The hydraulic concrete durability under the alternation of freeze-thaw and carbonation has been systematically investigated in this work, where both the micro part and the microscopic characteristics of concrete inter...The hydraulic concrete durability under the alternation of freeze-thaw and carbonation has been systematically investigated in this work, where both the micro part and the microscopic characteristics of concrete interface were analyzed based on computed tomography（CT） test and scanning electron microscopy（SEM）. Average CT numbers of each section, declined at water-cement ratio of 0.35, increased at 0.45, and changed a little at 0.55. The specimen in the absence of fly ash exhibited less types of hydration products and the surface was observed to be a needle-like ettringite, with a relatively dense overall structure. However, with the increase of fly ash content, pores and micro-cracks of specimen structure increased. Hexagonal flake calcium hydroxide, present in the specimen after the first carbonation, was negligible in the test pieces of the first freezethaw where the main hydration products were ettringite and calcium silicate gel. Regular hexagonal plates of calcium hydroxide exhibited in the interior of the specimen in which charring first occurred but calcium hydroxide rarely existed in the interior of the specimen in which freeze-thaw first occurred.展开更多
In Oxy-fuel circulating fluidized bed,the residual Ca O particles may react with high concentration of CO2 in flue gas to form bonded deposit on heat transfer surfaces in backpass when limestone is used as a sorbent t...In Oxy-fuel circulating fluidized bed,the residual Ca O particles may react with high concentration of CO2 in flue gas to form bonded deposit on heat transfer surfaces in backpass when limestone is used as a sorbent to capture SO2.In this paper,experiments were designed on ash deposition in a bench-scale fluidized bed under oxy-fuel and air atmosphere. A novel ash deposit sampling probe was used to simulate the tubes of tail surfaces.The chemical composition of fly ash and ash deposit from both air-firing and oxy-fuel firing cases were analyzed by Inductively Coupled Plasma-Atomic Emission Spectrometry( ICP-AES) and Scanning Electron Microscopy( SEM),respectively. The degrees of carbonation reaction of ash deposits were measured by Thermo Gravimetric Analysis. The results showed that there are distinct differences in fly ash deposition rate between oxy-fuel and air firing cases,and oxy-fuel combustion with limestone addition can affect chemical composition of fly ash and ash deposit,especially for elements of Ca,Na,K,and S. However,the carbonation reaction degree of ash deposits is found weak,which is due to the relatively low Ca O content in ash deposit or not long enough of the sampling time.展开更多
In response to escalating challenges in energy conservation and emission reduction,this study delves into the complexities of heat transfer in two-phase flows and adjustments to combustion processes within coal-fired ...In response to escalating challenges in energy conservation and emission reduction,this study delves into the complexities of heat transfer in two-phase flows and adjustments to combustion processes within coal-fired boilers.Utilizing a fusion of hybrid modeling and automation technologies,we develop soft measurement models for key combustion parameters,such as the net calorific value of coal,flue gas oxygen content,and fly ash carbon content,within theDistributedControl System(DCS).Validated with performance test data,thesemodels exhibit controlled root mean square error(RMSE)and maximum absolute error(MAXE)values,both within the range of 0.203.Integrated into their respective automatic control systems,thesemodels optimize two-phase flow heat transfer,finetune combustion conditions,and mitigate incomplete combustion.Furthermore,this paper conducts an in-depth exploration of the generationmechanismof nitrogen oxides(NOx)and low oxygen emission reduction technology in coal-fired boilers,demonstrating a substantial reduction in furnace exit NOx generation by 30%to 40%and the power supply coal consumption decreased by 1.62 g/(kW h).The research outcomes highlight the model’s rapid responsiveness,enabling prompt reflection of transient variations in various economic indicator parameters.This provides a more effective means for real-time monitoring of crucial variables in coal-fired boilers and facilitates timely combustion adjustments,underscoring notable achievements in boiler combustion.The research not only provides valuable and practical insights into the intricacies of two-phase flow heat transfer and heat exchange but also establishes a pioneering methodology for tackling industry challenges.展开更多
基金Funded by the National Natural Science Foundation of China(Nos.51279017,51539002 and 51139001)China Postdoctoral Science Foundation Funded Project(No.2015M582213)
文摘The hydraulic concrete durability under the alternation of freeze-thaw and carbonation has been systematically investigated in this work, where both the micro part and the microscopic characteristics of concrete interface were analyzed based on computed tomography（CT） test and scanning electron microscopy（SEM）. Average CT numbers of each section, declined at water-cement ratio of 0.35, increased at 0.45, and changed a little at 0.55. The specimen in the absence of fly ash exhibited less types of hydration products and the surface was observed to be a needle-like ettringite, with a relatively dense overall structure. However, with the increase of fly ash content, pores and micro-cracks of specimen structure increased. Hexagonal flake calcium hydroxide, present in the specimen after the first carbonation, was negligible in the test pieces of the first freezethaw where the main hydration products were ettringite and calcium silicate gel. Regular hexagonal plates of calcium hydroxide exhibited in the interior of the specimen in which charring first occurred but calcium hydroxide rarely existed in the interior of the specimen in which freeze-thaw first occurred.
