We put forward a method of fabricating Aluminum(Al)/carbon fibers(CFs) composite sheets by the accumulative roll bonding(ARB) method. The finished Al/CFs composite sheet has CFs and pure Al sheets as sandwich and surf...We put forward a method of fabricating Aluminum(Al)/carbon fibers(CFs) composite sheets by the accumulative roll bonding(ARB) method. The finished Al/CFs composite sheet has CFs and pure Al sheets as sandwich and surface layers. After cross-section observation of the Al/CFs composite sheet, we found that the CFs discretely distributed within the sandwich layer. Besides, the tensile test showed that the contribution of the sandwich CFs layer to tensile strength was less than 11% compared with annealed pure Al sheet. With ex-situ observation of the CFs breakage evolution with-16%,-32%, and-45% rolling reduction during the ARB process, the plastic instability of the Al layer was found to bring shear damages to the CFs. At last, the bridging strengthening mechanism introduced by CFs was sacrificed. We provide new insight into and instruction on Al/CFs composite sheet preparation method and processing parameters.展开更多
The seismic performance of a caisson structure under two types of models with a saturated sandy foundation(CSS)and an expanded polystyrene(EPS)composite soil foundation(CES)are studied using shaking table tests.The ma...The seismic performance of a caisson structure under two types of models with a saturated sandy foundation(CSS)and an expanded polystyrene(EPS)composite soil foundation(CES)are studied using shaking table tests.The macro phenomena of the two different foundation models are described and analyzed.The effects of the replacement of EPS composite soil on seismic-induced liquefaction of backfill and the dynamic performance of a caisson structure are evaluated in detail.The results show that the excess pore water pressure generation in the CES is significantly slower than that in the CSS during the shaking.The dynamic earth pressure acting on the caisson has a triangular shape.The response of horizontal acceleration,displacement,settlement,and rotation angle of the caisson in the CES is smaller than that in the CSS,which means the caisson in the CES has a better seismic performance.Furthermore,the out-of-phase phenomenon between dynamic earth thrust and inertial force in the CES is more obvious than that in the CSS,which is beneficial to reduce the lateral force and improve the stability of the caisson structure.展开更多
The polymer-ceramic composites of epoxy resin (EP) and barium titanate (BT) were prepared. BT powders of different BT particle sizes from 100 nm to 1 μm were used in the preparation. The dielectric properties, such a...The polymer-ceramic composites of epoxy resin (EP) and barium titanate (BT) were prepared. BT powders of different BT particle sizes from 100 nm to 1 μm were used in the preparation. The dielectric properties, such as dielectric constant, dielectric loss and electrical breakdown strength, of the EP/BT composites were studied. The morphology of the composites was characterized by the means of scanning electron microscopy (SEM). The results show that the dielectric constant of the composites is much higher than the epoxy matrix at frequency range from 1 kHz to 10 MHz, and it is also obviously dependent on the size of BT particles. The electrical breakdown strength of the composites decreases with the increase of the BT content. The dependence of electrical breakdown strength on BT particle sizes was also discussed.展开更多
Flower-like copper foam Co_(3)O_(4) catalysts(Co_(3)O_(4)/CF) were prepared by hydrothermal method.The crystalline structure and microscopic morphology of the prepared samples were characterized by using X-ray diffrac...Flower-like copper foam Co_(3)O_(4) catalysts(Co_(3)O_(4)/CF) were prepared by hydrothermal method.The crystalline structure and microscopic morphology of the prepared samples were characterized by using X-ray diffractometer(XRD) and scanning electron microscope(SEM),and the electrochemical properties were investigated by an electrochemical workstation.The experimental results show that the Co_(3)O_(4) catalysts are successfully prepared on the foamed copper support by hydrothermal method,and the material’s morphology is mainly flower cluster.When the current density is 10 mA·cm^(-2),the overpotential value of the Co_(3)O_(4)/CF catalyst is 141 mV,lower than that of blank support.The electrochemical impedance(EIS) spectrum shows that the R_(ct )value of the Co_(3)O_(4)/CF catalyst decreases,and the Coulomb curves of double-layer show that the electrochemically active area of the Co_(3)O_(4)/CF catalyst efficiently increases compared with that of the blank support.Therefore,the as-obtained Co_(3)O_(4)/CF catalyst exhibits a good hydrogen evolution rate,showing great applicability potential in the catalytic electrolysis of water for hydrogen production.展开更多
