We put forward a method of fabricating Aluminum(Al)/carbon fibers(CFs) composite sheets by the accumulative roll bonding(ARB) method. The finished Al/CFs composite sheet has CFs and pure Al sheets as sandwich and surf...We put forward a method of fabricating Aluminum(Al)/carbon fibers(CFs) composite sheets by the accumulative roll bonding(ARB) method. The finished Al/CFs composite sheet has CFs and pure Al sheets as sandwich and surface layers. After cross-section observation of the Al/CFs composite sheet, we found that the CFs discretely distributed within the sandwich layer. Besides, the tensile test showed that the contribution of the sandwich CFs layer to tensile strength was less than 11% compared with annealed pure Al sheet. With ex-situ observation of the CFs breakage evolution with-16%,-32%, and-45% rolling reduction during the ARB process, the plastic instability of the Al layer was found to bring shear damages to the CFs. At last, the bridging strengthening mechanism introduced by CFs was sacrificed. We provide new insight into and instruction on Al/CFs composite sheet preparation method and processing parameters.展开更多
In-situ consolidation forming of high-performance thermoplastic composites by Automated Fiber Placement(AFP)is of significant interest in aerospace.During the laying process,the heating temperature has a great influen...In-situ consolidation forming of high-performance thermoplastic composites by Automated Fiber Placement(AFP)is of significant interest in aerospace.During the laying process,the heating temperature has a great influence on the quality of the formed components.A threedimensional heat transfer finite element model of Carbon Fiber(CF)/Polyether Ether Ketone(PEEK)heated by Slit Structure Nozzle Hot Gas Torch(SSNHGT)assisted AFP is proposed.The influence of gas flow rate,heat transfer distance,and laying speed on heating temperature is analysed.The results show that the overall temperature increases and then decreases as the gas flow rate increases.With the increase in heat transfer distance and laying speed,the overall temperature decreases.Meanwhile,the gas flow rate has the greatest influence on the temperature of CF/PEEK being heated,followed by the laying speed and finally the heat transfer distance.Furthermore,the model can also be extended to other fiber-reinforced polymer composites formed by hot gas torch assisted AFP,which can guide the optimization of process parameters for subsequent heating temperature control.展开更多
To investigate the ballistic performance and damage characteristics of quasi threedimensional（3D） needle-punched Cf/SiC composites prepared by chemical vapor infiltration（CVI）,penetration experiments were conducte...To investigate the ballistic performance and damage characteristics of quasi threedimensional（3D） needle-punched Cf/SiC composites prepared by chemical vapor infiltration（CVI）,penetration experiments were conducted by using 7.62 mm armor piercing incendiary（API）.Macro and micro fracture morphologies were then observed on recycled targets.The results show that the protection coefficient of 3D Cf/SiC composites is 2.54.High porosity and many micro thermal stress cracks may directly lead to the lower ballistic performance.Flat fracture morphology was observed on the crater surface.The low dynamic fracture strength along layer direction may be attributed to the voids and microcracks caused by residual thermal stress.The damage characteristics of Cf/Si C composites include matrix cracking,fiber bundle cracking,interfacial debonding,fiber fracture,and fiber bundle pull-out.And interfacial debonding and fiber fracture may play major roles in energy absorption.展开更多
基金Supported by Innovation and Technology Fund (No.ITP/045/19AP)Commercial Research&Development (CRD) Funding Supported by Hong Kong Productivity Council (No.10008787)。
文摘We put forward a method of fabricating Aluminum(Al)/carbon fibers(CFs) composite sheets by the accumulative roll bonding(ARB) method. The finished Al/CFs composite sheet has CFs and pure Al sheets as sandwich and surface layers. After cross-section observation of the Al/CFs composite sheet, we found that the CFs discretely distributed within the sandwich layer. Besides, the tensile test showed that the contribution of the sandwich CFs layer to tensile strength was less than 11% compared with annealed pure Al sheet. With ex-situ observation of the CFs breakage evolution with-16%,-32%, and-45% rolling reduction during the ARB process, the plastic instability of the Al layer was found to bring shear damages to the CFs. At last, the bridging strengthening mechanism introduced by CFs was sacrificed. We provide new insight into and instruction on Al/CFs composite sheet preparation method and processing parameters.
基金co-supported by the National Natural Science Foundation of China(No.52205460)the Heilongjiang Provincial Natural Science Foundation of China(No.LH2023E041)the China Scholarship Council(CSC)to study abroad at the Nanyang Technological University.
文摘In-situ consolidation forming of high-performance thermoplastic composites by Automated Fiber Placement(AFP)is of significant interest in aerospace.During the laying process,the heating temperature has a great influence on the quality of the formed components.A threedimensional heat transfer finite element model of Carbon Fiber(CF)/Polyether Ether Ketone(PEEK)heated by Slit Structure Nozzle Hot Gas Torch(SSNHGT)assisted AFP is proposed.The influence of gas flow rate,heat transfer distance,and laying speed on heating temperature is analysed.The results show that the overall temperature increases and then decreases as the gas flow rate increases.With the increase in heat transfer distance and laying speed,the overall temperature decreases.Meanwhile,the gas flow rate has the greatest influence on the temperature of CF/PEEK being heated,followed by the laying speed and finally the heat transfer distance.Furthermore,the model can also be extended to other fiber-reinforced polymer composites formed by hot gas torch assisted AFP,which can guide the optimization of process parameters for subsequent heating temperature control.
基金Funded by the National Natural Science Foundation of China(No.51271036)
文摘To investigate the ballistic performance and damage characteristics of quasi threedimensional（3D） needle-punched Cf/SiC composites prepared by chemical vapor infiltration（CVI）,penetration experiments were conducted by using 7.62 mm armor piercing incendiary（API）.Macro and micro fracture morphologies were then observed on recycled targets.The results show that the protection coefficient of 3D Cf/SiC composites is 2.54.High porosity and many micro thermal stress cracks may directly lead to the lower ballistic performance.Flat fracture morphology was observed on the crater surface.The low dynamic fracture strength along layer direction may be attributed to the voids and microcracks caused by residual thermal stress.The damage characteristics of Cf/Si C composites include matrix cracking,fiber bundle cracking,interfacial debonding,fiber fracture,and fiber bundle pull-out.And interfacial debonding and fiber fracture may play major roles in energy absorption.