基金Sponsored by the Foundation for Innovative Research Groups of the National Natural Science Foundation of China(Grant No.51421063)the Key Technologies Research and Development Program of China(Grant No.2012BAA02B01-04)the Collaborative Innovation Center of Clean Coal Power Plant with Poly-generation
文摘In Oxy-fuel circulating fluidized bed,the residual Ca O particles may react with high concentration of CO2 in flue gas to form bonded deposit on heat transfer surfaces in backpass when limestone is used as a sorbent to capture SO2.In this paper,experiments were designed on ash deposition in a bench-scale fluidized bed under oxy-fuel and air atmosphere. A novel ash deposit sampling probe was used to simulate the tubes of tail surfaces.The chemical composition of fly ash and ash deposit from both air-firing and oxy-fuel firing cases were analyzed by Inductively Coupled Plasma-Atomic Emission Spectrometry( ICP-AES) and Scanning Electron Microscopy( SEM),respectively. The degrees of carbonation reaction of ash deposits were measured by Thermo Gravimetric Analysis. The results showed that there are distinct differences in fly ash deposition rate between oxy-fuel and air firing cases,and oxy-fuel combustion with limestone addition can affect chemical composition of fly ash and ash deposit,especially for elements of Ca,Na,K,and S. However,the carbonation reaction degree of ash deposits is found weak,which is due to the relatively low Ca O content in ash deposit or not long enough of the sampling time.
文摘In response to escalating challenges in energy conservation and emission reduction,this study delves into the complexities of heat transfer in two-phase flows and adjustments to combustion processes within coal-fired boilers.Utilizing a fusion of hybrid modeling and automation technologies,we develop soft measurement models for key combustion parameters,such as the net calorific value of coal,flue gas oxygen content,and fly ash carbon content,within theDistributedControl System(DCS).Validated with performance test data,thesemodels exhibit controlled root mean square error(RMSE)and maximum absolute error(MAXE)values,both within the range of 0.203.Integrated into their respective automatic control systems,thesemodels optimize two-phase flow heat transfer,finetune combustion conditions,and mitigate incomplete combustion.Furthermore,this paper conducts an in-depth exploration of the generationmechanismof nitrogen oxides(NOx)and low oxygen emission reduction technology in coal-fired boilers,demonstrating a substantial reduction in furnace exit NOx generation by 30%to 40%and the power supply coal consumption decreased by 1.62 g/(kW h).The research outcomes highlight the model’s rapid responsiveness,enabling prompt reflection of transient variations in various economic indicator parameters.This provides a more effective means for real-time monitoring of crucial variables in coal-fired boilers and facilitates timely combustion adjustments,underscoring notable achievements in boiler combustion.The research not only provides valuable and practical insights into the intricacies of two-phase flow heat transfer and heat exchange but also establishes a pioneering methodology for tackling industry challenges.