Extracellular polymeric substances(EPS)constitutes crucial elements within bacterial biofilms,facili-tating accelerated antimicrobial resistance and conferring defense against the host's immune cells.Developing pr...Extracellular polymeric substances(EPS)constitutes crucial elements within bacterial biofilms,facili-tating accelerated antimicrobial resistance and conferring defense against the host's immune cells.Developing precise and effective antibiofilm approaches and strategies,tailored to the specific charac-teristics of EPS composition,can offer valuable insights for the creation of novel antimicrobial drugs.This,in turn,holds the potential to mitigate the alarming issue of bacterial drug resistance.Current analysis of EPS compositions relies heavily on colorimetric approaches with a significant bias,which is likely due to the selection of a standard compound and the cross-interference of various EPS compounds.Considering the pivotal role of EPS in biofilm functionality,it is imperative for EPS research to delve deeper into the analysis of intricate compositions,moving beyond the current focus on polymeric materials.This ne-cessitates a shift from heavy reliance on colorimetric analytic methods to more comprehensive and nuanced analytical approaches.In this study,we have provided a comprehensive summary of existing analytical methods utilized in the characterization of EPS compositions.Additionally,novel strategies aimed at targeting EPS to enhance biofilm penetration were explored,with a specific focus on high-lighting the limitations associated with colorimetric methods.Furthermore,we have outlined the challenges faced in identifying additional components of EPS and propose a prospective research plan to address these challenges.This review has the potential to guide future researchers in the search for novel compounds capable of suppressing EPS,thereby inhibiting biofilm formation.This insight opens up a new avenue for exploration within this research domain.展开更多
To investigate the ballistic performance and damage characteristics of quasi threedimensional（3D） needle-punched Cf/SiC composites prepared by chemical vapor infiltration（CVI）,penetration experiments were conducte...To investigate the ballistic performance and damage characteristics of quasi threedimensional（3D） needle-punched Cf/SiC composites prepared by chemical vapor infiltration（CVI）,penetration experiments were conducted by using 7.62 mm armor piercing incendiary（API）.Macro and micro fracture morphologies were then observed on recycled targets.The results show that the protection coefficient of 3D Cf/SiC composites is 2.54.High porosity and many micro thermal stress cracks may directly lead to the lower ballistic performance.Flat fracture morphology was observed on the crater surface.The low dynamic fracture strength along layer direction may be attributed to the voids and microcracks caused by residual thermal stress.The damage characteristics of Cf/Si C composites include matrix cracking,fiber bundle cracking,interfacial debonding,fiber fracture,and fiber bundle pull-out.And interfacial debonding and fiber fracture may play major roles in energy absorption.展开更多
Flame retardant epoxy resins were prepared by a simple mixed method using ammonium aluminum carbonate hydroxy hydrate （AACHH） as a halogen-free flame retardant. The prepared samples were characterized by X-ray diffr...Flame retardant epoxy resins were prepared by a simple mixed method using ammonium aluminum carbonate hydroxy hydrate （AACHH） as a halogen-free flame retardant. The prepared samples were characterized by X-ray diffraction, thermogravimetric and differential scanning calorimetry, scanning electron microscope and limiting oxygen index（LOI） experiments. Effects of AACHH content on LOI of epoxy resins/AACHH composite and flame retardant mechanism were investigated and discussed. Results show that AACHH exhibites excellent flame-retardant properties in epoxy resin（EP）. When the content of AACHH was 47.4%, the LOI of EP reached 32.2%. Moreover, the initial and terminal decomposition temperature of EP increased by 48 ℃ and 40 ℃, respectively. The flame retarded mechanism of AACHH is due to the synergic flame retardant effects of diluting, cooling, decomposition resisting and obstructing.展开更多
基金Supported by Innovation and Technology Fund (No.ITP/045/19AP)Commercial Research&Development (CRD) Funding Supported by Hong Kong Productivity Council (No.10008787)。
文摘We put forward a method of fabricating Aluminum(Al)/carbon fibers(CFs) composite sheets by the accumulative roll bonding(ARB) method. The finished Al/CFs composite sheet has CFs and pure Al sheets as sandwich and surface layers. After cross-section observation of the Al/CFs composite sheet, we found that the CFs discretely distributed within the sandwich layer. Besides, the tensile test showed that the contribution of the sandwich CFs layer to tensile strength was less than 11% compared with annealed pure Al sheet. With ex-situ observation of the CFs breakage evolution with-16%,-32%, and-45% rolling reduction during the ARB process, the plastic instability of the Al layer was found to bring shear damages to the CFs. At last, the bridging strengthening mechanism introduced by CFs was sacrificed. We provide new insight into and instruction on Al/CFs composite sheet preparation method and processing parameters.
