We put forward a method of fabricating Aluminum(Al)/carbon fibers(CFs) composite sheets by the accumulative roll bonding(ARB) method. The finished Al/CFs composite sheet has CFs and pure Al sheets as sandwich and surf...We put forward a method of fabricating Aluminum(Al)/carbon fibers(CFs) composite sheets by the accumulative roll bonding(ARB) method. The finished Al/CFs composite sheet has CFs and pure Al sheets as sandwich and surface layers. After cross-section observation of the Al/CFs composite sheet, we found that the CFs discretely distributed within the sandwich layer. Besides, the tensile test showed that the contribution of the sandwich CFs layer to tensile strength was less than 11% compared with annealed pure Al sheet. With ex-situ observation of the CFs breakage evolution with-16%,-32%, and-45% rolling reduction during the ARB process, the plastic instability of the Al layer was found to bring shear damages to the CFs. At last, the bridging strengthening mechanism introduced by CFs was sacrificed. We provide new insight into and instruction on Al/CFs composite sheet preparation method and processing parameters.展开更多
Cf/Cu composite was prepared by vacuum melting infiltration. Ti and Cr were doped to the Cu alloy to improve the wettability between Cu and carbon. The microstrueture was investigated by XRD, SEM and EDS. The arc eros...Cf/Cu composite was prepared by vacuum melting infiltration. Ti and Cr were doped to the Cu alloy to improve the wettability between Cu and carbon. The microstrueture was investigated by XRD, SEM and EDS. The arc erosion rate of Cf/Cu composite was investigated in vacuum. The results showed that the Ti and Cr could improve the wettability between Cu and C/C preform and the infiltration ability of Cu into C/ C preform greatly. A TiC interface formed between the fibers and matrix. The good bonding between the fiber and matrix guaranteed that part of the Cu matrix can still be bonded on the fibers even when the material was exposed to the plasma. Consequently, the carbon fibers were protected from the erosion. In comparison, Cu was completely consumed by the arc erosion. Hence, the graphite was eroded and presented a cauliflower-like morphology. Therefore, the prepared C/Cu bad better ability to resist the arc erosion, compared with common Cu-C material.展开更多
The polymer-ceramic composites of epoxy resin (EP) and barium titanate (BT) were prepared. BT powders of different BT particle sizes from 100 nm to 1 μm were used in the preparation. The dielectric properties, such a...The polymer-ceramic composites of epoxy resin (EP) and barium titanate (BT) were prepared. BT powders of different BT particle sizes from 100 nm to 1 μm were used in the preparation. The dielectric properties, such as dielectric constant, dielectric loss and electrical breakdown strength, of the EP/BT composites were studied. The morphology of the composites was characterized by the means of scanning electron microscopy (SEM). The results show that the dielectric constant of the composites is much higher than the epoxy matrix at frequency range from 1 kHz to 10 MHz, and it is also obviously dependent on the size of BT particles. The electrical breakdown strength of the composites decreases with the increase of the BT content. The dependence of electrical breakdown strength on BT particle sizes was also discussed.展开更多
Flower-like copper foam Co_(3)O_(4) catalysts(Co_(3)O_(4)/CF) were prepared by hydrothermal method.The crystalline structure and microscopic morphology of the prepared samples were characterized by using X-ray diffrac...Flower-like copper foam Co_(3)O_(4) catalysts(Co_(3)O_(4)/CF) were prepared by hydrothermal method.The crystalline structure and microscopic morphology of the prepared samples were characterized by using X-ray diffractometer(XRD) and scanning electron microscope(SEM),and the electrochemical properties were investigated by an electrochemical workstation.The experimental results show that the Co_(3)O_(4) catalysts are successfully prepared on the foamed copper support by hydrothermal method,and the material’s morphology is mainly flower cluster.When the current density is 10 mA·cm^(-2),the overpotential value of the Co_(3)O_(4)/CF catalyst is 141 mV,lower than that of blank support.The electrochemical impedance(EIS) spectrum shows that the R_(ct )value of the Co_(3)O_(4)/CF catalyst decreases,and the Coulomb curves of double-layer show that the electrochemically active area of the Co_(3)O_(4)/CF catalyst efficiently increases compared with that of the blank support.Therefore,the as-obtained Co_(3)O_(4)/CF catalyst exhibits a good hydrogen evolution rate,showing great applicability potential in the catalytic electrolysis of water for hydrogen production.展开更多
