Carbon Fiber Breakage Mechanism in Aluminum(Al)/Carbon Fibers(CFs) Composite Sheet during Accumulative Roll Bonding(ARB) Process

We put forward a method of fabricating Aluminum(Al)/carbon fibers(CFs) composite sheets by the accumulative roll bonding(ARB) method. The finished Al/CFs composite sheet has CFs and pure Al sheets as sandwich and surface layers. After cross-section observation of the Al/CFs composite sheet, we found that the CFs discretely distributed within the sandwich layer. Besides, the tensile test showed that the contribution of the sandwich CFs layer to tensile strength was less than 11% compared with annealed pure Al sheet. With ex-situ observation of the CFs breakage evolution with-16%,-32%, and-45% rolling reduction during the ARB process, the plastic instability of the Al layer was found to bring shear damages to the CFs. At last, the bridging strengthening mechanism introduced by CFs was sacrificed. We provide new insight into and instruction on Al/CFs composite sheet preparation method and processing parameters.

RELATIONS BETWEEN INTERFACE OF CF/Al-4.5 Cu COMPOSITE AND SOLIDIFICATION PROCESSING

ＲＥＬＡＴＩＯＮＳＢＥＴＷＥＥＮＩＮＴＥＲＦＡＣＥＯＦＣＦ／Ａｌ４．５ＣｕＣＯＭＰＯＳＩＴＥＡＮＤＳＯＬＩＤＩＦＩＣＡＴＩＯＮＰＲＯＣＥＳＳＩＮＧ①ＣｈｕＳｈｕａｎｇｊｉｅ，ＷｕＲｅｎｊｉｅＲｅｓｅａｒｃｈＩｎｓｔｉｔｕｔｅｏｆＣｏｍｐｏｓｉｔｅＭ...

Ballistic Performance and Damage Characteristics of Chemical Vapor Infiltration Quasi 3D-Cf/SiC Composites

To investigate the ballistic performance and damage characteristics of quasi threedimensional（3D） needle-punched Cf/SiC composites prepared by chemical vapor infiltration（CVI）,penetration experiments were conducted by using 7.62 mm armor piercing incendiary（API）.Macro and micro fracture morphologies were then observed on recycled targets.The results show that the protection coefficient of 3D Cf/SiC composites is 2.54.High porosity and many micro thermal stress cracks may directly lead to the lower ballistic performance.Flat fracture morphology was observed on the crater surface.The low dynamic fracture strength along layer direction may be attributed to the voids and microcracks caused by residual thermal stress.The damage characteristics of Cf/Si C composites include matrix cracking,fiber bundle cracking,interfacial debonding,fiber fracture,and fiber bundle pull-out.And interfacial debonding and fiber fracture may play major roles in energy absorption.

偶联剂对CF/SiO_2/BMI复合材料性能的影响

在氧化处理后的碳纤维 (CF)表面涂敷不同的偶联剂 ,石英粉用KH -5 5 0和脱模剂处理 ,然后在双辊混炼机上与双马来酰亚胺 (BMI)树脂熔融混炼 ,采用模压工艺制备CF/SiO2 /BMI复合材料试样 ,对其弯曲强度和吸水率进行了测试。并且用电子光谱化学分析 (ESCA)分析了氧化前后碳纤维表面的成分和官能团 ,讨论了碳纤维表面处理对复合材料弯曲强度的影响。结果表明 。

Evaluation of Tribological Performance of PTFE Composite Filled with Rare Earths Treated Carbon Fibers under Water-Lubricated Condition

Carbon fibers （CFs） were surface treated with air-oxidation, rare earths （RE） after air-oxidation, and rare earths, respectively. Erichsen test was conducted to study the interfacial adhesion of PTFE composites filled with carbon fibers treated with different treatment methods. Tribological properties of the PTFE composites, sliding against GCr15 steel under water-lubricated condition, were investigated on a reciprocating ball-on-disk UMT-2MT tribometer. The worn surfaces of the composites were examined using scanning electron microscopy. Experimental results reveal that RE treatment is superior to air oxidation in promoting tribological properties of CF reinforced PTFE （CF/PTFE） composite. The friction and wear properties of PTFE composite filled with RE treated CF are the best of the PTFE composites. RE treatment is more effective than air oxidation to improve the tribological properties of CF/PTFE composite owing to the effective improvement of interfacial adhesion between carbon fibers and PTFE matrix.