基金National Natural Science Foundation of China under Grant Nos. 52178336 and 52108324Natural Science Research Project of Colleges and Universities in Jiangsu Province of China under Grant No. 18KJA560002+1 种基金the Middle-Aged&Young Science Leaders of Qinglan Project of Universities in Jiangsu Province of ChinaPostgraduate Research&Practice Innovation Program in Jiangsu Province of China under Grant No. KYCX24_1585
文摘The seismic performance of a caisson structure under two types of models with a saturated sandy foundation(CSS)and an expanded polystyrene(EPS)composite soil foundation(CES)are studied using shaking table tests.The macro phenomena of the two different foundation models are described and analyzed.The effects of the replacement of EPS composite soil on seismic-induced liquefaction of backfill and the dynamic performance of a caisson structure are evaluated in detail.The results show that the excess pore water pressure generation in the CES is significantly slower than that in the CSS during the shaking.The dynamic earth pressure acting on the caisson has a triangular shape.The response of horizontal acceleration,displacement,settlement,and rotation angle of the caisson in the CES is smaller than that in the CSS,which means the caisson in the CES has a better seismic performance.Furthermore,the out-of-phase phenomenon between dynamic earth thrust and inertial force in the CES is more obvious than that in the CSS,which is beneficial to reduce the lateral force and improve the stability of the caisson structure.
文摘The polymer-ceramic composites of epoxy resin (EP) and barium titanate (BT) were prepared. BT powders of different BT particle sizes from 100 nm to 1 μm were used in the preparation. The dielectric properties, such as dielectric constant, dielectric loss and electrical breakdown strength, of the EP/BT composites were studied. The morphology of the composites was characterized by the means of scanning electron microscopy (SEM). The results show that the dielectric constant of the composites is much higher than the epoxy matrix at frequency range from 1 kHz to 10 MHz, and it is also obviously dependent on the size of BT particles. The electrical breakdown strength of the composites decreases with the increase of the BT content. The dependence of electrical breakdown strength on BT particle sizes was also discussed.
基金Funded by the National Natural Science Foundation of China(No.51474170)the Foundation of Shaanxi Educational Committee(No.17JK0395)the Xi’an Science and Technology Committee Program(No.GXYD9.2)。
文摘Flower-like copper foam Co_(3)O_(4) catalysts(Co_(3)O_(4)/CF) were prepared by hydrothermal method.The crystalline structure and microscopic morphology of the prepared samples were characterized by using X-ray diffractometer(XRD) and scanning electron microscope(SEM),and the electrochemical properties were investigated by an electrochemical workstation.The experimental results show that the Co_(3)O_(4) catalysts are successfully prepared on the foamed copper support by hydrothermal method,and the material’s morphology is mainly flower cluster.When the current density is 10 mA·cm^(-2),the overpotential value of the Co_(3)O_(4)/CF catalyst is 141 mV,lower than that of blank support.The electrochemical impedance(EIS) spectrum shows that the R_(ct )value of the Co_(3)O_(4)/CF catalyst decreases,and the Coulomb curves of double-layer show that the electrochemically active area of the Co_(3)O_(4)/CF catalyst efficiently increases compared with that of the blank support.Therefore,the as-obtained Co_(3)O_(4)/CF catalyst exhibits a good hydrogen evolution rate,showing great applicability potential in the catalytic electrolysis of water for hydrogen production.