Flame retardant epoxy resins were prepared by a simple mixed method using ammonium aluminum carbonate hydroxy hydrate （AACHH） as a halogen-free flame retardant. The prepared samples were characterized by X-ray diffr...Flame retardant epoxy resins were prepared by a simple mixed method using ammonium aluminum carbonate hydroxy hydrate （AACHH） as a halogen-free flame retardant. The prepared samples were characterized by X-ray diffraction, thermogravimetric and differential scanning calorimetry, scanning electron microscope and limiting oxygen index（LOI） experiments. Effects of AACHH content on LOI of epoxy resins/AACHH composite and flame retardant mechanism were investigated and discussed. Results show that AACHH exhibites excellent flame-retardant properties in epoxy resin（EP）. When the content of AACHH was 47.4%, the LOI of EP reached 32.2%. Moreover, the initial and terminal decomposition temperature of EP increased by 48 ℃ and 40 ℃, respectively. The flame retarded mechanism of AACHH is due to the synergic flame retardant effects of diluting, cooling, decomposition resisting and obstructing.展开更多
To investigate the ballistic performance and damage characteristics of quasi threedimensional（3D） needle-punched Cf/SiC composites prepared by chemical vapor infiltration（CVI）,penetration experiments were conducte...To investigate the ballistic performance and damage characteristics of quasi threedimensional（3D） needle-punched Cf/SiC composites prepared by chemical vapor infiltration（CVI）,penetration experiments were conducted by using 7.62 mm armor piercing incendiary（API）.Macro and micro fracture morphologies were then observed on recycled targets.The results show that the protection coefficient of 3D Cf/SiC composites is 2.54.High porosity and many micro thermal stress cracks may directly lead to the lower ballistic performance.Flat fracture morphology was observed on the crater surface.The low dynamic fracture strength along layer direction may be attributed to the voids and microcracks caused by residual thermal stress.The damage characteristics of Cf/Si C composites include matrix cracking,fiber bundle cracking,interfacial debonding,fiber fracture,and fiber bundle pull-out.And interfacial debonding and fiber fracture may play major roles in energy absorption.展开更多
Carbon fibers （CFs） were surface treated with air-oxidation, rare earths （RE） after air-oxidation, and rare earths, respectively. Erichsen test was conducted to study the interfacial adhesion of PTFE composites fi...Carbon fibers （CFs） were surface treated with air-oxidation, rare earths （RE） after air-oxidation, and rare earths, respectively. Erichsen test was conducted to study the interfacial adhesion of PTFE composites filled with carbon fibers treated with different treatment methods. Tribological properties of the PTFE composites, sliding against GCr15 steel under water-lubricated condition, were investigated on a reciprocating ball-on-disk UMT-2MT tribometer. The worn surfaces of the composites were examined using scanning electron microscopy. Experimental results reveal that RE treatment is superior to air oxidation in promoting tribological properties of CF reinforced PTFE （CF/PTFE） composite. The friction and wear properties of PTFE composite filled with RE treated CF are the best of the PTFE composites. RE treatment is more effective than air oxidation to improve the tribological properties of CF/PTFE composite owing to the effective improvement of interfacial adhesion between carbon fibers and PTFE matrix.展开更多
基金Supported by Innovation and Technology Fund (No.ITP/045/19AP)Commercial Research&Development (CRD) Funding Supported by Hong Kong Productivity Council (No.10008787)。
文摘We put forward a method of fabricating Aluminum(Al)/carbon fibers(CFs) composite sheets by the accumulative roll bonding(ARB) method. The finished Al/CFs composite sheet has CFs and pure Al sheets as sandwich and surface layers. After cross-section observation of the Al/CFs composite sheet, we found that the CFs discretely distributed within the sandwich layer. Besides, the tensile test showed that the contribution of the sandwich CFs layer to tensile strength was less than 11% compared with annealed pure Al sheet. With ex-situ observation of the CFs breakage evolution with-16%,-32%, and-45% rolling reduction during the ARB process, the plastic instability of the Al layer was found to bring shear damages to the CFs. At last, the bridging strengthening mechanism introduced by CFs was sacrificed. We provide new insight into and instruction on Al/CFs composite sheet preparation method and processing parameters.
基金Funded by the National Natural Science Foundation of China(No.51002121)Postgraduate Technology Innovation Project of Taiyuan University of Science and Technology(No.20134008)
文摘Cf/Cu composite was prepared by vacuum melting infiltration. Ti and Cr were doped to the Cu alloy to improve the wettability between Cu and carbon. The microstrueture was investigated by XRD, SEM and EDS. The arc erosion rate of Cf/Cu composite was investigated in vacuum. The results showed that the Ti and Cr could improve the wettability between Cu and C/C preform and the infiltration ability of Cu into C/ C preform greatly. A TiC interface formed between the fibers and matrix. The good bonding between the fiber and matrix guaranteed that part of the Cu matrix can still be bonded on the fibers even when the material was exposed to the plasma. Consequently, the carbon fibers were protected from the erosion. In comparison, Cu was completely consumed by the arc erosion. Hence, the graphite was eroded and presented a cauliflower-like morphology. Therefore, the prepared C/Cu bad better ability to resist the arc erosion, compared with common Cu-C material.