Effect of rare earths surface treatment on tribological properties of carbon fibers reinforced PTFE composite under oil-lubricated condition

The effect of rare earths （RE） surface treatment of carbon fibers （CF） on tribological properties of CF reinforced polytetrafluoroethylene （PTFE） composites under oil-lubricated condition was investigated. Experimental results revealed that RE treated CF reinforced PTFE （CF/PTFE） composite had the lowest friction coefficient and wear under various applied loads and sliding speeds compared with untreated and air-oxidated composites. X-ray photoelectron spectroscopy （XPS） study of carbon fiber surface showed that, after RE treatment, oxygen concentration increased obviously, and the amount of oxygen-containing groups on CF surfaces were largely increased. The increase in the amount of oxygen-containing groups enhanced interfacial adhesion between CF and PTFE matrix. With strong interfacial adhesion of the composite, stress could be effectively transmitted to carbon fibers; carbon fibers were strongly bonded with VITE matrix, and large scale rubbing-off of PTFE be prevented, therefore, tribological properties of the composite was improved.

Improved wettability and mechanical properties of metal coated carbon fiber-reinforced aluminum matrix composites by squeeze melt infiltration technique

In order to improve the wettability and bonding performance of the interface between carbon fiber and aluminum matrix,nickel-and copper-coated carbon fiber-reinforced aluminum matrix composites were fabricated by the squeeze melt infiltration technique.The interface wettability,microstructure and mechanical properties of the composites were compared and investigated.Compared with the uncoated fiber-reinforced aluminum matrix composite,the microstructure analysis indicated that the coatings significantly improved the wettability and effectively inhibited the interface reaction between carbon fiber and aluminum matrix during the process.Under the same processing condition,aluminum melt was easy to infiltrate into the copper-coated fiber bundles.Furthermore,the inhibited interface reaction was more conducive to maintain the original strength of fiber and improve the fiber−matrix interface bonding performance.The mechanical properties were evaluated by uniaxial tensile test.The yield strength,ultimate tensile strength and elastic modulus of the copper-coated carbon fiber-reinforced aluminum matrix composite were about 124 MPa,140 MPa and 82 GPa,respectively.In the case of nickel-coated carbon fiber-reinforced aluminum matrix composite,the yield strength,ultimate tensile strength and elastic modulus were about 60 MPa,70 MPa and 79 GPa,respectively.The excellent mechanical properties for copper-coated fiber-reinforced composites are attributed to better compactness of the matrix and better fiber−matrix interface bonding,which favor the load transfer ability from aluminam matrix to carbon fiber under the loading state,giving full play to the bearing role of carbon fiber.

Preparation and Arc Erosion Resistance of C_f/Cu Composite by Vacuum Melting Infiltration

Cf/Cu composite was prepared by vacuum melting infiltration. Ti and Cr were doped to the Cu alloy to improve the wettability between Cu and carbon. The microstrueture was investigated by XRD, SEM and EDS. The arc erosion rate of Cf/Cu composite was investigated in vacuum. The results showed that the Ti and Cr could improve the wettability between Cu and C/C preform and the infiltration ability of Cu into C/ C preform greatly. A TiC interface formed between the fibers and matrix. The good bonding between the fiber and matrix guaranteed that part of the Cu matrix can still be bonded on the fibers even when the material was exposed to the plasma. Consequently, the carbon fibers were protected from the erosion. In comparison, Cu was completely consumed by the arc erosion. Hence, the graphite was eroded and presented a cauliflower-like morphology. Therefore, the prepared C/Cu bad better ability to resist the arc erosion, compared with common Cu-C material.

Study on Anticorrosive Cerium Conversion Coating of C_f/6061A1 Composite Surface

The optimum chemical passivation process of the rare earth metal (REM) conversion coating on the Cf/6061Al composite surface was introduced in this paper and its polarization curves properties were investigated. Ridge-like coatings were found by scanning electro microscope (SEM) observations, and the Al matrix and carbon fibre reinforcement were both coated with Ce conversion coatings, with some minor cracks. The energy dispersive spectroscopy (EDS) plane scan analysis indicates that the major elements in the coating are Ce, O, Si, Al and the Ce content reaches 47.48% (mass fraction). The Ce conversion coatings increase the corrosion resisting properties of Cf/6061A1 composite, with a higher free corrosion potential (Ecorr) and a lower free corrosion current density (icorr) for the coated composite than those of the bare composite. And the Boehmite-treatment would enhance the corrosion resistance of the REM conversion coating. The ca-thodic polarization and anodic polarization were retarded by REM conversion coating, resulting in an improved corrosion resistance.