基金funded by the National Natural Science Foundation of China(Grant Nos.:81803812,81803237).
文摘Extracellular polymeric substances(EPS)constitutes crucial elements within bacterial biofilms,facili-tating accelerated antimicrobial resistance and conferring defense against the host's immune cells.Developing precise and effective antibiofilm approaches and strategies,tailored to the specific charac-teristics of EPS composition,can offer valuable insights for the creation of novel antimicrobial drugs.This,in turn,holds the potential to mitigate the alarming issue of bacterial drug resistance.Current analysis of EPS compositions relies heavily on colorimetric approaches with a significant bias,which is likely due to the selection of a standard compound and the cross-interference of various EPS compounds.Considering the pivotal role of EPS in biofilm functionality,it is imperative for EPS research to delve deeper into the analysis of intricate compositions,moving beyond the current focus on polymeric materials.This ne-cessitates a shift from heavy reliance on colorimetric analytic methods to more comprehensive and nuanced analytical approaches.In this study,we have provided a comprehensive summary of existing analytical methods utilized in the characterization of EPS compositions.Additionally,novel strategies aimed at targeting EPS to enhance biofilm penetration were explored,with a specific focus on high-lighting the limitations associated with colorimetric methods.Furthermore,we have outlined the challenges faced in identifying additional components of EPS and propose a prospective research plan to address these challenges.This review has the potential to guide future researchers in the search for novel compounds capable of suppressing EPS,thereby inhibiting biofilm formation.This insight opens up a new avenue for exploration within this research domain.
基金Funded by the National Natural Science Foundation of China(No.51271036)
文摘To investigate the ballistic performance and damage characteristics of quasi threedimensional（3D） needle-punched Cf/SiC composites prepared by chemical vapor infiltration（CVI）,penetration experiments were conducted by using 7.62 mm armor piercing incendiary（API）.Macro and micro fracture morphologies were then observed on recycled targets.The results show that the protection coefficient of 3D Cf/SiC composites is 2.54.High porosity and many micro thermal stress cracks may directly lead to the lower ballistic performance.Flat fracture morphology was observed on the crater surface.The low dynamic fracture strength along layer direction may be attributed to the voids and microcracks caused by residual thermal stress.The damage characteristics of Cf/Si C composites include matrix cracking,fiber bundle cracking,interfacial debonding,fiber fracture,and fiber bundle pull-out.And interfacial debonding and fiber fracture may play major roles in energy absorption.
基金Funded by the Defense Preresearch Project of the Eleventh-Five-Year-Plan of China(No.51312040404)
文摘Flame retardant epoxy resins were prepared by a simple mixed method using ammonium aluminum carbonate hydroxy hydrate （AACHH） as a halogen-free flame retardant. The prepared samples were characterized by X-ray diffraction, thermogravimetric and differential scanning calorimetry, scanning electron microscope and limiting oxygen index（LOI） experiments. Effects of AACHH content on LOI of epoxy resins/AACHH composite and flame retardant mechanism were investigated and discussed. Results show that AACHH exhibites excellent flame-retardant properties in epoxy resin（EP）. When the content of AACHH was 47.4%, the LOI of EP reached 32.2%. Moreover, the initial and terminal decomposition temperature of EP increased by 48 ℃ and 40 ℃, respectively. The flame retarded mechanism of AACHH is due to the synergic flame retardant effects of diluting, cooling, decomposition resisting and obstructing.