文摘The polymer-ceramic composites of epoxy resin (EP) and barium titanate (BT) were prepared. BT powders of different BT particle sizes from 100 nm to 1 μm were used in the preparation. The dielectric properties, such as dielectric constant, dielectric loss and electrical breakdown strength, of the EP/BT composites were studied. The morphology of the composites was characterized by the means of scanning electron microscopy (SEM). The results show that the dielectric constant of the composites is much higher than the epoxy matrix at frequency range from 1 kHz to 10 MHz, and it is also obviously dependent on the size of BT particles. The electrical breakdown strength of the composites decreases with the increase of the BT content. The dependence of electrical breakdown strength on BT particle sizes was also discussed.
基金Funded by the National Natural Science Foundation of China(No.51474170)the Foundation of Shaanxi Educational Committee(No.17JK0395)the Xi’an Science and Technology Committee Program(No.GXYD9.2)。
文摘Flower-like copper foam Co_(3)O_(4) catalysts(Co_(3)O_(4)/CF) were prepared by hydrothermal method.The crystalline structure and microscopic morphology of the prepared samples were characterized by using X-ray diffractometer(XRD) and scanning electron microscope(SEM),and the electrochemical properties were investigated by an electrochemical workstation.The experimental results show that the Co_(3)O_(4) catalysts are successfully prepared on the foamed copper support by hydrothermal method,and the material’s morphology is mainly flower cluster.When the current density is 10 mA·cm^(-2),the overpotential value of the Co_(3)O_(4)/CF catalyst is 141 mV,lower than that of blank support.The electrochemical impedance(EIS) spectrum shows that the R_(ct )value of the Co_(3)O_(4)/CF catalyst decreases,and the Coulomb curves of double-layer show that the electrochemically active area of the Co_(3)O_(4)/CF catalyst efficiently increases compared with that of the blank support.Therefore,the as-obtained Co_(3)O_(4)/CF catalyst exhibits a good hydrogen evolution rate,showing great applicability potential in the catalytic electrolysis of water for hydrogen production.
基金Funded by the Defense Preresearch Project of the Eleventh-Five-Year-Plan of China(No.51312040404)
文摘Flame retardant epoxy resins were prepared by a simple mixed method using ammonium aluminum carbonate hydroxy hydrate （AACHH） as a halogen-free flame retardant. The prepared samples were characterized by X-ray diffraction, thermogravimetric and differential scanning calorimetry, scanning electron microscope and limiting oxygen index（LOI） experiments. Effects of AACHH content on LOI of epoxy resins/AACHH composite and flame retardant mechanism were investigated and discussed. Results show that AACHH exhibites excellent flame-retardant properties in epoxy resin（EP）. When the content of AACHH was 47.4%, the LOI of EP reached 32.2%. Moreover, the initial and terminal decomposition temperature of EP increased by 48 ℃ and 40 ℃, respectively. The flame retarded mechanism of AACHH is due to the synergic flame retardant effects of diluting, cooling, decomposition resisting and obstructing.
基金Funded by the National Natural Science Foundation of China(No.51271036)
文摘To investigate the ballistic performance and damage characteristics of quasi threedimensional（3D） needle-punched Cf/SiC composites prepared by chemical vapor infiltration（CVI）,penetration experiments were conducted by using 7.62 mm armor piercing incendiary（API）.Macro and micro fracture morphologies were then observed on recycled targets.The results show that the protection coefficient of 3D Cf/SiC composites is 2.54.High porosity and many micro thermal stress cracks may directly lead to the lower ballistic performance.Flat fracture morphology was observed on the crater surface.The low dynamic fracture strength along layer direction may be attributed to the voids and microcracks caused by residual thermal stress.The damage characteristics of Cf/Si C composites include matrix cracking,fiber bundle cracking,interfacial debonding,fiber fracture,and fiber bundle pull-out.And interfacial debonding and fiber fracture may play major roles in energy absorption.
基金Project supported bythe National Natural Science Foundation of China (50275093)
文摘Carbon fibers （CFs） were surface treated with air-oxidation, rare earths （RE） after air-oxidation, and rare earths, respectively. Erichsen test was conducted to study the interfacial adhesion of PTFE composites filled with carbon fibers treated with different treatment methods. Tribological properties of the PTFE composites, sliding against GCr15 steel under water-lubricated condition, were investigated on a reciprocating ball-on-disk UMT-2MT tribometer. The worn surfaces of the composites were examined using scanning electron microscopy. Experimental results reveal that RE treatment is superior to air oxidation in promoting tribological properties of CF reinforced PTFE （CF/PTFE） composite. The friction and wear properties of PTFE composite filled with RE treated CF are the best of the PTFE composites. RE treatment is more effective than air oxidation to improve the tribological properties of CF/PTFE composite owing to the effective improvement of interfacial adhesion between carbon fibers and PTFE matrix.