Feasibility Study on Cryogenic Milling of Carbon Fiber Reinforced Silicon Carbide Composites

Carbon fiber reinforced silicon carbide matrix(Cf/SiC)composites have the most potential application for high-temperature components of aerospace high-end equipment.However,high cutting temperature,rapid tool wear and severe surface damages are the main problems in dry cutting Cf/SiC composites process.The feasibility study on cryogenic milling of Cf/SiC composites using liquid nitrogen as coolant is investigated.Influences of milling parameters and coolant on temperature,cutting force,surface quality and tool wear are investigated,which is compared with dry cutting.Experimental results reveal that the cutting temperature in cryogenic milling of Cf/SiC composites is reduced by about 40%—60%compared with dry cutting.The milling force increases gradually with the increase of spindle speed,feed rate,depth and width of milling in cryogenic milling process.In addition,the machined surface quality in cryogenic milling is superior to that in dry cutting process.Fiber fracture,matrix damage and fiber matrix debonding are main material removal mechanisms.Flank face wear is the main wear form of the polycrystalline diamond(PCD)end mills.The tool life is prolonged in the cryogenic milling process because the reduced temperature inhibits the softening of Co binder and phase transition of diamond in the PCD end mills.

Study on vacuum brazing of C_f/C composites

Vacuum brazing experiments of Cf/C composites were carried out using pure Al and Al-5 Ti-B as brazing fillers , and shearing strength of the joints was measured. The microstructures of the brazed joints were studied by means of scanning electron microscopy （SEM） and energy dispersive X-ray spectrometer. The results indicate that the brazing temperature is the important processing parameter affecting the quality of the brazed joints. Vacuum brazing of Cf/C composites can be achieved employing the pure Al and AI-S Ti-B brazing fillers at a brazing temperature of 730 ℃ or 750 ℃ , respectively. Moreover, the joints have excellent microstructures with shear strength reaching the level of practical applications.

CF/BMI纤维缠绕成型工艺及其复合材料性能的研究

本文研究了CF／BMI纤维缠绕成型工艺，并采用常压固化制成CF／BMI复合材料和耐高温管。

Improving Corrosion Resistance of C_f/Mg Composites using Rare Earth Conversion Coatings

The surface of carbon fiber reinforced Mg matrix (Cf/Mg) composites was modified by treatment of rare earth conversion coating, and nontoxic, non-pollution Ce conversion coatings were prepared. The effect of the coatings on corrosion behaviors of composites was investigated by electrochemical polarization technology and electrochemical impedance spectroscopy (EIS) in 3.5% NaCl solution. The higher Ecorr and lower icorr were obtained by Ce conversion coatings. EIS results showed that the higher values of R2 were obtained by treatment containing CeCl3, the high corrosion resistance occured in treatment containing CeCl3, the low corrosion resistance in uncoating sample, the coating of treatment containing Ce(NO3)3 was medium. The microstructure of Ce conversion coatings was observed by scanning electron microscopy (SEM), and the elements of corresponding for coatings was characterized by energy dispersive spectrometer (EDS). The micro-cracks and Ce-riched spherical particles were characteristics of these coatings.

Processing and characterization of C_f/SiC composites

Carbon fiber-reinforced SiC composites were prepared by precursor pyrolysis-hot pressing （PP-HP） and precursor impregnation-pyrolysis （PIP）, respectively. The effect of fabrication methods on the microstructure and mechanical properties of the composites was investigated. It was found that the composite prepared by PP-HP exhibits a brittle fracture behavior, which is mainly ascribed to a strongly bonded fiber/matrix interface and the degradation of the fibers caused by a higher processing temperature. On the contrary, the composite prepared by PIP shows a tough fracture behavior, which could be rationalized on the basis of a weakly bonded fiber/matrix interface as well as a higher strength retention of the fibers. As a result, in comparison with the composite prepared by PP-HP, the composite prepared by PIP achieves better mechanical properties with a flexural strength of 573.4 MPa and a fracture toughness of 17.2 MPa.m^1/2.

单向CF/PA6复合材料性能劣化及老化寿命预测

利用热压成型工艺制备出碳纤维(CF)/尼龙6(PA6)复合材料单向板,并将复合材料试样置于蒸馏水热水浴中,分别在25,60,80℃下进行不同时间的湿热老化,再对湿热老化后复合材料试样进行吸湿测试、三点弯曲测试、微观形貌表征,探究复合材料的吸湿规律、力学性能劣化规律和微观形貌变化,并对复合材料的长期寿命进行预测。结果发现,复合材料在25,60℃下的吸湿行为基本符合Fick扩散定律,而80℃下在老化最后阶段出现了背离Fick扩散定律现象。复合材料的弯曲强度随老化温度、老化时间的增加呈下降趋势,分别在25,60,80℃下老化120 d后,试样弯曲强度分别下降了22.78%,25.0%,26.25%。但是老化温度、老化时间对弯曲弹性模量无显著影响,且CF与PA6树脂之间的界面黏合性能随着温度、时间的增加逐渐变差。以绍兴2021年平均温度作为服役温度,基于加速老化测试模型和阿伦尼乌斯理论建立了CF/PA6复合材料在服役环境下剩余弯曲强度的预测模型,可预测到1 400 d后,CF/PA6复合材料的弯曲强度保留率在64.8%左右。

