. The precipitates of alloy aged at 160 ℃ for 48 h are coarse disc-like and fine dispersed grainy. When the alloy is subjected to aging at 160 ℃ for 227 h, the microstructure consists of numerous MgZn2 precipitates and Ca2Mg6Zn3 precipitates. All the analyses show that Ca is a particularly effective trace addition in improving the age-hardening and postponing the formation of MgZn2 precipitates in Mg-8Zn-4Al alloy aged at 160 ℃.展开更多
In order to further understand the debismuthizing mechanism with calcium and magnesium, the influence of adding amount of calcium on the bismuth removal from lead was examined. A part of the debismuthizing dross sampl...In order to further understand the debismuthizing mechanism with calcium and magnesium, the influence of adding amount of calcium on the bismuth removal from lead was examined. A part of the debismuthizing dross samples were studied by electron probe microanalysis （EPMA）. The results show that the calculated bismuthide governing debismuthizing process is Ca3Mg7Bi8, which may be a mixture of Ca3Bi2, CaBi, CaBi3 and Mg3Bi2. And the bismuthide formed during the debismuthizing process exists in two states： one is free bismuthide in the matrix of dross, and the other is symbiotic with Pb-Ca phase.展开更多
基金Project(51141007)supported by the National Natural Science Foundation of ChinaProject(E2013501096)supported by Hebei Province Natural Science Foundation,China
文摘The microstructure of Mg-8Zn-4Al-1Ca aged alloy was investigated by TEM and HRTEM. The results show that the hardening produced in the Mg-8Zn-4Al-1Ca alloy is considerably higher than that in the Mg-8Zn-4A1 alloy. A dense dispersion of disc-like Ca2Mg6Zn3 precipitates are formed in Mg-8Zn-4Al-1Ca alloy aged at 160 ℃ for 16 h. In addition, the lattice distortions, honeycomb-looking Moir＆#233; fringes, edge dislocations and dislocation loop also exist in the microstructure. The precipitates of alloy aged at 160 ℃ for 48 h are coarse disc-like and fine dispersed grainy. When the alloy is subjected to aging at 160 ℃ for 227 h, the microstructure consists of numerous MgZn2 precipitates and Ca2Mg6Zn3 precipitates. All the analyses show that Ca is a particularly effective trace addition in improving the age-hardening and postponing the formation of MgZn2 precipitates in Mg-8Zn-4Al alloy aged at 160 ℃.
文摘In order to further understand the debismuthizing mechanism with calcium and magnesium, the influence of adding amount of calcium on the bismuth removal from lead was examined. A part of the debismuthizing dross samples were studied by electron probe microanalysis （EPMA）. The results show that the calculated bismuthide governing debismuthizing process is Ca3Mg7Bi8, which may be a mixture of Ca3Bi2, CaBi, CaBi3 and Mg3Bi2. And the bismuthide formed during the debismuthizing process exists in two states： one is free bismuthide in the matrix of dross, and the other is symbiotic with Pb-Ca phase.