自成核行为在CF/PPS复合材料中的差异性与普适性

以半结晶高分子为基体的碳纤维增强热塑性复合材料,其基体的结晶行为将受到碳纤维表面性质与热历史的共同影响。当这种材料在经历反复加热冷却的热循环过程时,基体会产生自成核行为,其结晶过程变得更加复杂。通过三种T300级碳纤维分别制备了碳纤维增强聚苯硫醚(CF/PPS)复合材料,并探究了二次熔融温度与CF/PPS复合材料结晶行为的关系,揭示了不同碳纤维表面性质对CF/PPS复合材料自成核行为的影响。在此基础上阐明了CF/PPS复合材料基体自成核与CF异相成核的竞争关系。最后,通过冲压成型制得具有自成核行为的CF/PPS复合材料角片,验证了自成核对于CF/PPS复合材料二次热成型技术的有效性与重要性。

Quantitative Analysis of Composition Change in AZ31 Magnesium Alloy Using CF-LIBS After Laser Material Processing

The concentration of elements in molten metal of AZ31 magnesium alloy after long pulsed Nd：YAG laser processing was quantitatively analyzed by using calibration-free laser-induced breakdown spectroscopy （CF-LIBS）. The composition change in AZ31 magnesium alloy under different laser pulse width was also investigated. The experimental results showed that CF-LIBS can obtain satisfactory quantitative or semi-quantitative results for matrix or major elements, while only qualitative analysis was possible for minor or trace elements. Moreover, it is found that the chemical composition of molten metal will change after laser processing. The concentration of magnesium in molten metal is lower than that present in the base metal. The Mg loss increases with an increase of pulse width in the laser processing. This result shows that the selective vaporization of different elements is affected by the pulse width during laser processing.

Longitudinal changes in body weight of breastfeeding mothers in the first year after delivery and its relationship with human milk composition:a combined longitudinal and cross-sectional cohort study

Objective:Postpartum weight retention(PPWR)is a common problem among women after childbirth.The main objectives of this study are to understand the changes in body weight of breastfeeding mothers during long-term follow-up and preliminarily explore the relationship between maternal body weight and human milk composition,including macronutrients,leptin,and adiponectin.Methods:The study included a longitudinal cohort(122 mothers),and a cross-sectional cohort(37 mothers).The human milk,maternal weight,and dietary surveys were collected in the longitudinal cohort at different follow-up time points(1-14 days postpartum,2-4 months postpartum,5-7 months postpartum,and 12-17 months postpartum).The maternal body weight was analyzed using the responses in the survey questionnaires.A milk analyzer based on the mid-infrared spectroscopy(MIRS)was used to determine milk composition,and nutrition analysis software evaluated dietary intakes.In the cross-sectional cohort,participating mothers were asked to provide blood and human milk samples and pertinent information related to maternal body composition.Maternal body composition was measured by bioelectrical impedance analysis(BIA),while ELISA analyzed leptin and adiponectin in milk and serum.Results:At 5-7 months postpartum,the PPWR of breastfeeding mothers was(2.46±3.59)kg.At 12-17 months postpartum,the PPWR was(0.98±4.06)kg.PPWR was found to be negatively correlated with milk fat content within 14 days postpartum and positively correlated at 2-4 months postpartum.In addition,the maternal weight and body muscle mass were positively correlated with leptin and adiponectin in milk.Plasma leptin was positively correlated with the mother’s body weight,body mass index(BMI),FAT percentage,and body fat mass,while plasma adiponectin did not correlate with any parameter.The results also indicate that the PPWR did not correlate with leptin and adiponectin in plasma or milk.Conclusions:Breastfeeding mothers may retain considerable weight gain one year after delivery.Human milk composition may be related to changes in maternal body weight.Leptin and adiponectin in breast milk and leptin in plasma are associated with the maternal body composition.This study supports the notion that maternal nutritional status may affect offspring health through lactation,and future research should focus on exploring weight management of postpartum mothers.

烯丙基多羟基聚醚改性BMI树脂基复合材料的研究

采用烯丙基多羟基聚醚、ｏ，ｏ′—二烯丙基双酚Ａ对ＢＭＩ进行改性，详细研究了基体树脂及复合材料的性能。结果表明基体树脂具有良好的韧性和耐热性；预浸料可用丙酮溶液进行制作且有良好的铺贴性；玻璃布复合材料具有良好的力学性能。